Blended elastic knitted fabric and preparation method thereof

A preparation process and technology for knitted fabrics, which are applied in knitting, weft knitting, textiles and papermaking, etc., can solve the problems of poor comfort of high-elasticity fabrics, single structure of grasping and shearing machines, and inability to remove floating hair well. Excellent moisture and breathability, good permeability and rheology, and the effect of improving elasticity

Active Publication Date: 2020-06-23
石狮市聚宝针纺织品织造有限责任公司
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the comfort of the highly elastic fabric prepared by this patent is not good
[0004] In addition, the structure of the grasping and shearing machine used for fabrics in the prior art is single, the grasping and shearing process is relatively short, and the floating wool on the surface of the fabric cannot be removed well, so the surface of the fabric is rough and the quality is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blended elastic knitted fabric and preparation method thereof
  • Blended elastic knitted fabric and preparation method thereof
  • Blended elastic knitted fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A kind of lightweight warm knitted fabric and its preparation process

[0047] Blended elastic knitted fabric, prepared by the following process:

[0048]Step A, mix 50kg of polyvinyl chloride, 25kg of ethylene propylene rubber, 9kg of sodium stearate, 12kg of bamboo charcoal powder and 4kg of nano-titanium dioxide, heat to a molten state, add coupling agent 8.5kg, cellulose ester 2.5kg and alginic acid Sodium 1.7kg, continue to mix evenly, extrude from the spinneret to obtain synthetic fibers; the particle size of bamboo charcoal powder is 500-1000 mesh;

[0049] In step B, the synthetic fibers, cotton fibers and modal fibers obtained in step A are alternately arranged in the order of 1:1:1, and the single yarn is obtained through the spinning process;

[0050] In step C, the single yarn obtained in step B is parallel-twisted to form strands, and the twist is 14 twists / hour;

[0051] Step D, using a rib machine to weave the composite yarn obtained in step C to obtain...

Embodiment 2

[0055] A kind of lightweight warm knitted fabric and its preparation process

[0056] Blended elastic knitted fabric, prepared by the following process:

[0057] Step A, mix 40kg of polyvinyl chloride, 20kg of ethylene propylene rubber, 6kg of sodium stearate, 8kg of bamboo charcoal powder and 2.5kg of nano-titanium dioxide, heat to a molten state, add 5kg of coupling agent, 1.5kg of cellulose ester and alginic acid Sodium 1.2kg, continue to mix evenly, extrude from the spinneret to obtain synthetic fibers; the particle size of bamboo charcoal powder is 500-1000 mesh;

[0058] In step B, the synthetic fibers, cotton fibers and modal fibers obtained in step A are alternately arranged in the order of 2:1:3, and single yarns are obtained through the spinning process;

[0059] In step C, the single yarn obtained in step B is parallel-twisted to form strands, and the twist is 12 twists / hour;

[0060] Step D, using a rib machine to weave the composite yarn obtained in step C to ob...

Embodiment 3

[0064] A kind of lightweight warm knitted fabric and its preparation process

[0065] Blended elastic knitted fabric, prepared by the following process:

[0066] Step A, mix 60kg of polyvinyl chloride, 35kg of ethylene propylene rubber, 12kg of sodium stearate, 16kg of bamboo charcoal powder and 5kg of nano-titanium dioxide, heat to a molten state, add 12kg of coupling agent, 3.5kg of cellulose ester and sodium alginate 2.2kg, continue to mix evenly, extrude from the spinneret to obtain synthetic fibers; the particle size of bamboo charcoal powder is 500-1000 mesh;

[0067] In step B, the synthetic fibers, cotton fibers and modal fibers obtained in step A are alternately arranged in the order of 2:3:1, and single yarns are obtained through spinning process;

[0068] In step C, the single yarn obtained in step B is parallel-twisted to form strands, and the twist is 16 twists / hour;

[0069] Step D, using a rib machine to weave the composite yarn obtained in step C to obtain a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a blended elastic knitted fabric and a preparation method thereof. The preparation method comprises the steps of: a step A of uniformly mixing polyvinyl chloride, ethylene propylene rubber, sodium stearate, bamboo charcoal powder and nanometer titania, heating into a molten state, adding a coupling agent, cellulose ester and sodium alga acid, continuing to uniformly mix, and extruding from a spinneret plate to obtain synthetic fibers; a step B of alternatively arranging the synthetic fibers, cotton fibers and modal fibers according to a sequence of 2:(1 to 3):(1 to 3),and obtaining single yarns by a spinning process; a step C of carrying out cabling on the single yarns to form folded yarns; a step D of carrying out weaving on composite yarns by a rib knitting machine to obtain a gray fabric; a step E of carrying out high-temperature presetting on the gray fabric; and a step F of carrying out ball wool opening and shearing treatment on the gray fabric to obtainthe blended elastic knitted fabric. The blended elastic knitted fabric prepared by the preparation method has high elasticity, is comfortable to wear, excellent in moisture permeability and air permeability, simple in preparation process and easy in operation of a production process, and has wide application prospect.

Description

technical field [0001] The invention relates to the technical field of knitted fabrics, in particular to a blended elastic knitted fabric and a preparation process thereof. Background technique [0002] Wearing fabrics should not only meet the advantages of high softness, breathability and sweat absorption, but also have certain elasticity. However, existing elastic fabrics lack sufficient elastic deformation capacity, and fabrics with high elasticity often use dense fabric structures. The small gaps between the yarns seriously affect the moisture permeability and breathability of the fabric, which in turn affects the comfort of wearing. [0003] Chinese patent CN103668700A discloses a high-elastic fabric and its preparation method, which consists of ethylene-propylene rubber, polyethylene glycol, monomethylaniline, polyphenylene ether, calcium stearate, fatty acid polyvinyl chloride ether, and a coupling agent. Originally mixed and heated to a molten state, adding a coupli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/18D06C13/06D06G1/00D01F8/10D01F1/10
CPCD01F1/10D01F8/10D04B1/18D06C13/06D06G1/00D10B2201/02D10B2201/22D10B2321/041
Inventor 蔡鸿达杨漳山李玲妮林洲萍
Owner 石狮市聚宝针纺织品织造有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap