Zirconium self-flowing castable

A castable and zirconium technology, applied in the field of refractory materials, can solve problems such as poor crack resistance, achieve excellent refractory performance, improve crack resistance, and stable performance

Inactive Publication Date: 2020-11-10
浙江攀盛冶金材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Refractory materials are widely used in metallurgy, chemical industry, petroleum, machinery manufacturing, silicate, power and other industrial fields, and are used in the largest amount in the metallurgical industry, accounting for 50% to 60% of the total output; in the process of using refractory materials, the original refractory The crack resistance of the material is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A zirconium self-flowing castable, including: aggregate, powder, and admixture;

[0022] Aggregate is 70-80% high alumina bauxite clinker, sub-white corundum, zircon, baddeleyite, which account for 70-80% of the total mass of aggregate and powder.

[0023] The powder is 1% to 6% of silica powder in the sum of aggregate and powder mass, 1 to 10% of sub-white corundum powder in the sum of aggregate and powder mass, and 1 to 12% in the sum of aggregate and powder mass. % Alumina powder, 2% to 3% of the sum of aggregate and powder mass, 2% to 3% zirconia powder, 1 to 10% of aggregate and powder mass, white clay, 0% of aggregate and powder mass ~25% high-alumina bauxite clinker powder, 0-3% high-alumina cement accounting for the sum of aggregate and powder mass, 0-6% pure calcium aluminate cement accounting for the sum of aggregate and powder mass,

[0024] The admixture is 0.1-0.3% sodium hexametaphosphate accounting for the sum of aggregate and powder mass, and 4%-7% wate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flame retardantaaaaaaaaaa
Login to View More

Abstract

The invention discloses a zircon self-flowing castable. The zircon self-flowing castable is characterized by comprising aggregate, powder and an admixture, the aggregate is prepared from high-aluminabauxite clinker, sub-white corundum, zirconite and baddeleyite which account for 70-80% of the sum of the mass of the aggregate and the mass of the powder; the powder comprises silica powder accounting for 1-6% of the sum of the mass of the aggregate and the powder, sub-white corundum powder accounting for 1-10% of the sum of the mass of the aggregate and the powder, alumina powder accounting for1-12% of the sum of the mass of the aggregate and the powder, zirconia powder accounting for 2-3% of the sum of the mass of the aggregate and the powder, white mud accounting for 1-10% of the sum of the aggregate and powder, high-alumina bauxite clinker accounting for 0-25% of the sum of agrregate and the power, the mass of the high-alumina cement accounting for 0-3% of the total mass of the aggregate and the powder, and the mass of the pure calcium aluminate cement accounting for 0-6% of the total mass of the aggregate and the powder. The zirconium self-flowing castable is stable in propertyand performance at high temperature and excellent in fire resistance, the cracking resistance can be improved by 2%-3% of zirconium oxide powder, and the fire resistance is integrally improved.

Description

technical field [0001] The invention relates to the technical field of refractory materials, in particular to a zirconium self-flowing castable. Background technique [0002] A class of inorganic non-metallic materials with a refractoriness not lower than 1580°C. Refractoriness refers to the Celsius temperature at which a refractory conical sample can resist high temperature without softening and melting without load. However, it is not possible to fully describe refractory materials only by the definition of refractoriness, and 1580°C is not absolute. It is now defined as a material whose physical and chemical properties allow it to be used in a high temperature environment is called a refractory material. Refractory materials are widely used in metallurgy, chemical industry, petroleum, machinery manufacturing, silicate, power and other industrial fields, and are used in the largest amount in the metallurgical industry, accounting for 50% to 60% of the total output; in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/106
CPCC04B35/106C04B2235/3418C04B2235/349C04B2235/3222C04B2235/447
Inventor 江群英施永益张新财沈伟龙陈百静
Owner 浙江攀盛冶金材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products