Putty powder for exterior wall and preparation method thereof

A technology of exterior wall putty and raw materials, which is applied in the direction of filling slurry, etc., can solve the problems of difficulty in adjusting the thickness of exterior wall putty, variability of mastic thickness, bulkiness and workability that cannot meet the adjustment thickness, etc., to achieve strong heat preservation, The effect of increased density and high flatness

Active Publication Date: 2020-01-24
浙江壁灵宝建材科技有限公司
View PDF7 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because of the thickness variability, bulkiness and workability of the existing cement, it is impossible to adjust the thickness
When workers use exterior wall putty to stick tiles, if they do not grasp the amount, it is difficult to adjust the thickness of exterior wall putty after the wall is installed, especially for new workers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Example 1 External wall putty powder 1#

[0040] The exterior wall putty powder 1# is made from raw materials including the following parts by weight: 350 parts of heavy calcium, 400 parts of quartz sand, 300 parts of white cement, 20 parts of latex powder, 4 parts of cellulose ether, 0.5 part of starch ether and silicic acid 1 part magnesium aluminum.

[0041] The preparation method of exterior wall putty powder 1# is as follows:

[0042] 1) Under the rotating state of the mixer at 60 rpm, first pour 175 parts of heavy calcium, 400 parts of quartz sand and 60 parts of white cement, and stir evenly;

[0043] 2) Keep the speed of the mixer, and continue to put 20 parts of latex powder, 4 parts of cellulose ether, 0.5 part of starch ether and 1 part of magnesium aluminum silicate into the mixer, and stir evenly;

[0044] 3) Continue to put 175 parts of heavy calcium into the mixer and stir evenly.

[0045] During construction of exterior wall putty powder 1#, the weigh...

Embodiment 2

[0046] Example 2 External wall putty powder 2#

[0047] External wall putty powder 2# is made from the following raw materials in parts by weight: 350 parts of heavy calcium, 400 parts of quartz sand, 300 parts of white cement, 20 parts of latex powder, 4 parts of cellulose ether, 0.5 part of starch ether, silicic acid 1 part of magnesium aluminum, 8 parts of rubber ball, 2 parts of polyvinyl alcohol, 4 parts of pregelatinized starch, 2 parts of wood fiber and 4 parts of ash calcium powder;

[0048] Wherein, the particle size distribution of the rubber balls includes 20 wt% of 10-30 μm, 30 wt% of 31-70 μm and 50 wt% of 77-100 μm.

[0049] The preparation method of exterior wall putty powder 2# is as follows:

[0050] 1) Under the rotating state of the mixer at 60 rpm, first pour 175 parts of heavy calcium, 400 parts of quartz sand and 60 parts of white cement, and stir evenly;

[0051] 2) Keep the speed of the mixer, and continue to put into the mixer 20 parts of latex powde...

Embodiment 3

[0054] Example 3 External wall putty powder 3#

[0055] External wall putty powder 3# is made from raw materials including the following parts by weight: 350 parts of heavy calcium, 400 parts of quartz sand, 300 parts of white cement, 20 parts of latex powder, 4 parts of cellulose ether, 0.5 part of starch ether, silicic acid 1 part of magnesium aluminum, 8 parts of rubber ball, 2 parts of polyvinyl alcohol, 4 parts of pregelatinized starch, 2 parts of wood fiber and 8 parts of light calcium carbonate;

[0056] Wherein, the particle size distribution of the rubber balls includes 20 wt% of 10-30 μm, 30 wt% of 31-70 μm and 50 wt% of 77-100 μm.

[0057] The preparation method of exterior wall putty powder 3# is as follows:

[0058] 1) Under the rotating state of the mixer at 60 rpm, first throw in 350 parts of heavy calcium, 400 parts of quartz sand, and 300 parts of white cement, and stir evenly;

[0059] 2) Keep the speed of the mixer, and continue to put into the mixer 20 pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses putty powder for an exterior wall and a preparation method thereof, belonging to the field of building coatings. The putty powder for the exterior wall is prepared from the following raw materials in parts by weight: 300-400 parts of ground calcium carbonate, 250-350 parts of white cement, 350-500 parts of quartz sand, 12-30 parts of latex powder, 4-5 parts of cellulose ether, 0.1-2 parts of starch ether and 1-3 parts of magnesium aluminum silicate. The thickness of the exterior wall putty powder can be finely adjusted; tiles pasted by using the exterior wall putty powder are high in flatness; and the putty powder is strong in heat preservation perfromance, good in constructability and high in viscosity.

Description

technical field [0001] The application relates to an exterior wall putty powder and a preparation method thereof, belonging to the field of architectural coatings. Background technique [0002] Putty powder for exterior walls is also called cement, which is used for viscose for tiling. Because the thickness variability, bulkiness, and workability of the existing cement cannot meet the adjustment thickness. When workers use exterior wall putty to stick tiles, if they do not grasp the amount, it is difficult to adjust the thickness of exterior wall putty after the wall is installed, especially for new workers. Contents of the invention [0003] In order to solve the above problems, an exterior wall putty powder with improved comprehensive performance and a preparation method thereof, especially a putty powder with improved construction performance, are provided. The thickness of the putty powder for external walls can be fine-tuned, and the use of the putty powder for exte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 钱国林
Owner 浙江壁灵宝建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com