Biodegradable straw and preparation method thereof

A straw and biological technology, which is applied to straw materials and their preparation, biodegradable straws and their preparation fields, can solve the problems of poor mechanical properties, easy breeding of harmful microorganisms, low heat-resistant temperature and easy degradation, etc., so as to improve strength, reduce Hydrolysis phenomenon, the effect of improving compatibility

Active Publication Date: 2020-04-21
NANJING PRIDE PLASTIC TECH
View PDF12 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Purpose of the invention: In view of the problems of poor mechanical properties, low heat-resistant temperature, easy degradation, and easy breeding of harmful microorganisms in th

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biodegradable straw and preparation method thereof
  • Biodegradable straw and preparation method thereof
  • Biodegradable straw and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] Example 1

[0019] The weight content of each raw material component in the biodegradable straw is:

[0020]

[0021] The preparation process of the biodegradable straw is as follows:

[0022] (1) Add 6.3 parts of bamboo powder to the high-speed mixer, set the temperature of the equipment to 80℃, and set the stirring speed to 500r / min. After turning on the equipment, slowly add 0.6 parts of aluminum titanium coupling agent from the feeding port and continue stirring After 10 minutes, turn off the equipment to form a bamboo powder pretreatment material.

[0023] (2) According to the set ratio, add 80 parts of PLA and 10 parts of PHA to the high-speed mixer. The mixing speed is set to 100r / min. After turning on the equipment, first add 2 parts of epoxy soybean oil, and then sequentially Add bamboo powder pretreatment material, lubricant and anti-hydrolysis agent, and continue to stir for 10 minutes to form a polylactic acid mixture.

[0024] (3) The polylactic acid mixture is add...

Example Embodiment

[0025] Example 2

[0026] The weight content of each raw material component in the biodegradable straw is:

[0027]

[0028] Refer to the preparation process of Example 1 to prepare a biodegradable straw, the difference lies in:

[0029] (1) In step 1, the stirring temperature is 100°C, and the stirring speed is 1000r / min. After adding the aluminum-titanium coupling agent, continue to stir for 15 minutes to form a bamboo powder pretreatment material;

[0030] (2) In step 3, the extrusion temperature is 150°C, the die temperature is 160°C; the cooling temperature is 42°C; and the pulling speed is 1.5 m / s.

Example Embodiment

[0031] Example 3

[0032] The weight content of each raw material component in the biodegradable straw is:

[0033]

[0034] Refer to the preparation process of Example 1 to prepare a biodegradable straw, the difference lies in:

[0035] (1) In step 1, the stirring temperature is 90°C, and the stirring speed is 600r / min. After adding the aluminum titanium coupling agent, continue to stir for 12 minutes to form the bamboo powder pretreatment material;

[0036] (2) In step 3, the extrusion temperature is 160°C, the die temperature is 200°C; the cooling temperature is 50°C; and the pulling speed is 1 m / s.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a biodegradable straw and a preparation method thereof. The straw comprises, by mass, 50%-80% of polylactic acid, 10%-40% of polyhydroxyalkanoate, 3%-12% of bamboo powder, 1%-2% of epoxidized soybean oil, 0.3%-1% of an aluminum-titanium coupling agent, 0.1%-1% of a lubricating agent and 0.1%-1% of an anti-hydrolysis agent. The preparation method comprises the following steps: uniformly stirring the bamboo powder and the aluminum-titanium coupling agent to obtain a bamboo powder pretreated material for later use; sequentially adding the epoxidized soybean oil, the bamboopowder pretreated material, the lubricant and the anti-hydrolysis agent into a resin mixture of the polylactic acid and the polyhydroxyalkanoate at a stirring speed of 100-250 r/min, and uniformly stirring to form a polylactic acid mixture; and adding the polylactic acid mixture into double-screw extrusion equipment, extruding a straw blank, and sequentially carrying out water cooling, air cooling, water removal and cutting on the straw blank under the traction of traction equipment to obtain the biodegradable straw product. The biodegradable straw material can effectively prolong the degradation time of the PLA straw, improve the mechanical properties of the PLA straw, and effectively improve the harmful bacterium inhibition ability of the straw.

Description

technical field [0001] The invention relates to a straw material and a preparation method thereof, in particular to a biodegradable straw and a preparation method thereof, and belongs to the technical field of polymer materials and processing thereof. Background technique [0002] Straw products are supplies for drinking various beverages. It greatly facilitates people's daily diet and life, and has become an indispensable article in daily life. However, traditional straw materials are usually polypropylene, etc., and the extensive use of these plastic straws, which have no recycling value and cannot be quickly degraded, has caused serious white pollution to people's living environment. Based on this, people began to use biodegradable material polylactic acid to replace traditional polypropylene straws. [0003] However, due to problems such as hardness, brittleness and poor toughness, polylactic acid materials cannot meet the production and molding requirements of existing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/04C08L97/02C08L91/00C08K5/10C08K5/20
CPCC08L67/04C08L2201/06C08L2201/08C08L2205/035C08L2205/025C08L97/02C08L91/00C08K5/10C08K5/20
Inventor 李进吴兴旺刘之烨戴春发王仕杰吴立丰
Owner NANJING PRIDE PLASTIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap