A kind of acid-resistant industrial brush and preparation method thereof

An industrial and industrial technology, which is applied in the field of acid-resistant industrial brushes and its preparation, can solve problems such as waste of resources and corrosion of items, and achieve the effects of saving costs, prolonging service life, and good user experience

Active Publication Date: 2021-06-15
安徽省忆德工业刷制造有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing industrial brushes are generally made into an integral structure, and the bristles are consumables. After consumption, the entire device is thrown away and a new device is used. At this time, the industrial brush handle can continue to be used, which causes Waste of resources; since there are many acids in the industry, it is easy to cause corrosion of items, so it is necessary to design acid-resistant industrial brushes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of acid-resistant industrial brush and preparation method thereof
  • A kind of acid-resistant industrial brush and preparation method thereof
  • A kind of acid-resistant industrial brush and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Based on the preparation method of above-mentioned a kind of acid-resistant industrial brush, comprise following preparation method:

[0033] Preparation of brush main body 5: Prepare 58-64 parts of polybutylene adipamide, 15-25 parts of polysulfone, 8-14 parts of polyether ether ketone, 2-6 parts of polytetrafluoroethylene, 6-6 parts of liquid crystal polymer 12 parts, heat the above materials to 350-380°C and mix and stir evenly, after stirring evenly, add 26-28% chromium and 21-23% nickel by weight to the above mixture while it is hot, and mix evenly again Finally, set a fixed size, and use a wire drawing machine to draw while it is hot, and form the brush body 5 after it cools down;

[0034] Preparation of the brush mounting seat 1: Prepare the raw material of the brush mounting seat 1 with a ring structure, and open three evenly arranged arc-shaped slots 3 on the inner wall, and open the position of the brush mounting seat 1 corresponding to the arc-shaped slot 3 ...

Embodiment 2

[0041] Based on the preparation method of above-mentioned a kind of acid-resistant industrial brush, comprise following preparation method:

[0042] Preparation of brush body 5: prepare 58-64 parts of polybutylene adipamide, 15-25 parts of polysulfone, 8-14 parts of polyetheretherketone, 2-6 parts of polytetrafluoroethylene, 6-6 parts of liquid crystal polymer 12 parts, heat the above materials to 350-380°C and mix and stir evenly, after stirring evenly, add 26-28% chromium and 21-23% nickel by weight to the above mixture while it is hot, and mix evenly again Finally, set a fixed size, and use a wire drawing machine to draw while it is hot, and form the brush main body 5 after it cools down;

[0043] Preparation of the brush mounting seat 1: Prepare the raw material of the brush mounting seat 1 with a ring structure, and open three evenly arranged arc-shaped slots 3 on its inner wall, and open the position of the brush mounting seat 1 corresponding to the arc-shaped slot 3 Th...

Embodiment 3

[0050] Based on the preparation method of above-mentioned a kind of acid-resistant industrial brush, comprise following preparation method:

[0051] Preparation of brush body 5: prepare 58-64 parts of polybutylene adipamide, 15-25 parts of polysulfone, 8-14 parts of polyetheretherketone, 2-6 parts of polytetrafluoroethylene, 6-6 parts of liquid crystal polymer 12 parts, heat the above materials to 350-380°C and mix and stir evenly, after stirring evenly, add 26-28% chromium and 21-23% nickel by weight to the above mixture while it is hot, and mix evenly again Finally, set a fixed size, and use a wire drawing machine to draw while it is hot, and form the brush main body 5 after it cools down;

[0052] Preparation of the brush mounting seat 1: Prepare the raw material of the brush mounting seat 1 with a ring structure, and open three evenly arranged arc-shaped slots 3 on its inner wall, and open the position of the brush mounting seat 1 corresponding to the arc-shaped slot 3 Th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention disclosed a acid -resistant industrial brush and its preparation methods, including the brush installation seat, the hair brush main body was installed on the outer wall of the outer wall of the brush installation seat.There are several bar card slots, the internal card of the bar slot runs through the strip card, the top of the strip card is fixed with a handle connector, and the top of the handle connector is fixed with the handle.The present invention adopts the assembly structure to divide the entire industry into a brush installation part, the installation disk part, and the handle part. It can be assembled when used.It is necessary to replace the damaged part, which is convenient and practical; the hairpiece of the bristles made of acid -resistant polyboxyl -dimies, polyethyls, polyether ether, polytrafluoroethylene, and liquid crystal polymers can be used.It has a acid -resistant effect, which greatly extends the service life of the device and indirectly saves costs.

Description

technical field [0001] The invention relates to related fields of industrial brushes, in particular to an acid-resistant industrial brush and a preparation method thereof. Background technique [0002] The industrial brush is a new type of product upgraded and improved on the basis of the civilian brush. It is mainly used for cleaning, dust removal and polishing in the process of industrial production. It is widely used in the textile industry, ceramic industry, leather and shoe industry, Glass industry, papermaking, printing, cigarette industry, wood industry, furniture industry, electronics industry, environmental protection industry, door and window industry, metal industry, color steel plate, steel tile industry and metallurgy, have very extensive application value. [0003] Existing industrial brushes are generally made into an integral structure, and the bristles are consumables. After consumption, the entire device is thrown away and a new device is used. At this time...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More