Silver paste for multilayer wiring of low-temperature co-fired low-dielectric-constant dielectric ceramic
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A low dielectric constant, dielectric ceramic technology, applied in the field of materials, can solve problems such as unsuitable co-firing temperature, sintering mismatch, etc., and achieve the effect of eliminating silver diffusion phenomenon, clear pattern and excellent performance
Active Publication Date: 2020-06-19
LUOYANG INST OF SCI & TECH
View PDF10 Cites 7 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Application number: 201910312643.2 "A conductive silver paste for low-temperature sintering LTCC" solves the problem of sintering mismatch between DuPont paste and self-made LTCC ceramic
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0037] Sampling according to the following mass percentages: spherical silver powder 80wt%, aluminum borosilicate barium glass powder 0.5wt%, inorganic modifier TiO 2 0.5wt%, Fe 2 o 3 0.2wt%, organic vehicle 18.8wt%. The D50 of the spherical silver powder is 2.3 μm, and the tap density is 4.9 g / cm3. The preparation method is as described above. The prepared slurry has a viscosity of 260±50dPa ▪S, a slurry fineness≦8μm, and a solid content of 81.2%. It is used to make four-layer co-fired test samples, and the test results are shown in Table 2.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
D50
aaaaa
aaaaa
D50
aaaaa
aaaaa
D50
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to silver paste for multilayer wiring of low-temperature co-fired low-dielectric-constant dielectric ceramic, which belongs to the technical field of materials. The silver pastecomprises the components of, by mass, 80 to 90% of silver powder, 0.2 to 5% of an inorganic modifier, 0 to 3% of glass powder and 8 to 19.5% of an organic carrier. The silver paste can be co-fired with a microcrystalline glass and glass ceramic composite system low-temperature co-fired ceramic green tape at 850 DEG C, and has excellent matching performance. According to the multilayer wiring structure made of the silver paste, conductor silver wire patterns are clear, surrounding porcelain bodies do not turn yellow, and the bad silver diffusion phenomenon is eliminated.
Description
technical field [0001] The invention belongs to the technical field of materials, and relates to a silver paste, in particular to a silver paste for multilayer wiring used in low-permittivity co-fired dielectric ceramics. Background technique [0002] Low temperature co-fired ceramics (LTCC) technology is widely used in multilayer discrete components, such as capacitors, resistors, inductors, transformers; multilayer radio frequency, microwave, millimeter wave passive components; multilayer interconnect substrates and surface acoustic wave (SAW ) devices, and Si, GaAs, InP and other microwave devices and IC packaging, including traditional packaging forms to PGA, BGA, LCC, MCM-C, MCM-C / D, MEMS devices and module packaging and other system SIP (System in Package) package. Various products based on low-temperature co-fired ceramic technology are widely used in computer, communication, automobile, aerospace, biomedical, lighting, Internet of Things and other fields. It is an ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.