Permeable closed amphoteric emulsion for primer and preparation method thereof
A technology of sealing and primer, applied in the direction of primer, coating, etc., can solve the problems of vigorous promotion and application of unsealable primer, wall foundation reinforcement performance that cannot be loosened, and insufficient maintenance time of cement substrate, etc., to achieve excellent Penetration reinforcement performance, improvement of permeability performance, and strong anti-salinity performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0033] In addition, the present invention also provides a preparation method of the amphoteric emulsion for the penetration-blocking primer, comprising the following steps:
[0034] 1) Preparation of pre-emulsion: under normal temperature and pressure, add 1.5-3.75 parts of emulsifier and 40-85 parts of deionized water to the emulsification tank, after fully stirring and dissolving, slowly add the formula amount of benzene while stirring. Ethylene, n-butyl acrylate in formula, isooctyl acrylate in formula, glycidyl methacrylate in formula, cationic monomer in formula, anionic monomer in formula, hydrophilic monomer in formula, 0.4 -2 parts of cross-linking monomer and 0.3-1.2 parts of initiator, fully stirred for 30-40min to obtain pre-emulsion;
[0035] 2) Preparation of seed emulsion: under normal temperature and pressure, add the remaining amount of emulsifier and the remaining amount of deionized water into the reaction kettle, stir and dissolve fully, add hydrochloric aci...
Example Embodiment
[0038] Example 1
[0039] An amphoteric emulsion for penetrating and sealing primer, which is prepared by mass parts from the following raw materials: 60 parts of deionized water, 50 parts of styrene, 5 parts of n-butyl acrylate, 5 parts of isooctyl acrylate, and 2 parts of emulsifier parts, 2 parts of glycidyl methacrylate, 3 parts of dodecyl methacrylate, 3 parts of methyl erucate, 2 parts of cationic monomer, 2 parts of anionic monomer, 1 part of crosslinking monomer, hydrophilic 3 parts of monomer and 1 part of initiator.
[0040] The emulsifier is mixed with N-(1,2-dicarboxylate ethyl)-N-octadecylaminosulfosuccinylplatinate sodium salt and polyethylene glycol methacrylate in a mass ratio of 2:1. The crosslinking monomer adopts trimethylolpropane trimethacrylate.
[0041] The cationic monomer is mixed with acryloyloxyethyltrimethylammonium chloride and dimethyldiallylammonium chloride in a mass ratio of 1:1. The anionic monomer adopts acrylic acid.
[0042] The hydroph...
Example Embodiment
[0051] Example 2
[0052] An amphoteric emulsion for penetrating and sealing primer, which is prepared in parts by mass from the following raw materials: 70 parts of deionized water, 60 parts of styrene, 10 parts of n-butyl acrylate, 10 parts of isooctyl acrylate, and 3 parts of emulsifier parts, 5 parts of glycidyl methacrylate, 5 parts of dodecyl methacrylate, 5 parts of methyl erucate, 5 parts of cationic monomer, 3 parts of anionic monomer, 2 parts of cross-linking monomer, hydrophilic 5 parts of monomer and 1.5 parts of initiator.
[0053] The emulsifier is mixed with cetyltrimethylammonium bromide and allyloxy polyoxyethylene ether in a mass ratio of 5:1.
[0054] The cross-linking monomer is mixed with vinyl tri(methoxyethoxy) silane and pentaerythritol triallyl ether in a mass ratio of 1:1.
[0055] The cationic monomer is mixed with acryloyloxyethyltrimethylammonium chloride, dimethyldiallylammonium chloride and dimethylaminoethyl methacrylate in a mass ratio of 1:2...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap