Special calcium powder production material for MS glue and production method thereof
A production method and technology of calcium powder, applied in the field of calcium powder production materials for MS glue, can solve the problems of wide particle size distribution, weak tensile strength, poor thixotropic performance, etc., achieve narrow particle size distribution and improve performance , the effect of reducing production costs
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0024] A special calcium powder production material for MS glue, consisting of the following raw materials:
[0025] Materials; 600 mesh coarse powder 700kg, water 300kg, dispersant 2.8kg, solid calcium powder, silane coupling agent;
[0026] The water used is production water, and after disinfection and other treatment, select suitable soft water or hard water according to the needs;
[0027] The main component of the dispersant is: sodium polyacrylate, and the addition amount is 4‰ of the powder. The industrial sodium polyacrylate meets the standard: HG / T2838-2010. The standard stipulates that the product appearance is colorless to yellow liquid, and the solid content is greater than or equal to 30%. According to the softness and hardness of water, the viscosity of sodium polyacrylate is adjusted and selected.
Embodiment 2
[0029] A kind of production method of calcium powder special for MS glue, comprises the following steps:
[0030] Step 1: take each raw material in proportion for subsequent use;
[0031] Step 2: Stir the 600-mesh coarse powder, water, and dispersant evenly (powder: water = 7:3, and the amount of dispersant is 4‰ of the powder) using a stirring device for 20 minutes at high speed, and the stirring speed per minute is not Less than 900 rpm;
[0032] Step 3: Pour the mixed raw materials that have been stirred into the water mill for grinding. The water mill realizes grinding through the feeding part, the discharging part, the turning part, the transmission part (reducer, small transmission gear, motor, electric control), etc.;
[0033] Step 4: Obtain a 2500-3000 mesh fine powder slurry by grinding, and make the solid content reach about 85%, and at the same time mix 1.5‰ of solid calcium powder (stearic acid);
[0034] Step 5: Pour the mixed raw materials into the drum dryer f...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap