Special engineering plastic composite material and preparation method thereof

A technology for special engineering plastics and composite materials, applied in the field of special engineering plastics composite materials and their preparation, can solve the problems of low production process efficiency, slow processing and molding process, poor processability, etc., and achieve simple and rapid molding and high molecular weight. , Overcome the effect of poor toughness

Pending Publication Date: 2020-08-14
江苏百通塑业发展有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Special engineering plastic composite materials can meet higher requirements in terms of mechanical properties, durability, corrosion resistance, heat resistance, etc., and are more convenient to process and can replace metal materials. They are widely used in electronics, automobiles, construction, office In the equipment, machinery, aerospace and other industries, it has become an international trend to replace steel and wood with plastic, and it also promotes the transformation of traditional industries and the adjustment of product structure. However, the existing special engineering plastic composite materials crystallize after mixing The speed is slow, which makes the processing and molding process slow and the production process is not efficient. Secondly, the toughness of the material is poor, and the molding process is easy to break, resulting in poor processability. Therefore, we propose a special engineering plastic composite material and its Preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A special engineering plastic composite material, comprising the following materials in parts by weight: 20 parts of polyester resin, 18 parts of polyethylene sebacamide, 16 parts of polyvinyl chloride, 21 parts of modifier, and 10 parts of additive.

[0028] The modifier includes 8 parts of polyglyceryl sebacate, 5 parts of propylene glycol adipate, 6 parts of acrylate, and 3 parts of xylyl phosphate.

[0029] The additives include 5 parts of nano-titanium nitride and 6 parts of nano-calcium oxide. These nanoparticles can block the molecular gap, making it difficult for gas to diffuse and penetrate, thereby improving the barrier properties of plastic materials, increasing the crystallization rate, and improving production efficiency.

[0030] Polyglycerol sebacate is obtained by polycondensation of glycerin and sebacic acid under the condition of nitrogen flow and water separation, the flow rate of nitrogen gas is 0.1m3 / h, the reaction temperature is 160°C, the reaction...

Embodiment 2

[0034] A preparation method of a special engineering plastic composite material, comprising the following steps:

[0035] S1: Prepare 30 parts of polyester resin, 20 parts of polyethylene sebacamide, 20 parts of polyvinyl chloride, 20 parts of modifier, and 10 parts of additives according to parts by weight;

[0036] S2: mixing polyester resin, polyethylene sebacyl diamine, and polyvinyl chloride to form a mixed slurry;

[0037] S3: Add modifiers and additives to the mixed solution in S2. Modifiers include 10 parts of polyglyceryl sebacate, 4 parts of propylene glycol adipate polyester, 4 parts of acrylate, 2 parts of xylyl phosphate, additives Including 5 parts of nano-titanium nitride and 5 parts of nano-calcium oxide, stirring, while the pH of the mixed solution is detected in real time during the addition of modifiers and additives, the pH is controlled to be neutral, and the plastic slurry is obtained after fully mixing ;

[0038] S4: Put the plastic slurry obtained in ...

Embodiment 3

[0041] A preparation method of a special engineering plastic composite material, comprising the following steps:

[0042] S1: 16 parts of polyester resin, 15 parts of polyethylene sebacamide, 11 parts of polyvinyl chloride, 13 parts of modifier, and 7 parts of additives are prepared according to parts by weight;

[0043] S2: mixing polyester resin, polyethylene sebacyl diamine, and polyvinyl chloride to form a mixed slurry;

[0044]S3: Add modifiers and additives to the mixed solution in S2. The modifiers include 4 parts of polyglyceryl sebacate, 3 parts of propylene glycol adipate polyester, 4 parts of acrylate, 2 parts of xylyl phosphate, additives Including 3 parts of nano-titanium nitride and 4 parts of nano-calcium oxide, stirring, and at the same time, the pH of the mixed solution is detected in real time during the addition of modifiers and additives, and the pH is controlled to be neutral, and the plastic slurry is obtained after fully mixing ;

[0045] S4: Put the p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of plastic materials, and discloses a special engineering plastic composite material which is prepared from the following materials in parts by weight: 16 to 30 parts of polyester resin, 15 to 20 parts of polysebacyl ethylenediamine, 11 to 20 parts of polyvinyl chloride, 13 to 30 parts of modifier and 7 to 12 parts of additive. The invention also provides a preparation method of the special engineering plastic composite material. The special engineering plastic composite material and the preparation method thereof have the advantages that the crystallizationrate is high, the toughness of the composite material is good, and the composite material is easy to process.

Description

technical field [0001] The invention relates to the field of plastic materials, in particular to a special engineering plastic composite material and a preparation method thereof. Background technique [0002] Special engineering plastic composite materials can meet higher requirements in terms of mechanical properties, durability, corrosion resistance, heat resistance, etc., and are more convenient to process and can replace metal materials. They are widely used in electronics, automobiles, construction, office In the equipment, machinery, aerospace and other industries, it has become an international trend to replace steel and wood with plastic, and it also promotes the transformation of traditional industries and the adjustment of product structure. However, the existing special engineering plastic composite materials crystallize after mixing The speed is slow, which makes the processing and molding process slow and the production process is not efficient. Secondly, the t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L67/00C08L77/06C08L27/06C08L67/02C08K13/02C08K3/22C08K3/28C08K5/523
CPCC08L67/00C08L2205/035C08L2205/02C08L2205/025C08L2201/08C08L2201/14C08K2201/011C08K2003/2206
Inventor 周辉孙钟富陆丽华
Owner 江苏百通塑业发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com