Environment-friendly wood paint and preparation method thereof

A technology for wood and paint, applied in the field of environmental protection wood paint and its preparation, can solve the problems of many types of raw materials, decreased comprehensive performance of paint, complexity, etc., and achieves the effects of improving decorative effect, fast drying of paint film, and reduced paint stripping rate.

Inactive Publication Date: 2020-12-11
何志强
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are many types of raw materials in the paint, which are complex, and antagonistic reactions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0029] Example 1

[0030] An environmentally friendly wood paint is characterized in that it is made of the following raw materials in parts by weight: 30 parts of rosin-modified hydroxyl-terminated hyperbranched polyurethane, 10 parts of castor oil, 3 parts of neoprene emulsion, carboxyl-modified β-cyclodextrin 4 parts, 6 parts of sodium tetraborate, 10 parts of porous rare earth oxide, 5 parts of ethanol, 0.8 parts of castor oil polyoxyethylene ether, 1 part of polyacrylate leveling agent, 0.7 parts of tributyl phosphate, 1 part of sodium hexametaphosphate part, 25 parts of water.

[0031] The preparation method of the porous rare earth oxide comprises the following steps: adding a rare earth source into a beaker containing ethanol, stirring for 0.5 hours, slowly adding acetate, ultrasonically dispersing for 20 minutes, and transferring the solution to a polyvinyl fluoride lining In a hydrothermal reactor, react at 190°C for 16h. Take out the reaction kettle, wash the reac...

Example Embodiment

[0034] Example 2

[0035] An environmentally friendly wood paint is characterized in that it is made of the following raw materials in parts by weight: 33 parts of rosin-modified hydroxyl-terminated hyperbranched polyurethane, 13 parts of castor oil, 3.5 parts of neoprene emulsion, carboxyl-modified β-cyclodextrin 4.5 parts, 7 parts of sodium tetraborate, 11 parts of porous rare earth oxide, 6 parts of glycerin, 0.9 parts of polyglycerol ester, 1.2 parts of cellulose acetate leveling agent, 0.8 parts of defoamer Deqian 31000, 1.2 parts of sodium polycarboxylate parts, 35 parts of water.

[0036] The preparation method of the porous rare earth oxide comprises the following steps: adding a rare earth source into a beaker containing ethanol, stirring for 0.7 hours, slowly adding acetate, ultrasonically dispersing for 23 minutes, and transferring the solution to a polyvinyl fluoride lining In a hydrothermal reactor, react at 195°C for 17h. Take out the reaction kettle, wash the ...

Example Embodiment

[0039] Example 3

[0040] An environmentally friendly wood paint is characterized in that it is made of the following raw materials in parts by weight: 35 parts of rosin-modified hydroxyl-terminated hyperbranched polyurethane, 15 parts of castor oil, 4 parts of neoprene emulsion, carboxyl-modified β-cyclodextrin 5 parts, 8 parts of sodium tetraborate, 13 parts of porous rare earth oxide, 8 parts of isopropanol, 1 part of lauryl glucoside, 1.5 parts of polyvinyl butyral leveling agent, 0.85 parts of defoamer BYK088, six 1.5 parts of sodium metaphosphate, 40 parts of water.

[0041] The preparation method of the porous rare earth oxide comprises the following steps: adding a rare earth source into a beaker containing ethanol, stirring for 0.8 hours, slowly adding acetate, ultrasonically dispersing for 25 minutes, and transferring the solution to a polyvinyl fluoride lining In a hydrothermal reactor, react at 205°C for 19h. Take out the reaction kettle, wash the reaction system...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environment-friendly wood paint and a preparation method thereof. The environment-friendly wood paint is prepared from the following raw materials in parts by weight: 30-40parts of rosin-modified hydroxyl-terminated hyperbranched polyurethane, 10-20 parts of castor oil, 3-5 parts of chloroprene rubber emulsion, 4-6 parts of carboxyl-modified beta-cyclodextrin, 6-10 parts of sodium tetraborate, 10-15 parts of porous rare earth oxide, 5-10 parts of an alcohol solvent, 0.8-1.2 parts of an emulsifier, 1-2 parts of a leveling agent, 0.7-1 part of an antifoaming agent, 1-2 parts of a dispersant and 25-55 parts of water. The invention also provides a preparation method of the environment-friendly wood paint. The environment-friendly wood paint is better in waterproofness and wear resistance, faster in paint film drying, more excellent in dirt adhesion resistance, scratch resistance and weather resistance, and safer and more environment-friendly to use.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an environmentally friendly wood paint and a preparation method thereof. Background technique [0002] Paint is a chemical mixture that can firmly cover the surface of objects for protection, decoration, marking and other special purposes. Paint is widely used in our life, furniture, props, exterior walls, home decoration and handicrafts all need paint. Paint can make items bright in color, delicate in touch, fashionable and beautiful, and it also has special functions such as strong and durable, moisture-proof, high-temperature resistance, and corrosion resistance. Wood paint is one of the more common paints. It is a paint sprayed on the surface of wood to beautify the surface of wood and protect wood. It has the characteristics of moisture resistance, water resistance, oil resistance, and corrosion resistance. [0003] Most traditional wood paints are solvent-based paints, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D187/00C09D191/00C09D5/24C09D5/14C09D5/18C09D5/16C09D7/65C09D7/61C09D7/20
CPCC08K2003/387C08L2201/02C08L2201/04C08L2201/08C08L2205/035C09D5/14C09D5/1687C09D5/18C09D5/24C09D187/005C09D7/20C08L91/00C08L11/02C08L5/16C08K13/04C08K7/24C08K5/521C08K3/38
Inventor 何志强
Owner 何志强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap