A kind of rubber adhesive and preparation method thereof

A rubber adhesive and rubber technology, applied in the direction of halogen rubber derivative adhesives, adhesives, adhesive types, etc., can solve problems such as low temperature resistance and unsatisfactory thermodynamic properties of rubber adhesives

Active Publication Date: 2020-09-11
SHANDONG HUIDA RUBBER CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

One of the deficiencies in the prior art is that the thermodynamic properties of rubber adhesives are not ideal and are not resistant to high temperatures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045] Embodiments of the present invention provide a kind of preparation method of rubber adhesive, comprising the following steps:

[0046] Step S100. Prepare the first mixture by using graphene filler, inorganic filler, fiber filler, organic filler and rubber main material;

[0047] Step S200. According to the mass percentage of the first mixture: 1,6-hexanediol diacrylate: dibutyltin dilaurate = (92-96): (2-4): (2-4), will pass through step S100 The obtained first mixture is uniformly mixed with 1,6-hexanediol diacrylate and dibutyltin dilaurate at a temperature of 20°C to 30°C to obtain a second mixture;

[0048] Step S300. Curing the second mixture obtained in step S200 at a temperature of 60°C to 80°C for 12h to 18h to obtain a rubber adhesive.

[0049] In this example, the graphene filler is used to improve the thermodynamic stability of the rubber adhesive. Graphene is a nanomaterial with excellent thermodynamic properties and toughness. The addition of graphene fi...

Embodiment 1

[0080] The present embodiment provides a kind of preparation method of rubber adhesive, and it comprises the following steps:

[0081] Step S1. Mix silicon carbide and chitosan evenly according to the mass ratio of silicon carbide: chitosan = 40:60, keep the temperature at 180° C. for 2 hours, and obtain a silicon-carbon mixture after cooling;

[0082] Step S2. Mix the silicon-carbon mixture and graphene obtained in step S1 uniformly according to the mass ratio of silicon-carbon mixture:graphene=5:95, keep the temperature at 620° C. for 2 hours, and obtain the graphene filler after cooling;

[0083] Step S3. According to the mass ratio of silicon oxide: aluminum oxide: yttrium oxide: lithium oxide = 44: 28: 22: 10, mix silicon oxide, aluminum oxide, yttrium oxide and lithium oxide evenly, then raise the temperature to 1400 ° C and keep it warm for 2 hours , after cooling, grind and pulverize to obtain inorganic fillers;

[0084] Step S4. According to the mass ratio of p-pheny...

Embodiment 2

[0097] The present embodiment provides a kind of preparation method of rubber adhesive, and it comprises the following steps:

[0098] Step S1. Mix silicon carbide and chitosan evenly according to the mass ratio of silicon carbide: chitosan = 50:50, keep the temperature at 200° C. for 2 hours, and obtain a silicon-carbon mixture after cooling;

[0099] Step S2. Mix the silicon-carbon mixture and graphene obtained in step S1 uniformly according to the mass ratio of silicon-carbon mixture:graphene=15:85, keep the temperature at 660° C. for 2 hours, and obtain the graphene filler after cooling;

[0100] Step S3. According to the mass ratio of silicon oxide: aluminum oxide: yttrium oxide: lithium oxide = 46: 26: 22: 6, mix silicon oxide, aluminum oxide, yttrium oxide and lithium oxide evenly, then heat up to 1600 ° C and keep it warm for 2 hours , after cooling, grind and pulverize to obtain inorganic fillers;

[0101]Step S4. Combine p-phenylenediamine, o-chloro-p-phenylenediami...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shear strengthaaaaaaaaaa
shear strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a rubber adhesive and a preparation method thereof. The preparation method of the rubber adhesive comprises the following steps: step S100. adopting graphene filler, inorganic filler, fiber filler, organic filler and rubber main material to prepare the first mixture; step S200. according to the first mixture: 1,6-hexanedi Alcohol diacrylate: dibutyltin dilaurate = (92‑96): (2‑4): (2‑4) mass percent, the first mixture obtained through step S100 is mixed with 1,6-hexanediol di Acrylate and dibutyltin dilaurate are uniformly mixed at a temperature of 20°C to 30°C to obtain a second mixture; step S300. curing the second mixture obtained through step S200 at a temperature of 60°C to 80°C for 12 hours By 18h, a rubber adhesive was obtained. The rubber adhesive of the invention has excellent high temperature resistance and mechanical properties.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to a rubber adhesive and a preparation method thereof. Background technique [0002] Rubber adhesive is a kind of adhesive formulated with synthetic rubber or natural rubber such as chloroprene, nitrile, butyl silicone rubber, polysulfide, etc. as the main material. It has excellent elasticity and is especially suitable for bonding soft or materials with different thermal expansion coefficients, such as the bonding between rubber and rubber, rubber and metal, plastic, leather, wood and other materials. One of the deficiencies in the prior art is that the thermodynamic properties of the rubber adhesive are not satisfactory and are not resistant to high temperatures. Contents of the invention [0003] The present invention aims to solve at least one of the above technical problems. [0004] For this reason, the first object of the present invention is to provide a kind of prepar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J115/02C09J111/00C09J11/08C09J11/04
CPCC09J115/02C09J111/00C09J11/08C09J11/04C08L2205/035C08L2205/16C08L11/00C08L77/06C08L5/08C08L75/04C08K3/042C08K3/34C08K3/22C08K3/013C08L15/02
Inventor 赵会岩张志胜赵海林闫玉良
Owner SHANDONG HUIDA RUBBER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com