Preparation method of 310S stainless steel and 310S stainless steel

A technology for stainless steel and stainless steel strips, applied in the direction of manufacturing tools, heat treatment equipment, furnace types, etc., can solve the problems of longitudinal cracks in the casting billet, difficulty in meeting steel grade requirements, and difficulty in deoxidation, and achieve the goal of reducing oxygen content and improving product surface quality. Effect

Active Publication Date: 2020-01-10
ZHANGJIAGANG POHANG STAINLESS STEEL
View PDF16 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage is that the production of 310S stainless steel is more difficult: deoxidation is more difficult, and the ordinary production process can only reach the oxygen content level of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of 310S stainless steel and 310S stainless steel
  • Preparation method of 310S stainless steel and 310S stainless steel
  • Preparation method of 310S stainless steel and 310S stainless steel

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0039] The present invention will be further described below in conjunction with specific embodiments.

[0040] A 310S stainless steel, in terms of mass percentage, the 310S stainless steel includes the following components: C: 0.03-0.06; Si: 0.40-0.70; Mn: 1.30-1.60; P≤0.025; S≤0.0010; Cr: 25.30-25.90 ; Ni: 19.00~19.80; Mo: 0~0.5; N: 0.02~0.05; Cu: 0~0.5; Al: 0~0.1200; Cr is formed on the surface during isothermal oxidation at ℃ 2 O 3 Protective oxide film without internal oxidation; at the same time, increasing the nickel content can improve the adhesion of the oxide film, reduce peeling, and greatly improve its high temperature oxidation resistance. The preparation method of the 310S stainless steel includes smelting→continuous casting→hot rolling→annealing and pickling;

[0041] The smelting steps include:

[0042] A1) EAF (Electric Furnace) melts the alloy and scrap steel, the temperature reaches 1550 ℃, and the slag is removed after tapping;

[0043] A2) AOD (Argon ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of 310S stainless steel and the 310S stainless steel. The 310S stainless steel is prepared from the following components in percent by mass: 0.03-0.06% ofC, 0.40-0.70% of Si, 1.30-1.60% of Mn, less than or equal to 0.025% of P, less than or equal to 0.0010% of S, 25.30-25.90% of Cr, 19.00-19.80% of Ni, 0-0.5% of Mo, 0.02-0.05% of N, 0-0.5% of Cu, 0-0.1200% of Al and the balance Fe. The preparation method comprises the following steps: smelting; continuous casting; hot rolling; annealing and pickling. The preparation method has the beneficial effects that the oxygen content of plain steel is reduced effectively by controlling the oxygen content precisely, so that the surface quality of a product is enhanced; surface scales are easy to clean, andthe 310S stainless steel has excellent heat resistance and is suitable for a severe high-temperature environment.

Description

technical field [0001] The invention belongs to the technical field of stainless steel production, and in particular relates to a 310S stainless steel applicable to a high-temperature-resistant environment in the petrochemical industry and a preparation method thereof. Background technique [0002] With the development of the petrochemical industry, more and more operations are carried out under high temperature conditions, but equipment materials at high temperatures are prone to corrosion and failure. In the prior art, 310S stainless steel (2520) is an austenitic chromium-nickel stainless steel. Due to its high content of nickel (Ni) and chromium (Cr), it has good oxidation resistance, corrosion resistance, acid and salt resistance, and high temperature resistance. It is widely used in the petrochemical industry. There are many applications. The disadvantage is that the production of 310S stainless steel is more difficult: deoxidation is more difficult, and the ordinary p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C33/06B22D11/22C21D1/26C21D6/00C21D8/02C21D9/54C22C38/02C22C38/04C22C38/06C22C38/42C22C38/44C22C38/58C23G1/08C23G3/02
CPCB22D11/225C21D1/26C21D6/004C21D6/005C21D6/008C21D8/0226C21D9/54C22C33/06C22C38/001C22C38/002C22C38/02C22C38/04C22C38/06C22C38/42C22C38/44C22C38/58C23G1/086C23G3/02Y02P10/20
Inventor 陈功荣青亮林鸿亮
Owner ZHANGJIAGANG POHANG STAINLESS STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap