Composite lead salt thermally-stable anti-degradation auxiliary agent as well as preparation method and application thereof

A composite lead salt, thermally stable technology, applied in the field of plastic processing, can solve problems such as restrictions, and achieve the effects of reducing harm, improving stability, and simple synthesis process

Active Publication Date: 2019-10-15
内蒙古佳运通智能环保新材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the development trend of PVC heat-stable anti-degradation additives towards low toxicity and non-toxicity in recent years, the use of lead salt heat-stable anti-degradation additives has been limited to a certain extent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The present invention provides a preparation method of the composite lead salt heat-stable anti-degradation additive described in the technical solution, comprising the following steps:

[0036] Melting and dispersing the raw material components to obtain a slurry;

[0037] The slurry is aged to obtain a composite lead salt heat-stable anti-degradation additive.

[0038] In the invention, the raw material components are melt-dispersed to obtain slurry. In the present invention, the melting and dispersing is preferably carried out in a three-necked flask equipped with a mechanical stirring device and a reflux device under oil bath conditions; in the present invention, the process of melting and dispersing preferably includes: The first melting and dispersing is carried out; heating to 110-120°C, adding basic lead salt to the obtained dispersion material for the second melting and dispersing; then adding acid binding agent, titanium dioxide fly ash and calcium carbonate to...

Embodiment 1

[0043] Carry out batching according to following mass percentage content:

[0044] Tribasic lead sulfate 28%, lead stearate 7%, stearic acid 10%, polyethylene wax 10%, calcium carbonate 40%, fly ash 5%.

[0045] After weighing each raw material according to the above mass ratio, heat it to 90°C in an oil bath and a 250mL three-necked bottle equipped with a mechanical stirring device and a reflux device, add stearic acid and polyethylene wax, and add stearic acid and polyethylene wax under the condition of 100r / min Continue stirring for 15 minutes for the first melting and dispersing; heat to 110°C, add lead stearate and tribasic lead sulfate to the obtained dispersion material, and continue stirring for 20 minutes for the second melting and dispersing; then add calcium carbonate and Fly ash, continue to stir for 20 minutes to carry out the third melting and dispersing to obtain a gray-white uniform slurry; keep the slurry for 30 minutes to age, and cool the resulting product t...

Embodiment 2

[0048] Carry out batching according to following mass percentage content:

[0049] Tribasic lead sulfate 32%, lead stearate 8%, dibasic lead stearate 10%, 4A zeolite 5%, stearic acid 8%, polyethylene wax 8%, titanium dioxide 1%, calcium carbonate 18 %, fly ash 10%.

[0050] After weighing each raw material according to the above mass ratio, heat it to 90°C in an oil bath and a 250mL three-necked bottle equipped with a mechanical stirring device and a reflux device, add stearic acid and polyethylene wax, and add stearic acid and polyethylene wax under the condition of 120r / min Continue stirring for 15 minutes for the first melting and dispersing; heat to 115°C, add tribasic lead sulfate, lead stearate and dibasic lead stearate to the obtained dispersed material, and continue stirring for 25 minutes for the second melting and dispersing; Add 4A zeolite, titanium dioxide, calcium carbonate and fly ash to the obtained dispersed material, continue to stir for 25min to carry out th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of plastic processing, in particular relates to a composite lead salt thermally-stable anti-degradation auxiliary agent as well as a preparation method andapplication thereof. The composite lead salt thermally-stable anti-degradation auxiliary agent provided by the invention comprises the following raw material components by mass percentage: 35-60% ofbasic lead salt, 0-10% of an acid binding agent, 10-20% of a lubricant, 0-2% of titanium dioxide, 5-18% of fly ash and 10-40% of calcium carbonate. Results of embodiments show that the composite leadsalt thermally-stable anti-degradation auxiliary agent provided by the invention has outstanding thermal stability performance, can effectively improve the degradation temperature of polyvinyl chloride, and has high initial whiteness and good long-term stability.

Description

technical field [0001] The invention relates to the technical field of plastic processing, in particular to a composite lead salt heat-stable anti-degradation additive and its preparation method and application. Background technique [0002] Polyvinyl chloride (PVC) is one of the five general-purpose resins in the world. Its products have the advantages of superior processing performance, difficult combustion, high mechanical properties, low price, rich sources of raw materials, and mature manufacturing processes. Therefore, they are widely used in light industry, machinery, Electronics, construction, textile and aerospace and other fields. However, PVC has poor stability during processing, especially in being extremely sensitive to heat. When the temperature reaches above 120°C, an obvious thermal decomposition reaction will occur, causing the color of PVC to change (white-yellow-red-brown-black) , while releasing hydrogen chloride gas. This deficiency directly leads to a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08K13/04C08K3/30C08K3/32C08K5/098C08K5/3492C08K3/34C08K3/22C08K5/09C08K7/24C08K3/26C08L23/06C08L23/30C08L91/06
CPCC08K3/22C08K3/26C08K3/30C08K3/32C08K3/34C08K5/09C08K5/098C08K5/34928C08K7/24C08K13/04C08K2003/2206C08K2003/2227C08K2003/2241C08K2003/265C08K2003/3045C08L23/06C08L23/30C08L27/06C08L91/06C08L2201/08
Inventor 曹建伟郭峰方斌正张晓芳武可书常强强
Owner 内蒙古佳运通智能环保新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com