Monocrystalline silicon wafer texturing agent and texturing method using texturing agent

A single crystal silicon wafer and texturing agent technology, applied in the direction of single crystal growth, single crystal growth, chemical instruments and methods, etc., can solve the problems of increasing production cost, high reaction temperature, long reaction time, etc., to increase production The effect of productivity, lower reaction temperature and lower production cost

Active Publication Date: 2020-07-10
SUZHOU CRYSTAL CLEAR CHEMICAL CO LTD
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The reaction temperature of this texturing process is high, and the reaction time is long, which increases the production cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Monocrystalline silicon wafer texturing agent and texturing method using texturing agent
  • Monocrystalline silicon wafer texturing agent and texturing method using texturing agent
  • Monocrystalline silicon wafer texturing agent and texturing method using texturing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Prepare the initiator: mix 10 parts of HF with a concentration of 49% and 1 part of the glass component, soak at room temperature for more than 24 hours, filter to remove insoluble matter, and obtain the initiator.

[0038] Preparation of the regulating agent: 51.5 parts of copper nitrate hydrate, 4 parts of 1% nitric acid and 44.5 parts of deionized water were mixed and stirred for 30 minutes, and then dissolved to obtain the regulating agent.

[0039] Preparation of the first texturing agent: In 125L deionized water, add 36.72L of 49% HF and 16.44L of 31% H 2 o 2 , 1.2L regulator and 0.8L initiator, stirred at room temperature for 30 minutes and mixed uniformly to obtain 180.16L of the first texturing agent.

[0040] Preparation of the second texturing agent: In 119L deionized water, add 26.20L of 49%HF and 18L of 31%H 2 o 2 , 6L regulating agent and 0.8L initiator, stirred at room temperature for 30 minutes and mixed uniformly to obtain 170L second texturizing age...

Embodiment 2

[0043] Prepare the initiator: mix 10 parts of HF with a concentration of 49% and 1 part of the glass component, soak at room temperature for more than 24 hours, filter to remove insoluble matter, and obtain the initiator.

[0044] Preparation of the regulating agent: 51.5 parts of copper nitrate hydrate, 4 parts of 1% nitric acid and 44.5 parts of deionized water were mixed and stirred for 30 minutes, and then dissolved to obtain the regulating agent.

[0045] Preparation of the first texturing agent: in 126L of deionized water, add 36.72L of 49% HF and 15.24L of 31% H 2 o 2 , 1.2L regulator and 0.8L initiator, stirred at room temperature for 30 minutes and mixed uniformly to obtain 179.96L of the first texturing agent.

[0046] Preparation of the second texturing agent: In 118L deionized water, add 26.20L of 49%HF and 19.2L of 31%H 2 o 2 , 6L regulator and 0.8L initiator, stirred at room temperature for 30 minutes and mixed uniformly to obtain 170.2L of the second texturin...

Embodiment 3

[0049] Prepare the initiator: mix 10 parts of HF with a concentration of 49% and 1 part of the glass component, soak at room temperature for more than 24 hours, filter to remove insoluble matter, and obtain the initiator.

[0050] Preparation of the regulating agent: 51.5 parts of copper nitrate hydrate, 4 parts of 1% nitric acid and 44.5 parts of deionized water were mixed and stirred for 30 minutes, and then dissolved to obtain the regulating agent.

[0051] Preparation of the first texturing agent: In 125L deionized water, add 36.72L of 49% HF and 16.44L of 31% H 2 o 2 , 1.2L regulator and 0.8L initiator, stirred at room temperature for 30 minutes and mixed uniformly to obtain 180.16L of the first texturing agent.

[0052] Preparation of the second texturing agent: In 118L deionized water, add 26.20L of 49%HF and 19.2L of 31%H 2 o 2 , 6L regulator and 0.8L initiator, stirred at room temperature for 30 minutes and mixed uniformly to obtain 170.2L of the second texturing a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a monocrystalline silicon wafer texturing agent. The texturing agent comprises the following components in percentage by mass: 10%-25% of inorganic acid, 5%-15% of an oxidizingagent, 0.5%-5% of a regulating agent, 0.1%-1% of an initiator and the balance deionized water. The invention also discloses a method for texturing by using the texturing agent, which comprises the following steps: preparing a first texturing agent, putting a monocrystalline silicon wafer into the first texturing agent, and soaking at 32 DEG C for 3 minutes; preparing a second texturing agent, putting the monocrystalline silicon wafer treated by the first texturing agent into the second texturing agent, and soaking for 3 minutes at 25 DEG C; and putting the textured monocrystalline silicon wafer into a mixed solution of nitric acid and hydrofluoric acid, carrying out ultrasonic cleaning for 1 minute, then carrying out ultrasonic cleaning on the monocrystalline silicon wafer by using deionized water, and drying by using high-purity nitrogen to obtain the monocrystalline silicon wafer with a textured structure. According to the invention, the texturing process can be completed at room temperature within a short time by using the texturing agent, and an inverted pyramid textured structure better than a positive pyramid textured structure obtained by alkaline texturing is obtained.

Description

technical field [0001] The invention relates to the technical field of solar cell manufacturing, in particular to a texturing agent for monocrystalline silicon wafers and a texturing method using the texturing agent. Background technique [0002] In the process of preparing solar cells, in order to improve the performance and efficiency of solar cells, it is necessary to make a textured surface on the surface of the silicon wafer. The effective textured structure can make the incident sunlight reflect and refract multiple times on the surface of the silicon wafer, changing the incident light. The way forward in silicon. On the one hand, the optical path is extended, thereby increasing the absorption rate of infrared light by the silicon wafer; on the other hand, more photons are absorbed in the area near the p-n junction to generate photo-generated carriers, and these photo-generated carriers are more easily absorbed collection, thus increasing the collection efficiency of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C30B33/10C30B29/06H01L31/0236H01L31/18
CPCC30B29/06C30B33/10H01L31/02363H01L31/18Y02P70/50
Inventor 金炳生高小云刘兵
Owner SUZHOU CRYSTAL CLEAR CHEMICAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com