High/low-temperature-resistant APAO hot melt adhesive for filter production and preparation method of high/low-temperature-resistant APAO hot melt adhesive

A high and low temperature resistant, filter technology, applied in the direction of adhesives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problems of poor bonding strength, inconvenience, high viscosity, etc., and achieve soft adhesive layer Good performance, excellent high temperature resistance, long opening time

Active Publication Date: 2020-11-27
上海路嘉胶粘剂有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the expansion of application sites, the requirements for high temperature resistance, toughness, hardness, etc. of the glue are getting higher and higher; usually, the high temperature resistant polyester hot melt adhesive has a high viscosity, which is not conducive to the coating operation, and is difficult to infiltrate. sticky substance, poor bond strength
And the anti-yellowing performance is not good, the color difference changes greatly during the mixing process, and it is difficult to meet the places that require high hardness in automotive interiors, etc., which brings inconvenience to people's use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0062] Second aspect of the present invention provides the preparation method of high and low temperature resistant APAO hot-melt adhesive for filter production, and described preparation method comprises the following steps at least:

[0063] Add the viscosity modifier into the reactor, heat it, and when the temperature is 90-120°C, turn on the turntable of the reactor; when the viscosity modifier is completely dissolved, add thermoplastic polymer materials, antioxidants, and plasticizers to keep the material The temperature is 150-160°C until it dissolves evenly, then put in the tackifier, keep it for 50-60min, cool down, and discharge, that is to say.

Embodiment 1

[0069] Provided is a high and low temperature resistant APAO hot melt adhesive for filter production. In parts by weight, the preparation raw materials include: 60 parts of thermoplastic polymer materials, 45 parts of tackifiers, 8 parts of viscosity modifiers, 0.03 parts of antioxidants, 1.2 parts of plasticizer.

[0070] The thermoplastic polymer material is VESTOPLAST 828, an amorphous polyolefin.

[0071] The tackifier is C5 hydrogenated petroleum resin, the C5 hydrogenated petroleum resin is FST-H100, and the manufacturer is Puyang Hengfeng Petrochemical Co., Ltd.

[0072] The viscosity regulator is polyethylene wax. The manufacturer is Ninghai Boer Chemical Co., Ltd., and the brand name is BR-1.

[0073] The antioxidant is a combination of antioxidant 1010 and antioxidant 168, wherein the mass ratio of antioxidant 1010 to antioxidant 168 is 1:5.

[0074] The plasticizer is dioctyl sebacate.

[0075] The preparation method of high and low temperature resistant APAO ho...

Embodiment 2

[0078] Provided is a high and low temperature resistant APAO hot melt adhesive for filter production. In parts by weight, the preparation raw materials include: 40 parts of thermoplastic polymer materials, 30 parts of tackifiers, 2 parts of viscosity regulators, 0.01 parts of antioxidants, 0.5 parts of plasticizer.

[0079] The thermoplastic polymer material is VESTOPLAST 828, an amorphous polyolefin.

[0080] The tackifier is C5 hydrogenated petroleum resin, the C5 hydrogenated petroleum resin is FST-H100, and the manufacturer is Puyang Hengfeng Petrochemical Co., Ltd.

[0081] The viscosity regulator is polyethylene wax. The manufacturer is Ninghai Boer Chemical Co., Ltd., and the brand name is BR-1.

[0082] The antioxidant is a combination of antioxidant 1010 and antioxidant 168, wherein the mass ratio of antioxidant 1010 to antioxidant 168 is 1:5.

[0083] The plasticizer is dioctyl sebacate.

[0084] The preparation method of high and low temperature resistant APAO h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of adhesives, in particular to a high-and-low-temperature-resistant APAO hot melt adhesive for filter production and a preparation method thereof. The high-and-low-temperature-resistant APAO hot melt adhesive comprises the following preparation raw materials in parts by weight: 40 to 70 parts of a thermoplastic high polymer material, 30 to 60 parts of atackifier, 2 to 15 parts of a viscosity regulator, 0.01 to 0.05 part of an antioxidant and 0.5 to 2 parts of a plasticizer. The hot melt adhesive provided by the invention has excellent high-temperature resistance and low-temperature resistance, good adhesive layer flexibility, long opening time and high strength, is suitable for various special operation processes, and solves the problems of nohigh-temperature resistance and no low-temperature resistance of a common EVA hot melt adhesive in the prior art.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to a high and low temperature resistant APAO hot melt adhesive for filter production and a preparation method thereof. Background technique [0002] As the country's environmental protection requirements become more and more stringent, the control of air PM2.5 in various regions is also strict, and people's living standards, everyone has high requirements for control quality. At present, various air purifiers, vacuum cleaners, air conditioners, and water purifiers , automobiles, etc. are becoming more and more widely used. At the same time, it needs to be able to be used normally in various environments, such as the high temperature resistance requirements in automobiles, and vacuum cleaners also need to be used in high or low temperature environments. In these products, filters are required, so it is also required when the filter is produced The hot melt adhesive used can withst...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/02C09J157/02C09J11/08C09J11/06
CPCC09J123/02C09J157/02C09J11/08C09J11/06C08L2201/08C08L2205/02C08L2205/03C08L57/02C08L23/06C08K5/1345C08K5/526C08K5/11
Inventor 凌万青
Owner 上海路嘉胶粘剂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com