Negative ion ceramic product, and manufacturing method thereof

A technology of ceramic products and manufacturing methods, which is applied in the field of ceramic products, can solve the problems of poor negative ion release performance, etc., and achieve the effects of enhancing wear resistance, excellent negative ion release performance, and avoiding erosion

Inactive Publication Date: 2019-09-03
DEHUA HENGHAN ARTS
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Based on the above prior art, the object of the present invention is to provide a negative ion ceramic product and its manufacturing method, to solve the problem of poor negative ion release performance of existing ceramic products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of negative ion ceramic product, its raw material composition comprises green body raw material and glaze raw material; Green body raw material comprises the component of following mass fraction: 35 parts of bone meal, 12 parts of potassium feldspar, 5 parts of calcite, 25 parts of kaolin, 12 parts of Clay, 4 parts of water glass, 5 parts of carbon fiber powder, 5 parts of porous starch, 8 parts of tourmaline powder and 6 parts of Sogo stone powder;

[0034] The glaze raw materials include the following components in parts by mass: 15 parts of agate stone, 12 parts of potassium feldspar, 6 parts of quartz, 6 parts of burnt talc, 8 parts of zirconia, 12 parts of flux, 7 parts of energy mineral powder, 8 parts 1 part tourmaline powder and 4 parts monazite powder.

[0035] Among them, the energy mineral powder is mixed and stirred from titanium dioxide, neodymium ore, germanium ore, dysprosium ore, alumina and rare earth, and the mass ratio of titanium dioxide, neod...

Embodiment 2

[0051] A kind of negative ion ceramic product, its raw material composition comprises green body raw material and glaze raw material; Green body raw material comprises the following components of mass parts: 30 parts of bone powder, 10-15 parts of albite feldspar, 5 parts of calcite, 30 parts of kaolin, 10 parts of clay, 5 parts of water glass, 3 parts of carbon fiber powder, 6 parts of porous starch, 5 parts of tourmaline powder and 8 parts of Sogo stone powder;

[0052] The glaze raw materials include the following components in parts by mass: 10 parts of agate stone, 50 parts of albite, 5 parts of quartz, 8 parts of burnt talc, 3 parts of zirconia, 15 parts of flux, 3 parts of energy mineral powder, 10 parts of 1 part tourmaline powder and 2 parts monazite powder.

[0053] Among them, the energy mineral powder is mixed and stirred from titanium dioxide, neodymium ore, germanium ore, dysprosium ore, alumina and rare earth, and the mass ratio of titanium dioxide, neodymium or...

Embodiment 3

[0069] A kind of negative ion ceramic product, its raw material composition comprises green body raw material and glaze raw material; Green body raw material comprises the component of following mass fraction: 40 parts of bone meal, 10 parts of potassium feldspar, 6 parts of calcite, 20 parts of kaolin, 15 parts of Clay, 3 parts of water glass, 6 parts of carbon fiber powder, 3 parts of porous starch, 10 parts of tourmaline powder and 3 parts of Sogo stone powder;

[0070] The glaze raw materials include the following components in parts by mass: 20 parts of agate stone, 10 parts of potassium feldspar, 10 parts of quartz, 5 parts of burnt talc, 10 parts of zirconia, 5 parts of flux, 8 parts of energy mineral powder, 5 parts of part tourmaline powder and 5 parts monazite powder.

[0071] Among them, the energy mineral powder is mixed and stirred from titanium dioxide, neodymium ore, germanium ore, dysprosium ore, alumina and rare earth, and the mass ratio of titanium dioxide, n...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Moisture contentaaaaaaaaaa
Login to View More

Abstract

The invention discloses a negative ion ceramic product, and a manufacturing method thereof, and belongs to the technical field of ceramic. The blank body raw materials of the negative ion ceramic product comprise, by mass, 30-40 parts of bone meal, 10-15 parts feldspar, 5-6 parts calcite, 20-30 parts kaolin, 10-15 parts clay, 3-5 parts water glass, 3-6 parts carbon fiber powder, 3-6 parts porous starch, 5-10 parts of tourmaline powder and 3-8 parts of Chongguang stone powder; a glaze raw material comprises following components, by mass, 10-20 parts agate stone, 10-50 parts feldspar, 5-10 partsquartz, 5-8 parts of sintered talc, 3-10 parts of zirconia, 5-15 parts of a fluxing agent, 3-8 parts of energy mineral powder, 5-10 parts of tourmaline powder and 2-5 parts of monazite powder. The negative ion ceramic product is excellent in negative ion release performance, flat in ceramic glaze surface, fine in texture, bright and smooth in glaze color, and high in strength and wear resistance.

Description

technical field [0001] The invention belongs to the technical field of ceramic products, and in particular relates to a negative ion ceramic product and a manufacturing method thereof. Background technique [0002] Ceramic products are indispensable daily necessities in daily life. With the improvement of people's living standards, people's requirements for the functionality of ceramic products are also getting higher and higher. [0003] In the prior art, there are ceramic products with negative ion release function. However, because the ceramic raw material components contain more alkali metal or alkaline earth metal oxides with high chemical activity, the negative ion additives are easily eroded during high-temperature firing. The reaction occurs and its structure is destroyed, resulting in a decrease in the ability to release negative ions, thereby reducing the concentration of negative ions released. At the same time, due to the thicker glaze layer, in order to achieve ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/135C04B33/13C04B33/36C03C8/02C04B41/89
CPCC03C8/02C04B33/1305C04B33/131C04B33/1355C04B33/36C04B41/009C04B41/52C04B41/89C04B2235/3427C04B2235/3463C04B2235/442C04B2235/5248C04B2235/6022C04B2235/612C04B2235/96C04B41/5031C04B41/4545C04B41/5022Y02P40/60
Inventor 林锦明
Owner DEHUA HENGHAN ARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com