Textile refining agent containing organic clay
A technology of organoclay and refining agent, applied in textile and papermaking, detergent composition, detergent compounding agent, etc., can solve the problems of unclean processing and poor removal ability of silicone oil, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] A textile refining agent containing organic clay, including the following raw materials by weight:
[0022] 7 parts of organic nano clay;
[0023] 3 parts of alcohol ether carboxylate;
[0024] 3 parts of fatty acid methyl ester ethoxylated sulfonate;
[0025] 4 parts of alkyl glycosides;
[0026] 0.5 parts of antibacterial agent;
[0027] 70 parts of RO pure water;
[0028] In this embodiment, the organic nanoclay is composed of 0.5 parts by weight of organic quaternary ammonium salt, 8 parts of aqueous bentonite, 1 part of nonionic surfactant, and 0.5 part of weakly ionic anionic surfactant. The preparation process of organic nanoclay is as follows: organic quaternary ammonium salt and anionic surfactant are dissolved in nonionic surfactant, then mixed with aqueous bentonite and heated and extruded by a screw extruder to obtain organic nanoclay after crushing. In this embodiment, the organic quaternary ammonium salt includes alkyl trimethyl ammonium salt and dialkyl dimethyl am...
Embodiment 2
[0033] A textile refining agent containing organic clay, including the following raw materials by weight:
[0034] 13 parts of organic nano clay;
[0035] 6 parts of alcohol ether carboxylate;
[0036] 5 parts of fatty acid methyl ester ethoxylated sulfonate;
[0037] 7 parts of alkyl glycosides;
[0038] 1 part of antibacterial agent;
[0039] 80 parts of RO pure water;
[0040] In this embodiment, the organic nanoclay is composed of 1 part by weight of organic quaternary ammonium salt, 10 parts of aqueous bentonite, nonionic surfactant 2, and 1 part of weak ionic anionic surfactant. The preparation process of organic nanoclay is as follows: organic quaternary ammonium salt and anionic surfactant are dissolved in a nonionic surfactant, then mixed with aqueous bentonite and heated and extruded by a screw extruder to obtain organic nanoclay after crushing. In this embodiment, the organic quaternary ammonium salts include alkyl pyridinium salts, alkyl isoquinolinium salts and benzyl ammon...
Embodiment 3
[0045] A textile refining agent containing organic clay, including the following raw materials by weight:
[0046] 10 parts of organic nano clay;
[0047] 5 parts of alcohol ether carboxylate;
[0048] 4 parts of fatty acid methyl ester ethoxylated sulfonate;
[0049] 5 parts of alkyl glycosides;
[0050] 1 part of antibacterial agent;
[0051] 75 parts of RO pure water;
[0052] In this embodiment, the organic nanoclay is composed of 1 part by weight of organic quaternary ammonium salt, 10 parts of aqueous bentonite, nonionic surfactant 2, and 1 part of weak ionic anionic surfactant. The preparation process of organic nanoclay is as follows: organic quaternary ammonium salt and anionic surfactant are dissolved in nonionic surfactant, then mixed with aqueous bentonite and heated and extruded by a screw extruder to obtain organic nanoclay after crushing. In this embodiment, the organic quaternary ammonium salt includes alkyl dimethyl benzyl ammonium and pyridinium salt, the nonionic surf...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com