A hydrocarbon resin and composite material technology, which is applied in the field of modified hydrocarbon resin synthesis and composite material board preparation, can solve problems such as uneven molecular weight distribution, damage stress, and cracking of polymers

Active Publication Date: 2020-04-28
SICHUAN DONGFANG INSULATING MATERIAL
View PDF10 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the reaction belongs to free radical polymerization, the polymerization speed is fast and explosive, the molecular weight distribution of the polymer is u

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified hydrocarbon resin prepolymer, modified hydrocarbon-DCPD epoxy composite material copper-clad plate and preparation method
  • Modified hydrocarbon resin prepolymer, modified hydrocarbon-DCPD epoxy composite material copper-clad plate and preparation method
  • Modified hydrocarbon resin prepolymer, modified hydrocarbon-DCPD epoxy composite material copper-clad plate and preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0085] Preparation of the prepreg: put the reinforcing material in the combined material solution (full) dipped and take it out, and then bake it at 120°C-185°C for 1-10min to prepare the modified hydrocarbon resin prepreg;

[0086] Preparation of modified hydrocarbon-DCPD epoxy composite material copper-clad laminate: the modified hydrocarbon-DCPD epoxy composite material prepreg and metal copper foil are cut and stacked according to the requirements of length, width and thickness, and then placed in a hot In the press, keep the heating rate at 1-3°C / min. After reaching the temperature, press at a pressure of 0.2-1MPa and a temperature of 80-150°C for 1-3 hours, and then continue to heat up, keeping the heating rate at 1-3°C / min. min, after reaching the temperature, press at a pressure of 2-7MPa and a temperature of 180-250°C for 1-6 hours to obtain it;

[0087] The comparison of some technical performances of the modified hydrocarbon-DCPD epoxy composite copper-clad laminate...

Embodiment 3

[0106] A modified hydrocarbon resin prepolymer, the modified hydrocarbon resin prepolymer is composed of 50 parts by mass of hydrocarbon resin, 50 parts by mass of a resin mixture containing double bond benzoxazine resin / modified polyphenylene ether resin 1. The composition of 1 mass part of initiator A and 110 mass parts of solvent A, the modified hydrocarbon resin prepolymer obtained by mixing and reacting in a microchannel reactor and removing part of the solvent.

Embodiment 4

[0108] A modified hydrocarbon resin prepolymer, the modified hydrocarbon resin prepolymer is a resin mixture composed of 200 parts by mass of hydrocarbon resin, 50 parts by mass of double bond-containing benzoxazine resin / modified polyphenylene ether resin 1. The composition of 5 parts by mass of initiator A and 280 parts by mass of solvent A, the modified hydrocarbon resin prepolymer obtained by mixing and reacting in a microchannel reactor and removing part of the solvent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Peel strengthaaaaaaaaaa
Glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a modified hydrocarbon resin prepolymer, a modified hydrocarbon-DCPD epoxy composite material copper-clad plate and a preparation method thereof. The modified hydrocarbon resinprepolymer is prepared by mixing and reacting 50-200 parts by mass of hydrocarbon resin, 50 parts by mass of a resin mixture containing double-bond benzoxazine resin/modified polyphenyl ether resin,1-5 parts by mass of an initiator A and 110-280 parts by mass of a solvent A through a micro-channel reactor and removing part of the solvent. The modified hydrocarbon-DCPD epoxy composite material copper-clad plate is prepared by thermally curing a composition and a copper foil, wherein the mass ratio of a modified hydrocarbon resin prepolymer to DCPD epoxy resin to an inorganic filler to an initiator B to an accelerant A to a reinforcing material is 90: (10-30): (40-100): (0.01-1): (0.01-1): (70-200); the ceramic has the characteristics of low dielectric constant, low dielectric loss, low water absorption, high glass-transition temperature and high peel strength.

Description

technical field [0001] The invention belongs to the field of modified hydrocarbon resin synthesis and preparation of composite material boards, and relates to a modified hydrocarbon resin prepolymer, a modified hydrocarbon-DCPD epoxy composite material copper-clad board and a preparation method. The modified hydrocarbon resin prepolymer of the present invention is especially suitable for the manufacture of high-frequency and high-speed copper clad laminates required by 5G communication. Background technique [0002] Due to the requirements of 5G communication data transmission rate and high reliability, the use of laminates and copper clad laminates has become a technical difficulty that must be overcome in terms of dielectric constant, dielectric loss factor and heat resistance. [0003] Because the polarity of C-H in the molecular chain of hydrocarbon resin is small (the electronegativity of C and H are 2.5 and 2.1 respectively), it has excellent dielectric properties (vol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G81/02C08F299/02C08L87/00C08L53/00C08L63/00C08L1/02C08K7/14C08J5/24C08J5/04
CPCC08F299/022C08G81/025C08J5/043C08J5/045C08J5/24C08J2353/00C08J2387/00C08J2401/02C08J2463/00
Inventor 支肖琼黄杰唐安斌李建学
Owner SICHUAN DONGFANG INSULATING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap