Carbonization treatment agent and preparation method of carbonized floor

A treatment agent and carbonization technology, applied in wood treatment, wood treatment details, manufacturing tools, etc., can solve the problems of harsh treatment environment and conditions, high waste rate of carbonized wood, low production efficiency, etc., to achieve a rich sense of hierarchy and suitable scale The effect of chemical production and low production cost

Inactive Publication Date: 2020-08-25
JILIN CITY ACADEMY OF FORESTRY
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Conventional carbonized flooring needs to use carbonized wood surface boards. Conventional carbonized wood production processes generally require 4-8 hours of treatment in a closed oxygen-isolated tank at 170-220 ° C to achieve carbonization of the entire surface board inside and outside, but there are processing environments and conditions. Harsh, carbonized wood waste rate is high, special production equipment is required, and technical problems are high in cost. Therefore, many flooring companies need to purchase carbonized wood surface boards and cannot produce them by themselves.
In addition, carbonizing the surface of the floor is also a production method of carbonized flooring, but this method generally uses barbecue methods to heat the floor surface, such as burning, scalding, using oxygen torches or soldering irons, etc., and there is also a high waste rate of carbonized wood, Technical problems with low production efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbonization treatment agent and preparation method of carbonized floor
  • Carbonization treatment agent and preparation method of carbonized floor
  • Carbonization treatment agent and preparation method of carbonized floor

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] In the present invention, there is no special limitation on the preparation method of the carbonization treatment agent, as long as the components are mixed according to the above mass content. In the present invention, the preparation method of the carbonization treatment agent is preferably to mix sulfuric acid and water under the condition of stirring, and then add Pingpingao O, sodium chloride and sodium sulfate. The method of mixing sulfuric acid and water is not particularly limited in the present invention, and the mixing method of sulfuric acid and water well known in the art can avoid excessive temperature rise of the system and prevent liquid splashing. In the present invention, there is no special limitation on the stirring rate, and the conventional stirring rate is enough.

[0034] The present invention also provides a preparation method of carbonized floor, comprising the following steps:

[0035] (1) coating the carbonization treatment agent as described...

Embodiment 1

[0057] According to the mass content, the components of the carbonization treatment agent are: 12% of sulfuric acid, 0.1% of Pingao O, 0.1% of sodium chloride, 0.1% of sodium sulfate, and 87.7% of water.

Embodiment 2

[0071] In terms of mass content, the carbonization treatment agent includes the following components: 5% sulfuric acid, 0.1% Pyrene O, 0.1% sodium chloride, 0.1% sodium sulfate, and 94.7% water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a carbonization treatment agent and a preparation method of a carbonized floor, and belongs to the field of surface treatment agents. The carbonization treatment agent is coatedon the surface of a floor, after heating, sulfuric acid with corrosivity and oxidability is used for carrying out surface carbonization and oxidation on the floor, and meanwhile, the balance adjusting effect of sodium chloride and sodium sulfate and the diffusion stabilizing effect of peregal O of a nonionic surfactant are cooperated, so that controllable and rapid carbonization of the surface ofthe floor at a low temperature is promoted, excessive carbonization is avoided, carbonized wood waste is avoided, and the obtained carbonized floor is variable in surface color and rich in layering sense. Results of the embodiment show that the carbonization treatment agent can realize floor carbonization at a relatively low temperature of 70-80 DEG C, and no carbonized wood waste is generated; and the prepared carbonized floor is normally put into use for about one month, is stable in color and has no obvious change, and compared with the carbonized floor in a non-solarization area, the carbonized floor in the solarization area has no obvious chromatic aberration.

Description

technical field [0001] The invention relates to the field of surface treatment agents, in particular to a carbonization treatment agent and a preparation method for a carbonization floor. Background technique [0002] Carbonized floor has the following advantages: (1) After carbonization treatment, the wood fiber holes are highly integrated, which eliminates the internal stress of the wood, makes the wood stronger, and no longer expands and contracts with heat and cold; (2) Heat absorption and heat preservation, warm in winter and summer (2) After the moisture-proof wood is carbonized, the wood fiber holes are dense and concentrated, and it is difficult for water stains to soak into the wood; (4) After the anti-corrosion wood is treated with high temperature, all the organic matter in the wood is decomposed and denatured, so that fungi have no living space Wait. Therefore, in recent years, carbonized flooring has become a popular product in the decoration market. [0003] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27M1/06B27K3/52B27K3/20B27K3/16B27K3/36B27K5/00B27K5/04
CPCB27K3/16B27K3/20B27K3/36B27K3/52B27K5/001B27K5/04B27M1/06
Inventor 孟黎鹏付世萃李杰玲陈玲刘冰胡显宁崔铁花李继平付晓霞
Owner JILIN CITY ACADEMY OF FORESTRY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products