A kind of preparation method of foam yarn

A foam and yarn technology, which is applied in liquid/gas/steam yarn/filament treatment, plant fiber, fiber treatment, etc. It can solve the problem that the improvement of the appearance and performance of the core-spun yarn is not obvious enough, and the combination method and preparation process need to be studied , Yarn application has not been reported and other issues, to achieve the effect of strong plasticity, low equipment requirements, and short time consumption

Active Publication Date: 2021-11-16
WUHAN TEXTILE UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the surface of the core-spun yarn is wrapped with other types of yarn, although it is different from the core material, they all belong to fibers, and the overall difference is not large, and the improvement of the appearance and performance of the core-spun yarn is not obvious enough; With the improvement of people's living standards, the relatively simple appearance of traditional yarns has gradually become difficult to meet people's needs. It needs to be compounded with other materials to develop new types of yarns with different appearances and excellent performance.
[0004] At the same time, polyurethane materials, as a new organic polymer material, are widely used in many fields of the national economy; among them, polyurethane foam materials are mainly made of isocyanate and polyether, and are used in foaming agents, catalysts, flame retardants, etc. It is a high molecular polymer foamed under the action of various additives. It has a porous structure and is widely used for its good heat retention, adhesion, sound insulation, insulation and water resistance. The application in the thread has not been reported, and its combination with the yarn and the preparation process are still to be studied

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of foam yarn
  • A kind of preparation method of foam yarn
  • A kind of preparation method of foam yarn

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The present embodiment provides a kind of preparation method of foam yarn, comprises the steps:

[0036] (1) Preparation of main ingredients

[0037] Put the mixed solution of polyether polyol and isocyanate in the mixing tank, add tin catalyst and stir to obtain the main material; wherein, the mass ratio of polyether polyol to isocyanate is 30:70; the tin catalyst The mass fraction of the catalyst is 1.5%; the stirring temperature is 60° C., the stirring speed is 1000 r / min, and the stirring time is 6 min.

[0038] (2) Preparation of additives

[0039] Mix polyether polyol, amine catalyst, blowing agent, foam stabilizer, after stirring uniformly, obtain auxiliary agent; Wherein, the mass fraction of described polyether polyol is 66%; The mass fraction of described amine catalyst is 0.9%; the mass fraction of the foaming agent is 10.9%; the mass fraction of the foam stabilizer is 0.7%; the stirring temperature is 60° C., the stirring speed is 1000 r / min, and the stirr...

Embodiment 2～5

[0048] Embodiments 2-5 provide a kind of preparation method of foamed yarn, compared with embodiment 1, the difference is that polyether polyol, isocyanate, tin catalyst, amine catalyst, blowing agent and homogenizer in the raw material are changed. The mass fraction of foaming agent; Wherein polyether polyol is divided into two parts and adds in step (1) and step (2) respectively, and its specific consumption and the contrast with embodiment 1 are as shown in table 1.

[0049] The foamed yarn raw material mass fraction of table 1 embodiment 1~5

[0050]

[0051]

[0052] The foamed yarn appearance of the embodiment 1~5 prepared by the raw material mass fraction shown in table 1 is as follows figure 2 shown. Depend on figure 2 It can be seen that compared with the original cotton yarn, the surface of the foam yarn is covered with foam, and the degree of foaming of the foam yarn prepared according to different raw material mass fractions is different, so the size and ...

Embodiment 6～12

[0055] Embodiments 6-12 provide a preparation method of foamed yarn. Compared with Example 1, the difference is that the parameters of the stirring process, its specific parameter settings, and the elongation at break and breaking strength of the foamed yarn produced are changed. As shown in table 2.

[0056] The mechanical property comparison of the foamed yarn of table 2 embodiment 6~12 and embodiment 1

[0057]

[0058] According to the data shown in table 2, compare examples 6 and 7, embodiment 8 and 1, embodiment 9 and 10, embodiment 11 and 12 successively, it can be seen that when the stirring temperature is constant, with stirring speed and stirring time The elongation at break and the breaking strength of the foamed yarn produced showed a trend of decreasing first and then increasing. When the stirring speed reached 1000r / min and the stirring time was 6min, the effect of increasing the stirring speed and the stirring time on the foamed yarn The improvement of the p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of foam yarn. The preparation process includes the preparation of main materials, the preparation of auxiliary agents, the padding treatment and the preparation of foam yarn; the method is to mix polyether polyol, isocyanate and tin catalyst into The main material, and then the mixed solution of polyether polyol, amine catalyst, foaming agent, and foam stabilizer is used as auxiliary agent, and the raw materials required for the reaction are padd on two yarns by in-situ polymerization method, respectively. Simulate solution mixing by twisting, so that the yarn can form a uniform and dense polyurethane foam from the inside out, and increase the adhesion of the foam film layer, so as to obtain a foam yarn with a unique appearance, which can be used in different applications according to needs. It can be used as a base material to produce fabrics of different shapes, and has strong plasticity; and the preparation method is simple, time-consuming, and requires low equipment, and can be widely used.

Description

technical field [0001] The invention relates to the technical field of spinning, in particular to a method for preparing foam yarn. Background technique [0002] As a kind of textile, yarn is a product with a certain fineness processed from various textile fibers. It can be used for weaving, rope making, thread making, knitting and embroidery, etc., and is widely used in daily life. There are many kinds of yarns with different properties. According to the number of materials used in the yarns, they can be divided into pure spinning yarns with only a single fiber type and composite yarns composed of two or more fibers. Because composite yarns It can integrate the advantages of various raw materials, has better overall performance and wider application range, so it has attracted extensive attention. [0003] The currently commonly used composite yarn is core-spun yarn, which is a yarn spun with filament as the core and wrapped with short fibers. . However, since the surface...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M23/04D06M15/568D06M15/647D06B3/04C08G18/76C08G18/48C08G18/24C08G18/18C08G101/00D06M101/06
CPCC08G18/165C08G18/1808C08G18/246C08G18/4829C08G18/7614C08G2110/0083D06B3/04D06M15/568D06M15/647D06M23/04D06M2101/06
Inventor 徐卫林付专周思婕夏良君王阿明王运利
Owner WUHAN TEXTILE UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com