Foaming ceramic and preparation method thereof

A technology of foaming ceramics and foaming agent, which is applied in the direction of ceramic products, ceramic material production, clay products, etc., can solve the problems of long firing cycle, high production cost, poor slag stability, etc., to reduce bulk density and thermal conductivity. coefficient, the effect of reducing sintering energy consumption and saving production costs

Inactive Publication Date: 2019-12-20
FUJIAN DESHENG NEW BUILDING MATERIAL CO LTD
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the added value of this permeable brick (square brick) is low; and because Luo Yuanhong has poor plasticity, a large amount of bonding base material and liquid glue are added to the formula, which reduces the amount of Luo Yuanhong used
Therefore, it is impossible to realize large-scale resource utilization and high value-added utilization of Luoyuan red tailings
[0004] On the other hand, most of the existing foamed ceramics for construction use tile factory polishing waste or other waste (such as granite waste, fly ash, etc.) as the base material; among them, the polishing waste is greatly affected by the region
Different origins and different products have different components of polishing slag, and the stability of the slag is relatively poor
The traditional granite waste, due to the specificity of its composition, often has a low utilization rate
For example, in the Chinese patent CN106187087A, a facing composite foam ceramic based on granite tailings is disclosed. 1-10%, stabilizer 0.5-2%, debonding agent 0-2%, the utilization efficiency of the granite waste residue is low, and the additive dosage is high, the firing cycle is long and the energy consumption is high, resulting in high production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Foaming ceramic and preparation method thereof
  • Foaming ceramic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0055] In order to improve the various properties of the foamed ceramics in the present invention, it is also necessary to cooperate with a specific preparation method. Specifically, refer to figure 1 , the preparation method of foam ceramics among the present invention comprises the following steps:

[0056] S1: Mix various raw materials evenly according to the formula to obtain a mixture;

[0057] S2: ball milling the mixture to obtain a slurry;

[0058] Wherein, the fineness of the slurry is 250 mesh sieve <0.5%. It should be noted that in the general production process of foamed ceramics, the fineness is controlled at about 3-5% on a 250-mesh sieve. However, the present invention reduces the content of clay, so by reducing the fineness of the slurry, the suspension of the slurry and the fluidity of the powder after granulation are improved.

[0059] S3: subjecting the slurry to spray granulation to obtain a powder;

[0060] Specifically, after the slurry is stale in th...

Embodiment 1

[0068] This embodiment provides a foamed ceramic, the formula of which is: 90 parts of Luoyuan red tailings, 9 parts of sandbag soil, 0.1 parts of foaming agent, and 0.9 parts of stabilizer;

[0069] Among them, Luoyuan red tailings are composed of the following components: SiO 2 72.8%, Al 2 o 3 13.1%, Fe 2 o 3 1.9%, CaO1.0%, MgO0.2%, K 2 O 4.0%, Na 2 O 4.8%, LOI 2.2%;

[0070] Sandbag soil is composed of the following components: SiO 2 74.1%, Al 2 o 3 12.4%, Fe 2 o 3 1.2%, CaO 0.4%, MgO 0.08%, K 2 O 4.52%, Na 2 O 4.3%, LOI 3%;

[0071] The foaming agent is selected from carbon powder, and the stabilizer is selected from manganese dioxide.

[0072] Its preparation method is:

[0073] (1) According to the formula, various raw materials are mixed uniformly to obtain a mixture;

[0074] (2) ball milling the mixture to obtain a slurry;

[0075] Wherein, the fineness of the slurry is 0.5% after sieving through a 250 mesh sieve.

[0076] (3) Spray granulating t...

Embodiment 2

[0081] This embodiment provides a foamed ceramic, the formula of which is: 95 parts of Luoyuan red tailings, 1 part of black mud, 3 parts of recycled materials for ceramic grinding blocks, and 1 part of manganese dioxide;

[0082] Among them, Luoyuan red tailings are composed of the following components: SiO 2 70.7%, Al 2 o 3 13.6%, Fe 2 o 3 1.2%, CaO1.4%, MgO0.4%, K 2 O 5.2%, Na 2 O 4.5%, LOI 3%;

[0083] Black mud consists of the following components: SiO 2 64.6%, Al 2 o 3 23.4%, Fe 2 o 3 2.8%, CaO 0.6%, MgO 0.4%, K 2 O 1.7%, Na 2 O 0.3%, LOI 6.2%.

[0084] Its preparation method is:

[0085] (1) According to the formula, various raw materials are mixed uniformly to obtain a mixture;

[0086] (2) ball milling the mixture to obtain a slurry;

[0087] Wherein, the fineness of the slurry is 0.3% on a 250-mesh sieve.

[0088] (3) Spray granulating the slurry to obtain powder;

[0089] (4) distributing the powder into the high-temperature saggar;

[0090]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a foaming ceramic. The foaming ceramic is mainly prepared from the following raw materials in parts by weight: 90-95 parts of a Luoyuan red tailing, 1-9 parts of clay, 0.1-3 parts of a foaming agent and 0.1-1 part of a stabilizer; wherein the Luoyuan red tailing is mainly prepared from the following components in percentage by weight: 68-73% of SiO2, 12-15% of Al2O3, 1.2-2%of Fe2O3, 0.5-1.5% of CaO, 0.2-0.5% of MgO, 4-5.5% of K2O, 3-5% of Na2O and 0.5-3% of LOI. The invention further discloses a preparation method of the foaming ceramic. According to the foaming ceramic and the preparation method thereof, the Luoyuan red tailing is adopted as a main base material to prepare a foaming ceramic tile, and the resource utilization of the Luoyuan red tailing is effectively realized; and the prepared foaming ceramic tile has high compressive strength, low water absorption rate and low thermal conductivity.

Description

technical field [0001] The invention relates to the field of inorganic non-metallic materials, in particular to a foamed ceramic and a preparation method thereof. Background technique [0002] Luoyuanhong is a kind of granite produced in Luoyuan County, Fuzhou City, Fujian Province. It has bright colors and outstanding decorative properties. It is widely used as materials for panels, floor coverings, countertops, carvings, various building and garden stones. During the mining process of Luoyuanhong, a large amount of Luoyuanhong tailings were produced, which caused great pressure on the local ecological environment. Therefore, how to make resource utilization of Luoyuan red tailings is an urgent problem to be solved. [0003] Chinese patent CN108558359A discloses a technical scheme of using Luo Yuanhong to prepare permeable bricks, which uses 80-100 parts of stone fragments, 3-12 parts of bonding base material, and 3-12 parts of liquid glue to prepare sintered permeable bri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B33/13C04B38/02C04B38/06
CPCC04B33/1324C04B33/1321C04B33/131C04B38/02C04B38/067C04B38/068C04B2235/3418C04B2235/3217C04B2235/3272C04B2235/3208C04B2235/3206C04B2235/3201C04B2235/3826C04B2235/422C04B2235/3267C04B2235/96C04B2235/77C04B2235/9607C04B38/0067Y02P40/60
Inventor 朱祥辉
Owner FUJIAN DESHENG NEW BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com