A kind of anti-dripping polymer sulfonate flame retardant and preparation method thereof

A polymer sulfonate and flame retardant technology, applied in the field of polymers, can solve problems such as easy precipitation, lack of physical entanglement, and large application limitations, so as to improve flame retardancy, improve drip resistance, prevent The effect of the spread of fire

Active Publication Date: 2022-04-26
铨盛聚碳科技股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The introduction of sulfonate can endow polycarbonate with catalytic flame retardancy, and the organic sulfonate such as potassium diphenylsulfonesulfonate (KSS) which has been industrially applied has good catalytic flame retardancy for polycarbonate materials, but It is a small molecule flame retardant and the polycarbonate material matrix lacks physical entanglement and is easy to precipitate, so the application limitations are large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-dripping polymer sulfonate flame retardant and preparation method thereof
  • A kind of anti-dripping polymer sulfonate flame retardant and preparation method thereof
  • A kind of anti-dripping polymer sulfonate flame retardant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] An anti-dripping polymer sulfonate flame retardant, comprising the following raw materials in parts by weight:

[0028]

[0029] Each part of the unsaturated sulfonate is a mixture of sodium styrene sulfonate, sodium vinyl sulfonate and sodium methallyl sulfonate in a weight ratio of 0.8:0.4:0.1.

[0030] Each part of the unsaturated monomer is a mixture of vinyl ethyl ether, styrene and acrylonitrile in a weight ratio of 0.8:0.1:0.4.

[0031] Each part of the initiator is a mixture of ammonium persulfate, potassium persulfate and tert-butyl hydroperoxide-sodium bisulfite redox system in a weight ratio of 0.5:0.8:0.4.

[0032] Each part of the coagulant is calcium chloride.

[0033] Each part of the emulsifier is a mixture composed of fatty acid sulfoalkyl ester, N-alkyldiethanolamine salt and alkylphenol polyoxyethylene ether in a weight ratio of 0.8:0.4:0.6.

[0034] The anti-dripping polymer sulfonate flame retardant comprises the following steps:

[0035] 1) M...

Embodiment 2

[0040] An anti-dripping polymer sulfonate flame retardant, comprising the following raw materials in parts by weight:

[0041]

[0042] Each part of the unsaturated sulfonate is a mixture of sodium styrene sulfonate, sodium vinyl sulfonate and sodium methallyl sulfonate in a weight ratio of 0.9:0.5:0.2.

[0043] Each part of the unsaturated monomer is a mixture of vinyl ethyl ether, styrene and acrylonitrile in a weight ratio of 0.9:0.2:0.5.

[0044] Each part of the initiator is a mixture of ammonium persulfate, potassium persulfate and tert-butyl hydroperoxide-sodium bisulfite redox system in a weight ratio of 0.6:0.9:0.5.

[0045] Each part of the coagulant is calcium chloride.

[0046] Each part of the emulsifier is a mixture composed of fatty acid sulfoalkyl ester, N-alkyldiethanolamine salt and alkylphenol polyoxyethylene ether in a weight ratio of 0.9:0.5:0.7.

[0047] The anti-dripping polymer sulfonate flame retardant comprises the following steps:

[0048] 1) M...

Embodiment 3

[0054] An anti-dripping polymer sulfonate flame retardant, comprising the following raw materials in parts by weight:

[0055]

[0056] Each part of the unsaturated sulfonate is a mixture of sodium styrene sulfonate, sodium vinyl sulfonate and sodium methallyl sulfonate in a weight ratio of 1.0:0.6:0.3.

[0057] Each part of the unsaturated monomer is a mixture of vinyl ethyl ether, styrene and acrylonitrile in a weight ratio of 1.0:0.3:0.6.

[0058] Each part of the initiator is a mixture of ammonium persulfate, potassium persulfate and tert-butyl hydroperoxide-sodium bisulfite redox system in a weight ratio of 0.7:1.0:0.6.

[0059] Each part of the coagulant is calcium chloride.

[0060] Each part of the emulsifier is a mixture composed of fatty acid sulfoalkyl ester, N-alkyldiethanolamine salt and alkylphenol polyoxyethylene ether in a weight ratio of 1.0:0.6:0.8.

[0061] The anti-dripping polymer sulfonate flame retardant comprises the following steps:

[0062] 1) M...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of macromolecules, in particular to an anti-dripping polymer sulfonate flame retardant and a preparation method thereof, comprising the following steps: 1) according to weight parts, emulsifier, unsaturated sulfonate, unsaturated The monomer and part of the deionized water are mixed, heated and stirred until uniform, the mixture A is obtained and kept warm, and set aside; 2) the initiator is added to the mixture A, and heated and stirred for free radical reaction to obtain a polymer sulfonate copolymer emulsion, Standby; 3) Add another part of deionized water and polytetrafluoroethylene emulsion into the polymer sulfonate copolymer emulsion, heat up and stir to obtain mixture B, and set aside; 4) Add coagulant to mixture B and stir evenly After heating and reacting, the obtained precipitated product is washed, dried and pulverized to obtain an anti-dripping polymer sulfonate flame retardant. The anti-dripping polymer sulfonate flame retardant of the invention has both durable flame retardancy and anti-dripping properties.

Description

technical field [0001] The invention relates to the technical field of polymers, in particular to an anti-dripping polymer sulfonate flame retardant and a preparation method thereof. Background technique [0002] Thermoplastic materials have the advantages of being lightweight, easy to manufacture and industrialized production. They are used in all aspects of our daily production and life, and have brought great impetus to human development. However, thermoplastic materials are easy to burn, soften and deform when heated, and even drip. In the production process, flame retardants need to be added to make them have a wider scope of application. At present, the research and application of flame retardant modification of plastic products have proved that adding flame retardants can delay combustion and reduce the intensity of combustion. However, during the burning process of plastic products, in addition to burning themselves, other combustibles will be dripped and ignited, ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F212/14C08F228/02C08F216/18C08F212/08C08F220/44C08F4/40C08L27/18C08L25/18
CPCC08F212/14C08F4/40C08L27/18C08L2201/02C08F228/02C08F216/18C08F212/08C08F220/44C08L25/18
Inventor 王启瑶
Owner 铨盛聚碳科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com