An easy-to-form three-layer core-shell particle toughened polymer composite material and its preparation method

A technology of composite materials and core-shell particles, which is applied in the field of easy-to-form three-layer core-shell particle toughened polymer composite materials and its preparation, can solve the problems of environmental protection and sustainable development, limited toughening effect, pollution, etc.

Active Publication Date: 2021-10-08
JIANGNAN UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The particles in the above patents are not conducive to dispersion in the matrix due to their high viscosity during use, and their formability is poor. At the same time, the toughening effect is also limited.
And ethyl acrylate etc. all come from petroleum resources, all can cause the pollution of varying degrees in the preparation process, fail to solve the problem of environmental protection and sustainable development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • An easy-to-form three-layer core-shell particle toughened polymer composite material and its preparation method
  • An easy-to-form three-layer core-shell particle toughened polymer composite material and its preparation method
  • An easy-to-form three-layer core-shell particle toughened polymer composite material and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Mix 100 parts of cornstarch (Changchun Dacheng Corn Development Co., Ltd.) and 300 parts of ethyl acetate. After cooling down and stirring thoroughly, gradually add 15 parts of pyridine dropwise. After heating up and stirring fully, add 15 parts of acrylic acid dropwise and continue stirring. Washed with water and ethanol, filtered and dried to obtain Modified Starch 1 , The degree of substitution was determined to be 1.89.

Embodiment 2

[0046] Mix 100 parts of soybean starch (Tianquan Food Co., Ltd.) and 150 parts of ethyl acetate. After cooling down and stirring thoroughly, gradually add 10 parts of pyridine dropwise. Washed with absolute ethanol, filtered and dried Modified starch 2 , The degree of substitution was determined to be 2.30. 2. Preparation of core-shell particles with three-layer structure

Embodiment 3

[0048] With 100 parts in embodiment 2 Modified starch 2 with 50 parts of 2-methylene-1,3-dioxetane 50 parts of n-butyl itaconate were mixed and added to 300 parts of deionized water, fully stirred at room temperature for 30 minutes, then 1 part of initiator azobisisobutyronitrile was added, the temperature was raised to 60°C, stirred and polymerized, reacted for 8 hours, added 10 parts of styrene (Hangzhou Jessica Chemical Co., Ltd.), reacted for 3 hours, added ethanol to wash, filtered and dried to prepare a three-layer structure Easily Formable Core-Shell Particles 1 , The measured particle size is listed in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an easy-to-form three-layer core-shell particle toughened polymer composite material and a preparation method thereof. The composite material is obtained by blending raw materials comprising the following components: 100 parts by weight of polymer; three-layer core-shell 1 to 100 parts by weight of particles; the polymer is a thermosetting polymer and a thermoplastic polymer; the core-shell particle is composed of three parts: a bio-based hard core, a soft inner shell and a hard outer shell; the present invention does not require a plasticizer Composite materials can be plasticized and processed at the same time. While toughening the polymer, the outermost hard shell layer can effectively strengthen the composite material. It has high production efficiency, easy processing and molding, low cost, simple process, and controllable performance. It is suitable for Prepare composite materials with various performance requirements.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to an easy-to-form three-layer core-shell particle toughened polymer composite material and a preparation method thereof. Background technique [0002] With the gradual reduction of fossil energy reserves, the global energy crisis is looming. The energy structure dominated by fossil energy is obviously unsustainable. The use of fossil energy is also a key factor causing environmental change and pollution. Due to the decrease of global fossil resources, the traditional chemical industry at the cost of fossil resources and the environment is facing an increasingly severe situation. Making full use of biomass resources to replace fossil resources, synthesizing polymer materials or raw materials required for production is very important for getting rid of high The fact that molecular materials products and raw materials depend on petrochemical resources is of great significa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L79/08C08L63/00C08L61/06C08L67/04C08L69/00C08L59/00C08L51/02
CPCC08L59/00C08L61/06C08L63/00C08L67/04C08L69/00C08L79/08C08L2207/53C08L51/02
Inventor 东为富汪洋李婷吴正贵董新一陈明清
Owner JIANGNAN UNIV
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com