Carbon fiber electrode and preparation method for low-frequency ocean electric field detection
A carbon fiber electrode, carbon fiber technology, applied in the direction of carbon fiber, fiber processing, electromagnetic field characteristics, etc., can solve the problems of low surface activity, unable to respond to weak low-frequency signals, etc., achieve high surface activity, promote oxidation etching, and have wide application prospects Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028] Such as figure 1 As shown, a new type of carbon fiber electrode for low-frequency ocean electric field detection, its structure includes a copper column 1 for circuit connection, a waterproof sealing ring 2, an electrode body 3, and an electrode protective cover 4. The surface structure of a single carbon fiber includes an oxidized Viscose-based carbon fiber5, nanocomposite film6.
[0029] The electrode preparation method is as follows:
[0030] 1) Pretreatment: place the carbon fiber in an anhydrous ethanol solution and ultrasonically clean it for 90 minutes, wash it with distilled water, and put it in an oven at 80°C for 2 hours;
[0031] 2) Ultrasonic + Concentrated Nitric Acid Combined Oxidation Treatment: Soak the treated carbon fiber in 1) in concentrated nitric acid, treat it in an ultrasonic instrument at 110°C for 4 hours, then wash it with deionized water and absolute ethanol until pH>6, and dry it Stand still for 1 day under constant temperature and humidit...
Embodiment 2
[0036] Such as figure 1 As shown, a new type of carbon fiber electrode for low-frequency ocean electric field detection, its structure includes a copper column 1 for circuit connection, a waterproof sealing ring 2, an electrode body 3, and an electrode protective cover 4. The surface structure of a single carbon fiber includes an oxidized Viscose-based carbon fiber5, nanocomposite film6.
[0037] The electrode preparation method is as follows:
[0038] 1) Pretreatment: place the carbon fiber in an anhydrous ethanol solution and ultrasonically clean it for 90 minutes, wash it with distilled water, and put it in an oven at 80°C for 2 hours;
[0039] 2) Ultrasonic + Concentrated Nitric Acid Combined Oxidation Treatment: Take 1) the treated carbon fiber and soak it in concentrated nitric acid, treat it in an ultrasonic instrument at 70°C for 4 hours, then wash it with deionized water and absolute ethanol until ph>6, and dry it Stand still for 1 day under constant temperature and...
Embodiment 3
[0044] Such as figure 1 As shown, a new type of carbon fiber electrode for low-frequency ocean electric field detection, its structure includes a copper column 1 for circuit connection, a waterproof sealing ring 2, an electrode body 3, and an electrode protective cover 4. The surface structure of a single carbon fiber includes an oxidized Viscose-based carbon fiber5, nanocomposite film6.
[0045] The electrode preparation method is as follows:
[0046] 1) Pretreatment: place the carbon fiber in an anhydrous ethanol solution and ultrasonically clean it for 90 minutes, wash it with distilled water, and put it in an oven at 80°C for 2 hours;
[0047] 2) Ultrasonic + Concentrated Nitric Acid Combined Oxidation Treatment: Take 1) treated carbon fiber and soak it in concentrated nitric acid, treat it in an ultrasonic instrument at 150°C for 4 hours, then wash it with deionized water and absolute ethanol until pH>6, and dry it Stand still for 1 day under constant temperature and hu...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com