Crease resistant finishing agent for cotton fabric and crease resistant finishing method

An anti-wrinkle finishing agent, fabric technology, applied in the direction of fiber treatment, improved hand fiber, textiles and papermaking, etc., can solve the problems of formaldehyde content limitation, high price, restrictions, etc., achieve good whiteness, reduce production costs, reduce fabrics Intensity reduction effect

Inactive Publication Date: 2020-04-21
安徽捷融数据科技有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the gradual enhancement of people's awareness of environmental protection, there are more and more strict restrictions on the formaldehyde content of textiles in the world. The development and application of formaldehyde-free finishing agents is the main research direction of anti-wrinkle finishing. Among them, butane tetracarboxylic acid is recognized as the most Ideal replacement product, but limited in practical application due to its high price

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] An anti-wrinkle finishing method for cotton fabrics, comprising the following steps:

[0025] (1) Add 5 parts of pyromellitic dianhydride, 0.02 parts of nano-titanium dioxide, 0.5 parts of diethylaminomethyltriethoxysilane, 6 parts of quaternary ammonium cationic softener EQ-1, polyethylene Mix 7 parts of 500 diol and 45 parts of propylene glycol evenly, then heat up to 75°C, add 7 parts of butane tetracarboxylic acid, 4 parts of ethylenediamine tetraacetic acid, stir and dissolve, add 6 parts of chitosan, sodium hypophosphite 9 parts, fully stirred and dissolved to obtain anti-wrinkle finishing agent;

[0026] (2) Immerse the cotton fabric to be treated in the anti-wrinkle finishing agent, dipping and rolling twice, the liquid retention rate is 100%, and then pre-dry the cotton fabric, the pre-drying temperature is 65°C, and the pre-drying time is 3.5min ; Then bake at 165°C for 160s.

Embodiment 2

[0028] An anti-wrinkle finishing method for cotton fabrics, comprising the following steps:

[0029] (1) Add 6 parts of pyromellitic dianhydride, 0.03 parts of nano silicon dioxide, 0.4 parts of γ-(2,3-glycidoxy) propyltrimethoxysilane, polyamide cationic soft Mix 5 parts of agent HAS8601, 7 parts of polyethylene glycol 500, and 40 parts of propylene glycol, then heat up to 70°C, then add 8 parts of butane tetracarboxylic acid and 3 parts of ethylenediamine tetraacetic acid, stir to dissolve and add chitosan 5 parts, 7 parts of sodium hypophosphite, fully stirred and dissolved to obtain anti-wrinkle finishing agent;

[0030] (2) Immerse the cotton fabric to be treated in the anti-wrinkle finishing agent, two dipping and two rolling, the liquid retention rate is 100%, and then pre-dry the cotton fabric, the pre-drying temperature is 65 ° C, and the pre-drying time is 3 minutes; Then bake at 165°C for 150s.

Embodiment 3

[0032] An anti-wrinkle finishing method for cotton fabrics, comprising the following steps:

[0033] (1) Add 3.5 parts of pyromellitic dianhydride, 0.02 parts of nano-dioxide, 0.4 parts of γ-aminopropyltriethoxysilane, 6 parts of quaternary ammonium salt cationic softener EQ-1 to 1000 parts of water, Mix 7 parts of polyethylene glycol 500 and 50 parts of propylene glycol evenly, then heat up to 80°C, then add 8 parts of butane tetracarboxylic acid and 5 parts of ethylenediamine tetraacetic acid, stir and dissolve, add 5 parts of chitosan, 10 parts of sodium phosphate, fully stirred and dissolved to obtain anti-wrinkle finishing agent;

[0034] (2) Immerse the cotton fabric to be treated in the anti-wrinkle finishing agent, two dipping and two rolling, the liquid retention rate is 100%, and then pre-dry the cotton fabric, the pre-drying temperature is 70 ° C, and the pre-drying time is 4 minutes; Then bake at 160°C for 170s.

[0035] The nano-dioxide is composed of nano-titaniu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a crease resistant finishing agent for cotton fabric and a crease resistant finishing method, and relates to the technical field of garment fabric finishing. The crease resistant finishing agent for the cotton fabric is prepared from the following raw materials in parts by weight: 6-13 parts of butanetetracarboxylic acid, 3-7 parts of pyromellitic dianhydride, 3-6 parts of ethylenediamine tetraacetic acid, 3-7 parts of chitosan, 0.005-0.03 part of nano dioxide, 0.3-0.6 part of silane coupling agent, 4-8 parts of softening agent, 6-10.5 parts of sodium hypophosphite, 3-8parts of polyethylene glycol 500, 30-60 parts of propylene glycol and 1000 parts of water. Under the condition that a small amount of butanetetracarboxylic acid and sodium hypophosphite are used, thecotton fabric can be endowed with excellent comprehensive performance and is good in crease resistant effect, large in recovery angle, high in tear strength retention rate and good in whiteness.

Description

technical field [0001] The invention relates to the technical field of clothing fabric finishing, in particular to an anti-wrinkle finishing agent and an anti-wrinkle finishing method for cotton fabrics. Background technique [0002] Cotton fiber is a kind of natural cellulose fiber. Its microstructure is microfibrils formed by the aggregation of dozens of chain-like cellulose macromolecules. The microfibrils continue to aggregate into fibrils with a lateral size of about 10-25nm. Then the fibrils are arranged to form the sun ring layer, and finally the fibers are formed. The microscopic interior of cotton fibers is a porous material. Due to its own characteristics, it has good air permeability, moisture permeability and outstanding comfort, so it is loved by consumers. Due to the influence of various external factors during the wearing process, various creases and deformations are formed, which affects the appearance of the fabric on the one hand, and reduces the durabili...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/46D06M11/70D06M11/79D06M13/148D06M13/192D06M13/342D06M13/46D06M15/03D06M15/53D06M15/59D06M101/06
CPCD06M11/46D06M11/70D06M11/79D06M13/148D06M13/192D06M13/342D06M13/46D06M15/03D06M15/53D06M15/59D06M2101/06D06M2200/20D06M2200/50
Inventor 许克霞
Owner 安徽捷融数据科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com