Steel for ball screw bearing and manufacturing method thereof

A technology of steel for bearings and ball screws, applied in bearings, manufacturing tools, shafts and bearings, etc., can solve the problems of easy generation of bainite structure, easy deformation of heat treatment, high hardenability of steel, etc., and achieve secondary branching The effect of improving crystal arm spacing, improving and reducing composition segregation, and uniform rod structure

Active Publication Date: 2020-04-10
JIANGYIN XINGCHENG SPECIAL STEEL WORKS CO LTD
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] At present, the medium-carbon ball screw bearing steel used at home and abroad is mainly 50CrMo, which has high alloy element content and belongs to ultra-high-strength alloy-bonded structural steel. After quenching and tempering, the strength and toughness are high, but due to the high alloy content, the cost is high. , In addition, due to the high alloy content and high hardenability of the steel, it is easy to produce bainite structure after quenching and tempering, and subsequent heat treatment is easy to cause deformation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel for ball screw bearing and manufacturing method thereof
  • Steel for ball screw bearing and manufacturing method thereof
  • Steel for ball screw bearing and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0065] The present invention will be described in further detail below in conjunction with the examples, which are exemplary and intended to explain the present invention, but should not be construed as a limitation of the present invention.

[0066] The manufacturing process of the steel for roller screw bearings of the present invention: primary smelting in electric furnace or converter—LF refining outside furnace—VD or RH vacuum degassing—continuous casting—squaring of continuous casting slab into intermediate billet—heating and rolling of intermediate billet into slab— Finishing - quenching and tempering heat treatment - car polishing - packing into storage.

[0067] Molten steel smelting: When smelting, use high-quality molten iron, scrap steel, high-quality deoxidizer and refractory materials. During the initial smelting production process, the tapping endpoint C is controlled at 0.10-0.25%, and the endpoint P is required to be ≤0.020%. Using the relationship between C a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention relates to steel for a ball screw bearing. Alloy components of the steel comprise, by mass, 0.45-0.60% of C, 0.15-0.40% of Si, 0.50-0.80% of Mn, 0.15-0.40% of Cr, 0.002-0.006% of B, 0.02-0.07% of V, less than or equal to 0.015% of S, less than or equal to 0.025% of P, less than or equal to 0.10% of Mo, less than or equal to 0.08% of Al, less than or equal to 0.0010% of Ca, less thanor equal to 0.0010% of O, less than or equal to 0.04% of As, less than or equal to 0.03% of Sn, less than or equal to 0.005% of Sb, less than or equal to 0.002% of Pb, and the balance Fe and inevitable impurities. A preparation process of a bar product comprises the steps of molten steel smelting, continuous casting, cogging-down, hot rolling, tempering, stress relief annealing and the like. The final properties meet the conditions that the surface hardness of the bar reaches 220-260 HBW, the metallographic structure of the bar is a uniform sorbite structure, the austenitic grain size of the bar is higher than or equal to the seven-level, the yield strength of the bar is 600-800 MPa, the tensile strength of the bar is 800-900 MPa, and the percentage elongation of the bar is greater than orequal to 15%.

Description

technical field [0001] The present invention relates to the manufacture of bearing steels in iron-based alloys. Background technique [0002] The ball screw pair is one of the commonly used transmission devices in transmission machinery that uses the rolling of balls between the screw and the nut to simultaneously realize the functions of power transmission and motion conversion. It has the characteristics of high precision, high efficiency and reversibility at the same time. It has become the key executive component in the driving process of various CNC machine tools, automated machinery and machining centers. It is widely used in automobiles, machinery, nuclear industry, aviation, aerospace, etc. field. The rolling screw pair is usually composed of four parts: the screw bearing, the ball, the nut and the ball circulation return device. [0003] The ball screw bearing is the key component of the ball screw pair. The surface hardness and wear resistance of the ball screw b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/22C22C38/24C22C38/32C22C38/60C21D1/25C21D1/26C21C7/10C21C7/06C21D8/02
CPCC22C38/02C22C38/04C22C38/32C22C38/24C22C38/22C22C38/60C22C38/06C22C38/008C22C38/002C21D1/25C21D1/26C21C7/10C21C7/06C21D8/0226C21D2211/00F16C33/62F16C33/64F16C2204/64F16C2202/04F16C2204/74F16C2202/06C21D6/002C21D6/008C21D9/525C21D1/30C21D9/0081C21D1/60C21D9/36C21D1/84C21D2211/009C21D8/065C21D8/0247C21D8/0273
Inventor 陈敏耿克尹青李锋许晓红白云吴小林
Owner JIANGYIN XINGCHENG SPECIAL STEEL WORKS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products