A kind of antiskid heat aging resistant EVA, NR composite foam material and preparation method thereof

A composite foaming and heat-resistant aging technology, applied in the field of NR composite foaming materials and their preparation, anti-skid and heat-resistant aging EVA, can solve problems such as product failure, and achieve good compatibility, less addition, and huge social economy. effect of benefit

Active Publication Date: 2022-04-05
福建宸琦新材料科技有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to abrasion, product failure may occur in severe cases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of antiskid heat aging resistant EVA, NR composite foam material and preparation method thereof
  • A kind of antiskid heat aging resistant EVA, NR composite foam material and preparation method thereof
  • A kind of antiskid heat aging resistant EVA, NR composite foam material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A method for preparing anti-slip and heat-resistant aging EVA, NR composite foaming material, the specific steps are:

[0027] 1) Preparation of graphene oxide template: Dissolve 1 g of flake graphite in 23 mL of concentrated sulfuric acid, place it in a magnetic stirrer for stirring, and slowly add 3 g of potassium permanganate and 1 g of sodium nitrate after it is uniformly dispersed. Add within 1 hour; after another 2 hours of reaction, start to heat up to 98°C, when the solution system becomes thick, add 44ml deionized water and 5ml 5wt% hydrogen peroxide solution dropwise, and titrate with 5wt% hydrochloric acid until the solution is not Regeneration of bubbles means the end of the reaction; wash the prepared graphene oxide with deionized water, centrifuge, freeze-dry and add 200 mg of prepared graphene oxide into the flask, add deionized water for ultrasonication, and stir; 10 ml of absolute ethanol Put it into a flask, add 400 mg of sodium p-aminobenzenesulfonate...

Embodiment 2

[0033] A method for preparing anti-slip and heat-resistant aging EVA, NR composite foaming material, the specific steps are:

[0034] 1) Preparation of graphene oxide template: Dissolve 1 g of flake graphite in 23 mL of concentrated sulfuric acid, place it in a magnetic stirrer for stirring, and slowly add 3 g of potassium permanganate and 1 g of sodium nitrate after it is uniformly dispersed. Add within 1 hour; after another 2 hours of reaction, start to heat up to 98°C, when the solution system becomes thick, add 44ml deionized water and 5ml 5wt% hydrogen peroxide solution dropwise, and titrate with 5wt% hydrochloric acid until the solution is not Regeneration of bubbles means the end of the reaction; wash the prepared graphene oxide with deionized water, centrifuge, freeze-dry and add 200 mg of prepared graphene oxide into the flask, add deionized water for ultrasonication, and stir; 10 ml of absolute ethanol Put it into a flask, add 400 mg of sodium p-aminobenzenesulfonate...

Embodiment 3

[0040] A method for preparing anti-slip and heat-resistant aging EVA, NR composite foaming material, the specific steps are:

[0041] 1) Preparation of graphene oxide template: Dissolve 1 g of flake graphite in 23 mL of concentrated sulfuric acid, place it in a magnetic stirrer for stirring, and slowly add 3 g of potassium permanganate and 1 g of sodium nitrate after it is uniformly dispersed. Add within 1 hour; after another 2 hours of reaction, start to heat up to 98°C, when the solution system becomes thick, add 44ml of deionized water and 5ml of 5% hydrogen peroxide solution dropwise, and titrate with 5% hydrochloric acid until the solution is not Regeneration of bubbles means the end of the reaction; wash the prepared graphene oxide with deionized water, centrifuge, freeze-dry and add 200 mg of prepared graphene oxide into the flask, add deionized water for ultrasonication, and stir; 10 ml of absolute ethanol Put it into a flask, add 400 mg of sodium p-aminobenzenesulfona...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-slip, heat-resistant and aging-resistant EVA, NR composite foaming material and a preparation method thereof, belonging to the field of polymer composite foaming materials. The composition of raw materials is calculated in parts by weight: 97-100 parts of ethylene-vinyl acetate copolymer, 5-10 parts of NR, 1-10 parts of composite anti-skid heat-resistant aging agent, 2.5-3 parts of foaming agent AC, 0.5 parts of stearic acid 0.6 part, 0.6 part of zinc stearate, 0.8 part of zinc oxide, 0.2 part of dicumyl peroxide; Described composite antiskid heat-resistant aging agent is graphene-white carbon black nano-composite material. The present invention successfully prepares a graphene-white carbon black nanocomposite material by depositing and growing nano-white carbon black on the surface of graphene oxide and reducing graphene oxide in an environmentally friendly manner. Graphene-silica is used as a composite anti-slip heat-resistant aging agent, with less addition, good compatibility with the matrix, easy dispersion, excellent anti-slip effect, and excellent anti-slip performance.

Description

technical field [0001] The invention belongs to the field of polymer composite foam materials, and in particular relates to an anti-slip, heat-resistant and aging-resistant EVA, NR composite foam material and a preparation method thereof. Background technique [0002] EVA foam composite materials are widely used in shoe materials, construction, packaging and other fields due to their advantages such as low density, strong cushioning and shock absorption capacity, and low temperature resistance. Because the EVA material, like most polymer plastics, causes its anti-skid performance to decrease after foaming. Such a high abrasion will seriously restrict its application in some shoe materials with high anti-skid requirements. Due to abrasion, product failure may occur in severe cases. Therefore, the research of EVA and NR composite foam materials with anti-slip and heat-resistant aging has important application value in the field of shoe materials. [0003] Graphene is a two-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/08C08L7/00C08K5/09C08K5/098C08K3/22C08K5/14C08K3/04C08K3/36C08K9/12C08K9/10C08K13/06C08J9/10
CPCC08J9/103C08J2323/08C08J2407/00C08J2203/04C08K5/09C08K5/098C08K2003/2296C08K5/14C08K3/042C08K3/36C08K9/12C08K9/10C08K13/06
Inventor 郑玉婴洪贤晟
Owner 福建宸琦新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products