A kind of preparation method of moxifloxacin synthesis catalyst

The technology of catalyst and auxiliary agent is applied in the field of preparation of catalyst for moxifloxacin synthesis, which can solve the problems of high price, restricting production cost and the like, and achieve the effects of improving stability, strong binding ability and enhancing anti-nitrogen poisoning ability.

Active Publication Date: 2022-05-03
XIAN CATALYST NEW MATERIALS CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Palladium carbon catalyst is a kind of excellent hydrogenation and hydrogenolysis catalyst, is widely used in drug synthesis process, and it has advantages such as small consumption and environmental protection, but its price is expensive, restricts the production cost of moxifloxacin drug to a large extent, therefore Good catalyst activity, selectivity and mechanical performance are the key to the production cost of moxifloxacin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of moxifloxacin synthesis catalyst
  • A kind of preparation method of moxifloxacin synthesis catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The moxifloxacin synthesis catalyst of the present embodiment comprises activated carbon carrier, the oxide compound of the auxiliary agent element loaded on the activated carbon, and the active component Pd supported on the activated carbon; the auxiliary agent element is Si, the mass of the auxiliary agent element Be 1% of activated carbon mass, the mass percentage composition of active component Pd in ​​the catalyst is 5%;

[0025] The preparation method of described catalyst comprises the following steps:

[0026] Step 1. Weigh the specific surface area to be 820m 2 / g, 30g of activated carbon with a particle size of 200 to 400 meshes, place the weighed activated carbon in a hydrogen peroxide solution with a mass concentration of 5%, stir for 4 hours at 15°C, and wash the retentate with deionized water after filtration until neutral , to obtain activated carbon carrier after drying;

[0027] Step 2: Dissolve 3.04g sodium silicate nonahydrate in deionized water, th...

Embodiment 2

[0030] The moxifloxacin synthesis catalyst of the present embodiment comprises activated carbon carrier, the oxide compound of the auxiliary agent element loaded on the activated carbon, and the active component Pd supported on the activated carbon; the auxiliary agent element is Al, the mass of the auxiliary agent element Be 2% of activated carbon quality, the mass percentage composition of active component Pd in ​​the catalyst is 5%;

[0031] The preparation method of described catalyst comprises the following steps:

[0032] Step 1. Weigh the specific surface area to be 989m 2 / g, 30g of activated carbon with a particle size of 200 to 400 meshes, place the weighed activated carbon in a hydrogen peroxide solution with a mass concentration of 10%, stir at 30°C for 2 hours, and wash the retentate with deionized water after filtration until neutral , to obtain activated carbon carrier after drying;

[0033] Step 2: Dissolve 8.34g aluminum nitrate nonahydrate in deionized wate...

Embodiment 3

[0036] The moxifloxacin synthesis catalyst of the present embodiment comprises activated carbon carrier, the oxide compound of the auxiliary agent element loaded on the activated carbon, and the active component Pd supported on the activated carbon; the auxiliary agent element is Zr, and the mass of the auxiliary agent element Be 3% of activated carbon mass, the mass percentage composition of active component Pd in ​​the catalyst is 5%;

[0037] The preparation method of described catalyst comprises the following steps:

[0038] Step 1. Weigh the specific surface area to be 1463m 2 / g, 30g of activated carbon with a particle size of 200 to 400 meshes, place the weighed activated carbon in an aqueous solution of hydrogen peroxide with a mass concentration of 8%, stir for 3 hours at 25°C, and wash the retentate with deionized water after filtration until neutral , to obtain activated carbon carrier after drying;

[0039] Step 2: Dissolve 4.25g zirconium nitrate pentahydrate in d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a catalyst for moxifloxacin synthesis. The catalyst includes activated carbon, an oxide of an auxiliary element loaded on the activated carbon, and an active component Pd loaded on the activated carbon; the auxiliary element It is Si, Al or Zr; the preparation method of the catalyst includes: 1. preparation of activated carbon carrier; 2. oxide modified activated carbon carrier; The present invention changes the acidity and alkalinity of the surface of the catalyst by preferentially adsorbing the oxide of the auxiliary element on the activated carbon, thereby enhancing the ability of the catalyst to resist nitrogen poisoning, and at the same time, the active component palladium and the oxide of the auxiliary element have a strong binding ability, The performance degradation of the catalyst caused by the loss of active component metal is avoided, and the use of ethylene glycol aqueous solution as the impregnation solvent makes it easier to control the distribution depth of the active component on the carrier, forming a protein-type distribution with anti-toxicity, and improving the stability of the catalyst.

Description

technical field [0001] The invention belongs to the technical field of preparation of noble metal catalysts, in particular to a method for preparing a moxifloxacin synthesis catalyst. Background technique [0002] Moxifloxacin, the chemical name is 1-cyclopropyl-7-[(S,S)-2,8-diazabicyclo[4.3.0]-nonan-8-yl]-6-fluoro-8- Methoxy-1,4-dihydro-4-oxo-3-quinoline carboxylic acid is a fourth-generation broad-spectrum fluoroquinolone antibacterial drug developed by Bayer AG of Germany and launched in Germany in 1999. It is clinically used For the treatment of chronic obstructive pulmonary disease, acute bacterial sinusitis, and skin and soft tissue infections, the drug has strong antibacterial activity, broad antibacterial spectrum, and is not prone to drug resistance. In 2002, it entered the top ten best-selling antibiotic drugs in the world. In the second half of 2002, moxifloxacin was listed in my country. In 2004, the drug entered the national medical insurance catalog, and the m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/44C07D471/04
CPCB01J23/44C07D471/04
Inventor 王昭文翟康张磊李岳锋闫江梅万克柔曾永康张之翔
Owner XIAN CATALYST NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products