Anti-cracking exterior wall putty powder and preparation method thereof

A technology for exterior wall putty and putty powder, applied in the direction of filling slurry, etc., can solve the problems of low bonding strength of putty powder, coating cracks, poor water resistance, etc., and achieves a simple and easy preparation method, avoiding cracks, and resisting Good corrosion performance

Inactive Publication Date: 2020-11-27
贵州贵安碳酸钙实业发展有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current putty powder has low bonding strength and poor water resistance. There may be no problems within one or two years, but after a long time, problems such as cracks, peeling, and mildew will appear in the coating.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] An anti-cracking exterior wall putty powder comprises the following raw materials in parts by weight: 60 parts of putty powder base material, 15 parts of Shuangfei powder, 30 parts of anti-cracking additive, and 0.3 part of redispersible latex powder.

[0016] Further, the putty powder base material is composed of the following raw materials in parts by weight: 100 parts of talcum powder, 25 parts of white cement, 5 parts of mica powder, 4 parts of polyphenol oxygen resin, 2 parts of water retaining agent, and 1 part of lithium magnesium silicate.

[0017] In order to ensure the anti-cracking effect, the anti-cracking additive is composed of the following raw materials in parts by weight: 8 parts of hydroxypropyl methylcellulose, 4 parts of polypropylene short fibers, 40 parts of polymethyl methacrylate, 20 parts of tungsten zirconate share.

[0018] Further, the preparation method of the anti-cracking additive is: adding hydroxypropyl methylcellulose, polypropylene sho...

Embodiment 2

[0024] An anti-cracking exterior wall putty powder comprises the following raw materials in parts by weight: 80 parts of putty powder base material, 20 parts of Shuangfei powder, 40 parts of anti-cracking additive, and 0.4 part of redispersible latex powder.

[0025] Further, the putty powder base material is composed of the following raw materials in parts by weight: 110 parts of talcum powder, 30 parts of white cement, 6 parts of mica powder, 5 parts of polyphenol oxygen resin, 2.5 parts of water retaining agent, and 1.5 parts of lithium magnesium silicate.

[0026] In order to ensure the anti-cracking effect, the anti-cracking additive is composed of the following raw materials in parts by weight: 15 parts of hydroxypropyl methylcellulose, 7.5 parts of polypropylene short fiber, 50 parts of polymethyl methacrylate, 25 parts of tungsten zirconate share.

[0027] Further, the preparation method of the anti-cracking additive is: add hydroxypropyl methylcellulose, polypropylene...

Embodiment 3

[0033] An anti-cracking exterior wall putty powder comprises the following raw materials in parts by weight: 100 parts of putty powder base material, 30 parts of Shuangfei powder, 50 parts of anti-cracking additive, and 0.5 part of redispersible latex powder.

[0034] Further, the putty powder base material is composed of the following raw materials in parts by weight: 120 parts of talcum powder, 35 parts of white cement, 8 parts of mica powder, 6 parts of polyphenol oxygen resin, 3 parts of water retaining agent, and 2 parts of lithium magnesium silicate.

[0035] In order to ensure the anti-cracking effect, the anti-cracking additive is composed of the following raw materials in parts by weight: 30 parts of hydroxypropyl methylcellulose, 15 parts of polypropylene short fiber, 60 parts of polymethyl methacrylate, 30 parts of tungsten zirconate share.

[0036] Further, the preparation method of the anti-cracking additive is: adding hydroxypropyl methylcellulose, polypropylene ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses anti-cracking exterior wall putty powder. The anti-cracking exterior wall putty powder is prepared from the following raw materials in parts by weight: 60 to 100 parts of puttypowder base material; 15 to 30 parts of heavy calcium carbonate powder; 30 to 50 parts of anti-cracking additive; and 0.3 to 0.5 part of redispersible latex powder. The preparation method comprises the following steps of: (1) adding the putty powder base material and the heavy calcium carbonate powder into a mixer, and stirring the materials for 25-30 minutes at the stirring speed of 550-650r / minto obtain a mixture; and (2) adding the anti-cracking additive and redispersible latex powder into the mixture obtained in the step (1), heating to 60-75 DEG C, stirring again for 30-40 minutes at the stirring speed of 650-750 r / min, and then performing drying. The formula of the anti-cracking exterior wall putty powder is reasonable; the preparation method is simple and easy to implement; the prepared putty powder is good in bonding performance and waterproof performance; polymethyl methacrylate improves the weather resistance of the exterior wall putty powder and can prevent the exterior wall putty powder from cracking; tungsten zirconate can reduce the thermal expansion and cold contraction coefficient of the exterior wall putty powder; the tungsten zirconate is matched with the polymethyl methacrylate to well prevent the exterior wall putty powder from cracking.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to an anti-crack exterior wall putty powder and a preparation method thereof. Background technique [0002] Putty powder is a kind of building decoration material. Its main components are talcum powder and glue. It is divided into two types: interior wall and exterior wall. The putty on the exterior wall can resist wind and sun, so it has high gelatinity, high strength and low environmental index. Putty is generally composed of base material, filler, water and additives. Base material, also known as binder, is the most critical component of putty, which mainly plays various roles such as bonding. The most commonly used binders for putty are cement and organic polymers, and organic polymers can be divided into emulsion and latex powder. Cement is a cohesive, durable and cost-effective binder, but has poor tensile strength and crack resistance. Organic polyme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 赵廷功
Owner 贵州贵安碳酸钙实业发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products