Preparation method for optimizing thermoelectric performance of silver selenide/nylon flexible composite film

A composite thin film and thermoelectric performance technology, which is applied in the manufacture/processing of thermoelectric devices, thermoelectric device components, thermoelectric device node lead-out materials, etc., can solve the problem that the carrier concentration of the film is not optimized and the thermoelectric performance is selenized Silver gap, low power factor and other issues, to achieve the effect of improved thermoelectric performance, improved electrical conductivity, and excellent flexibility

Active Publication Date: 2020-02-21
TONGJI UNIV
View PDF8 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the thermoelectric performance of this thin film is still far from that of the existing high-performance bulk AgSe, mainly due to three aspects: (1) The sintering of uniform nanowires is challenging, resulting in the hot-pressed thin film being Porous structure, low density (relative density 70%); (2) The silver selenide grains of the film have an obvious preferred orientation in the (00l) direction, and the first-principle calculations show that in (00l), (0l0 ), (100) in the three directions, the silver selenide grains in the (00l) direction have the lowest power factor; (3) The carrier concentration of the film is not optimized

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for optimizing thermoelectric performance of silver selenide/nylon flexible composite film
  • Preparation method for optimizing thermoelectric performance of silver selenide/nylon flexible composite film
  • Preparation method for optimizing thermoelectric performance of silver selenide/nylon flexible composite film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A preparation of high thermoelectric performance silver selenide (Ag 2 Se) / nylon flexible composite film method, the method will 20ml selenium nanowire (Se) ethylene glycol (EG) dispersion (45mmol / L), 0.6g silver nitrate (AgNO 3 ) and 80ml of ethylene glycol were added to the beaker, stirred at 40°C for 2 hours, centrifuged at a speed of 4000r / min, and the black precipitate was extracted, then deionized water and absolute ethanol were added alternately and washed by centrifugation at a speed of 4000r / min for 3 minutes To remove impurities, after the centrifugation, the carefully cleaned black target product was dispersed in 15ml of absolute ethanol for ultrasonic dispersion for 15min, and then the nylon filter was used as a substrate to obtain a silver selenide / nylon flexible membrane by vacuum filtration. The film was dried in a vacuum oven at 60 °C for 12 h. After the film is taken out, it is hot-pressed at 200°C and 1MPa for 30 minutes, and the power factor can be o...

Embodiment 2

[0047] A method for preparing silver selenide / nylon flexible composite film with high thermoelectric performance, the method is ethylene glycol (EG) dispersion (45mmol / L) of 20ml selenium nanowire (Se), silver nitrate (AgNO 3 , the amount added meets the molar ratio of silver nitrate and selenium nanowires is 2:1) and 80ml of ethylene glycol were added to the beaker, stirred at 40°C for 1.5h, centrifuged at a speed of 4000r / min, and the resulting black precipitate was extracted, and the Alternately add deionized water and absolute ethanol, and centrifuge at a speed of 4000r / min for 3 minutes to remove impurities. After centrifugation, disperse the carefully cleaned black target product in 15ml of absolute ethanol for 15 minutes and ultrasonically disperse it with a nylon filter membrane. The substrate was vacuum filtered to obtain a silver selenide / nylon flexible film, and the obtained film was dried in a vacuum drying oven at a temperature of 60° C. for 12 hours. After the me...

Embodiment 3

[0049] A method for preparing silver selenide / nylon flexible composite film with high thermoelectric performance, the method is with the ethylene glycol (EG) dispersion (10mmol / L) of 20ml selenium nanowire (Se), silver nitrate (AgNO 3 , the amount added meets the molar ratio of silver nitrate and selenium nanowires is 4:1) and 80ml of ethylene glycol were added to the beaker, stirred at 40°C for 2.5h, centrifuged at a speed of 4000r / min, and the resulting black precipitate was extracted, and the Alternately add deionized water and absolute ethanol, and centrifuge at 4000r / min for 5min to remove impurities. After centrifugation, disperse the carefully cleaned black target product in 15ml of absolute ethanol for 15min and ultrasonically disperse it with a pore size of 0.22μm. The nylon filter membrane was used as the substrate, and the silver selenide / nylon flexible membrane was obtained by vacuum filtration, and the obtained membrane was dried in a vacuum drying oven at a temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
diameteraaaaaaaaaa
electrical conductivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method for optimizing the thermoelectric performance of a silver selenide / nylon flexible composite film, and the method comprises the following steps: (1) takinga selenium nanowire as a template, enabling the selenium nanowire to react with silver nitrate in an ethylene glycol solvent at 40 DEG C, and carrying out separation, thereby obtaining a silver selenide nanostructure; (2) dispersing the silver selenide nanostructure in absolute ethyl alcohol, taking a nylon filter membrane as a substrate, and performing suction filtration and drying to obtain a nylon-silver selenide film; and (3) finally, carrying out hot pressing treatment on the nylon-silver selenide film obtained in the step (2) to obtain a target product. Compared with the prior art, themethod has the advantages that the high-performance flexible thermoelectric thin film can be prepared, and the thin film is used for manufacturing a high-output-performance thermoelectric device to supply power to a wearable electronic device.

Description

technical field [0001] The invention belongs to the technical field of thermoelectric material preparation, and relates to a preparation method for optimizing the thermoelectric performance of silver selenide / nylon flexible composite film. Background technique [0002] Thermoelectric materials are a class of functional materials that can directly convert thermal energy to electrical energy. Thermoelectric power generation and refrigeration devices prepared by thermoelectric materials have the advantages of simple structure, small size, no moving parts, no wear, no noise, no pollution, etc. As an environmentally friendly material, thermoelectric materials have broad application prospects. [0003] The performance index of thermoelectric materials is generally measured by the dimensionless figure of merit ZT, and its expression is as follows: [0004] ZT = α 2 σT / κ where: [0005] α is the Seebeck coefficient; σ is the electrical conductivity; κ is the thermal conductivity...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01L35/34H01L35/16H01L35/02H10N10/01H10N10/80H10N10/852
CPCH10N10/80H10N10/852H10N10/01
Inventor 蔡克峰蒋聪丁宇飞童亮
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com