Plastic masterbatch and preparation method thereof

A technology of plastic masterbatch and raw materials, applied in the field of plastic masterbatch, can solve the problems of poor mechanical properties, wear resistance, poor toughness, etc., and achieve the effect of good elasticity, good gloss and improved rheology

Active Publication Date: 2020-08-14
JIANGXI FUSHANGMEI TECH CO LTD
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Plastic masterbatch is the raw material for the production of plastic products, but the existing plastic produc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0024] Example 1

[0025] Weigh the following parts by weight of raw materials: 70 parts of polypropylene resin, 8 parts of modified mica powder, 5 parts of modified pearl clay, 1 part of modified nano calcium carbonate, 2 parts of modified sepiolite fiber, lignin 1 part of fiber, 1 part of modified glass fiber, 1 part of chlorinated polyethylene, 6 parts of chlorinated paraffin;

[0026] Among them, the preparation method of modified mica powder includes: adding 10g of mica powder to 50mL of distilled water, placing it in an ice water bath, adding 5mL of concentrated hydrochloric acid while stirring, and dropping 10mL of TiCl with a concentration of 2mol / L. 4 Solution, then continue to add 10mL of ammonium sulfate solution with a concentration of 2mol / L, mix and stir, heat the mixture in a water bath to 90~100℃ and keep it for 30~60min; then adjust the pH of the mixture to 7 with ammonia water, filter and wash, Dry at 80°C to obtain modified mica powder.

[0027] The modification m...

Example Embodiment

[0037] Example 2

[0038] Weigh the following raw materials: 72 parts of polypropylene resin, 10 parts of modified mica powder, 6 parts of modified pearl clay, 2 parts of modified nano calcium carbonate, 3 parts of modified sepiolite fiber, lignin 2 parts of fiber, 1.5 parts of modified glass fiber, 1.5 parts of chlorinated polyethylene, 8 parts of chlorinated paraffin;

[0039] Among them, the modification methods of modified mica powder, modified pearl clay, modified nano calcium carbonate, modified sepiolite fiber, and modified glass fiber are the same as those in Example 1.

[0040] Prepare the plastic masterbatch with the above raw materials according to the following method:

[0041] S1. Mix the modified mica powder, modified pearl clay, and modified nano-calcium carbonate, add them to a ball mill and grind for 30 minutes to obtain mixture A;

[0042] S2. Add mixture A, half of the above-mentioned polypropylene resin and chlorinated polyethylene into a high-speed mixer, heat up t...

Example Embodiment

[0045] Example 3

[0046] Weigh the following raw materials to make: 75 parts of polypropylene resin, 11 parts of modified mica powder, 7 parts of modified pearl clay, 3 parts of modified nano-calcium carbonate, 4 parts of modified sepiolite fiber, lignin 3 parts of fiber, 2 parts of modified glass fiber, 2 parts of chlorinated polyethylene, 9 parts of chlorinated paraffin.

[0047] Among them, the modification methods of modified mica powder, modified pearl clay, modified nano calcium carbonate, modified sepiolite fiber, and modified glass fiber are the same as those in Example 1.

[0048] Prepare the plastic masterbatch with the above raw materials according to the following method:

[0049] S1. Mix the modified mica powder, modified pearl clay and modified nano-calcium carbonate, add them to a ball mill and grind for 20-30 minutes to obtain mixture A;

[0050] S2. Add mixture A, polypropylene resin and chlorinated polyethylene with half of the above weight into a high-speed mixer, h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Lengthaaaaaaaaaa
Lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses plastic masterbatch, and relates to the technical field of plastic masterbatch. The plastic masterbatch is prepared from the following raw materials in parts by weight: 70-80 parts of carrier resin, 8-14 parts of modified mica powder, 5-10 parts of modified nacrite, 1-5 parts of modified nano calcium carbonate, 2-6 parts of modified sepiolite fibers, 1-5 parts of lignin fibers, 1-3 parts of modified glass fibers, 1-3 parts of chlorinated polyethylene and 6-12 parts of chlorinated paraffin, wherein the length of the modified sepiolite fibers is 1-3 cm, the length of thelignin fibers is 0.2-0.6 cm, and the length of the modified glass fibers is 2-5 cm. The invention also provides a preparation method of the plastic masterbatch. The plastic masterbatch has the beneficial effects that the mechanical property of the plastic masterbatch is improved, the plastic masterbatch has good tensile strength, impact strength, bending strength, elongation at break and the like,meanwhile, the glossiness of the surface of a plastic product can be improved, the effects of shielding ultraviolet rays and resisting bacteria are achieved, the plastic product is prevented from being aged, and the service lifetime of the plastic product is prolonged.

Description

technical field [0001] The invention relates to the technical field of plastic master batches, in particular to a plastic master batch and a preparation method thereof. Background technique [0002] Plastic products are a general term for household and industrial products processed from plastic as the main raw material. Including plastic as raw material for injection molding, blister and other products of all processes. Together with synthetic rubber and synthetic fibers, it forms the three major synthetic materials indispensable to daily life. Specifically, plastic is a material with natural or synthetic resin as the main component, adding various additives, which can be molded into a certain shape under certain conditions such as temperature and pressure, and maintains the same shape at room temperature. Compared with metal, stone, and wood, plastic products have the advantages of low cost and strong plasticity, and are widely used in the national economy. The plastics i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L91/06C08L23/28C08L97/00C08K13/06C08K9/02C08K3/34C08K3/22C08K3/26C08K9/06C08K7/10C08K7/14C08J3/22
CPCC08J3/226C08J2423/12C08J2423/28C08J2497/00C08K2201/011C08K2201/004C08K13/06C08K9/02C08K3/34C08K2003/2241C08K2003/265C08K9/06C08K7/10C08K7/14
Inventor 蔡壮林
Owner JIANGXI FUSHANGMEI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap