Anti-static pearl wool and preparation method thereof

A pearl cotton and anti-static technology, which is applied in the field of anti-static pearl cotton and its preparation, can solve problems such as short circuit, damage, instability, etc., and achieve the effects of reducing manufacturing costs, good anti-static effect, and reducing space occupation

Inactive Publication Date: 2020-04-21
平湖市富利源塑业有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although there are anti-static pearl cotton on the market, most of these anti-static can only be maintained for half a year - a year or so. Once the temperature is low in winter, the anti-static effect is very unstable. If it is used in electronic Product chip circuit protection, it is easy to short circuit, and then damage the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1: antistatic pearl cotton, its preparation raw material comprises by weight: polyethylene 100 parts, antistatic agent 3 parts, titanate modified calcium carbonate 10 parts, talcum powder 1 part, silane coupling agent 1 part, 10 parts of mixed foaming agent; Wherein, described mixed foaming agent comprises the mixture of monoglyceride and butane, and mixed foaming agent is 4 parts of monoglyceride and 6 parts of butane, and the weight of butane accounts for the mixture of mixed foaming agent 60% by total weight.

[0033] In the present invention, in a specific embodiment, polyethylene can be conventional polyethylene pellets used to prepare pearl cotton materials in the art, and the melt index of polyethylene pellets generally used to prepare pearl cotton materials is between 1.8 and 1.8. 7g / 10min; polyethylene pellets can be purchased from Saudi Arabia (Arabia) product FT4119, product 2420E02 from Iran Petrochemical, product 2420 from Yamba, product 2023NN f...

Embodiment 2

[0053] Antistatic pearl cotton, its preparation raw materials include by weight: its preparation raw materials include by weight: 120 parts of polyethylene, 4 parts of antistatic agent, 15 parts of titanate modified calcium carbonate, 2 parts of talcum powder, silane coupling 2 parts of agent, 14 parts of mixed foaming agent; Wherein, described mixed foaming agent comprises the mixture of monoglyceride and butane, and mixed foaming agent is 5.6 parts of monoglyceride and 8.4 parts of butane, and the weight of butane accounts for The total weight of the mixed blowing agent is 60%.

[0054] The preparation method of antistatic pearl cotton comprises the following steps:

[0055] Step (1), batching, dry 2 parts of talcum powder and 15 parts of titanate-modified calcium carbonate, pass through a 100-150 mesh sieve, add to a high-speed mixer, and set the temperature at 110-120°C at a speed of 500-1000rpm Stir and mix for 20-30min, then add 2 parts of silane coupling agent and blen...

Embodiment 3

[0064] Antistatic pearl cotton, its preparation raw materials include by weight: its preparation raw materials include by weight: 155 parts of polyethylene, 5 parts of antistatic agent, 19 parts of titanate modified calcium carbonate, 3 parts of talcum powder, silane coupling 3 parts of agent, 20 parts of mixed foaming agent; Wherein, described mixed foaming agent comprises the mixture of monoglyceride and butane, and mixed foaming agent is 10 parts of monoglyceride and 10 parts of butane, and the weight of butane accounts for The total weight of the mixed blowing agent is 50%.

[0065] The preparation method of antistatic pearl cotton comprises the following steps:

[0066] Step (1), batching, dry 3 parts of talcum powder and 19 parts of titanate-modified calcium carbonate, pass through a 100-150 mesh sieve, add to a high-speed mixer, and set the temperature at 110-120°C at a speed of 500-1000rpm Stir and mix for 20-30min, then add 3 parts of silane coupling agent and blend ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to antistatic pearl wool and a preparation method thereof. The antistatic pearl wool comprises the following preparation raw materials in parts by weight: 100-155 parts of polyethylene, 3-5 parts of an antistatic agent, 10-19 parts of titanate modified calcium carbonate, 1-3 parts of talcum powder, 1-3 parts of a silane coupling agent and 10-20 parts of a mixed foaming agent,wherein the mixed foaming agent comprises a mixture of monoglyceride and butane, and the weight of monoglyceride accounts for less than or equal to 80% of the total weight of the mixed foaming agent;polyethylene particles, special anti-static water-soluble particles and the like are preferably selected to be mixed according to a certain proportion, a certain amount of butane gas and monoglyceride are introduced through a pressure pump to serve as foaming agents. Compared with the common anti-static pearl wool, the anti-static pearl wool has a better anti-static effect and the anti-static effect can be achieved for a long time.

Description

technical field [0001] The invention belongs to the technical field of pearl cotton, and in particular relates to an antistatic pearl cotton and a preparation method thereof. Background technique [0002] EPE pearl cotton has a non-cross-linked closed-cell structure. It is a high-foam polyethylene product extruded from low-density polyethylene (LDPE) as the main raw material. It is also called polyethylene foam cotton. It is a new type of environmentally friendly packaging material. Because it is composed of numerous independent bubbles produced by physical foaming of low-density polyethylene resin, it overcomes the shortcomings of ordinary foam rubber such as fragility, deformation, and poor recovery, and has good water and moisture resistance, shock resistance, sound insulation, heat preservation, and good plasticity. , Strong toughness, recycling, environmental protection, strong impact resistance, etc., also has good chemical resistance. [0003] Although there are anti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L71/02C08L33/04C08L87/00C08K13/06C08K9/04C08K3/26C08K3/34C08J9/14B65H23/195B65H27/00
CPCB65H23/195B65H27/00C08J9/0061C08J9/0071C08J9/009C08J9/141C08J9/142C08J2203/12C08J2203/14C08J2203/182C08J2323/06C08J2433/04C08J2471/02C08J2487/00C08K3/34C08K9/04C08K13/06C08K2003/265
Inventor 孙亚平吴彬枫许万陈斌斌曾荣
Owner 平湖市富利源塑业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More