Collaborative curing treatment method for electrolytic manganese slag and red mud

A technology for electrolytic manganese slag and solidification treatment, which is applied in chemical instruments and methods, inorganic chemistry, ammonia compounds, etc., to achieve the effects of reducing dosage, cost, and treatment cost

Inactive Publication Date: 2021-01-05
GUIZHOU ACAD OF ENVIRONMENTAL SCI & DESIGNING
View PDF11 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The method provided by the invention uses red mud, red mud leachate, and quicklime to stabilize manganese ions and ammonia nitrogen in electrolytic manganese slag, solves the problem of harmless sto

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Collaborative curing treatment method for electrolytic manganese slag and red mud
  • Collaborative curing treatment method for electrolytic manganese slag and red mud
  • Collaborative curing treatment method for electrolytic manganese slag and red mud

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0055]Example 1

[0056]A method for coordinated solidification treatment of electrolytic manganese slag and red mud includes the following steps:

[0057](1) Take the electrolytic manganese slag and old red mud to dry until the water content is below 20wt%, and then transport the electrolytic manganese slag, old red mud and quicklime to the crusher for crushing treatment to obtain electrolytic manganese slag powder and old red mud. Mud powder and quicklime powder, the particle size of electrolytic manganese slag powder is 50 mesh, the particle size of old red mud powder is 50 mesh, and the particle size of quicklime powder is 140 mesh; then take 10kg of electrolytic manganese slag powder and old red mud powder Add 3kg to the mixer, and then add 2L of the first red mud leachate, the pH of the first red mud leachate is 10, and the first stirring is performed at a stirring rate of 100r / min, stirring time is 10-15min, and ammonia gas is recovered , Get the first mixture;

[0058](2) Transfer th...

Example Embodiment

[0061]Example 2

[0062]A method for coordinated solidification treatment of electrolytic manganese slag and red mud includes the following steps:

[0063](1) Take the electrolytic manganese slag and fresh red mud to dry until the water content is below 20wt%, and then transport the electrolytic manganese slag, fresh red mud and quicklime to the crusher for crushing treatment to obtain electrolytic manganese slag powder and fresh red mud powder And quicklime powder, the particle size of electrolytic manganese slag powder is 120 mesh, the particle size of fresh red mud powder is 100 mesh, and the particle size of quicklime powder is 80 mesh; then take 10kg of electrolytic manganese slag powder and 3kg of fresh red mud powder and add to In the mixer, add 2L of the first red mud leachate. The pH of the first red mud leachate is 12.5. Perform the first stirring at a stirring rate of 150r / min and a stirring time of 10-15min. The ammonia gas is recovered to obtain the first A mixture

[0064](2) T...

Example Embodiment

[0067]Example 3

[0068]A method for coordinated solidification treatment of electrolytic manganese slag and red mud includes the following steps:

[0069](1) The electrolytic manganese slag, old red mud and quicklime are respectively transported to the crusher for crushing treatment to obtain electrolytic manganese slag powder, old red mud powder and quicklime powder. The particle size of the electrolytic manganese slag powder is 120 mesh, which is old The particle size of the red mud powder is 120 mesh, and the particle size of the quicklime powder is 50 mesh; then take 10kg of electrolytic manganese slag powder and 6kg of old red mud powder into the mixer, and then add 3L of the first red mud leachate. The pH of a red mud leachate is 12.5, the first stirring is performed, the stirring rate is 150r / min, and the stirring time is 10-15 minutes, and ammonia gas is recovered to obtain the first mixture;

[0070](2) Transfer the first mixture obtained in step (1) to the first mixer, and then ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a collaborative curing treatment method for electrolytic manganese slag and red mud. According to the method, quick lime, red mud and red mud leachate are adopted as raw materials to effectively cure and stabilize the electrolytic manganese slag, soluble alkali in the red mud exists in water in the form of OH-, reacts with manganese ions to generate precipitate, and reacts with ammonia nitrogen (NH3-N) to generate ammonia gas, and thus pollutants in the electrolytic manganese slag can be effectively removed. On one hand, the red mud leachate plays a role of a solvent, onthe other hand, alkaline substances in the red mud leachate play a role of reactants, thus the reaction rate is increased, and the treatment cost is reduced. The red mud and the red mud leachate areused, so that the use amount of the quick lime is effectively reduced, and the treatment cost is further reduced. According to the method, a step-by-step reaction means is adopted, the reaction efficiency is effectively improved, and the curing rate of manganese ions in the electrolytic manganese slag reaches 93.7% or above.

Description

technical field [0001] The invention belongs to the technical field of electrolytic manganese slag treatment, and in particular relates to a method for synergistic solidification treatment of electrolytic manganese slag and red mud. Background technique [0002] Manganese metal is a key basic material in the fields of metallurgy, chemical industry and aerospace, and is one of the national strategic resources. Pure manganese is mainly produced by electrolysis, so it is often called electrolytic metal manganese or electrolytic manganese. my country is a big country in the production, consumption and export of electrolytic manganese. According to statistics, in 2016, the output of electrolytic manganese in my country was as high as 1.15 million tons, accounting for more than 98.5% of the world's output of manganese metal. The electrolytic manganese production process will produce a large amount of electrolytic manganese slag, and every ton of electrolytic manganese produced w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B09B1/00C04B28/10C01C1/02
CPCB09B1/00C04B28/10C01C1/026C04B2111/00017C04B2111/00025C04B2111/00767C04B18/0409C04B18/0472
Inventor 刘津张军方
Owner GUIZHOU ACAD OF ENVIRONMENTAL SCI & DESIGNING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap