Preparation method of alumina fiber reinforced ceramic composite material containing alumina interface layer

A ceramic composite material and alumina fiber technology, which is applied in the field of alumina fiber reinforced ceramic composite materials, can solve the problems of high brittleness of alumina fiber, high preparation cost, large fiber damage, etc., and achieves a simple and easy preparation method and improves mechanical properties. performance, the effect of reducing yarn breakage waste

Active Publication Date: 2021-01-22
AEROSPACE INST OF ADVANCED MATERIALS & PROCESSING TECH
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method needs to weave continuous alumina fibers into three-dimensional fabrics in advance. Because alumina fibers are brittle and easy to break, the weaving process will cause great damage to the fibers, the utilization rate of alumina fibers is low, and the subsequent densification process of composite materials is complicated, resulting in It is expensive to prepare
In addition, due to the steric hindrance effect of the fiber, it is difficult for the alumina sol to penetrate into the interior of the fabric, resulting in poor uniformity of the interface layer on the surface of the fabric, thereby affecting the mechanical properties of the composite material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of alumina fiber reinforced ceramic composite material containing alumina interface layer
  • Preparation method of alumina fiber reinforced ceramic composite material containing alumina interface layer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] S1. Preparation of alumina sol: Add pseudoboehmite powder and ultrapure water into a three-necked flask, place it in an oil bath, set the heating temperature of the oil bath, heat and stir for 1 hour, then slowly add dilute Nitric acid solution, adjust the pH to 2.5-3.5, continue heating and stirring for 4 hours to obtain an alumina sol with a solid content of 8 wt%. The mass ratio of pseudo-boehmite powder and ultrapure water is 10:100, the heating reaction temperature is 85°C, and the concentration of dilute nitric acid is 1mol / L.

[0033] S2, pretreatment of alumina fiber: put alumina fiber (raw material with alumina as the main component, other components include mullite, silicon dioxide, boria) in a pressure vessel, pour ultrapure water, and heat to After 24 hours of heat preservation at 85°C, the alumina fibers were taken out, and dried naturally at room temperature to obtain continuous alumina fibers after removing the sizing agent.

[0034] S3. Winding molding ...

Embodiment 2

[0037] S1. Preparation of alumina sol: Add pseudo-boehmite powder and ultrapure water into a three-necked flask, place it in an oil bath, set the heating temperature of the oil bath, fully heat and stir for 2 hours, then slowly add dilute Nitric acid solution, adjust the pH to 2.5-3.5, continue heating and stirring for 3 hours to obtain an alumina sol with a solid content of 5 wt%. The mass ratio of pseudo-boehmite powder and ultrapure water is 15:100, the heating reaction temperature is 70°C, and the concentration of dilute nitric acid is 1mol / L.

[0038] S2. Pretreatment of alumina fiber: put the alumina fiber in a pressure vessel, pour ultrapure water into it, heat to 80°C, take out the alumina fiber after keeping it warm for 20 hours, and dry it naturally at room temperature to obtain the removal of the sizing agent After continuous alumina fiber.

[0039] S3. Winding molding preparation of alumina fiber reinforced ceramic matrix composites containing alumina interface la...

Embodiment 3

[0042]S1. Preparation of alumina sol: Add pseudoboehmite powder and ultrapure water into a three-necked flask, place it in an oil bath, set the heating temperature of the oil bath, fully heat and stir for 4 hours, then slowly add dilute Nitric acid solution, adjust the pH to 2.5-3.5, continue heating and stirring to react, and obtain an alumina sol with a solid content of 10wt% in 2 hours. The mass ratio of pseudo-boehmite powder and ultrapure water is 20:100, the heating reaction temperature is 90°C, and the concentration of dilute nitric acid is 1mol / L.

[0043] S2. Pretreatment of alumina fibers: put the alumina fibers in a pressure vessel, pour ultrapure water, heat to 80°C, take out the alumina fibers after 18 hours of heat preservation, and dry naturally at room temperature to obtain the removal of the sizing agent After continuous alumina fiber.

[0044] S3. Winding molding preparation of alumina fiber reinforced ceramic matrix composites containing alumina interface l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of an alumina fiber reinforced ceramic composite material containing an alumina interface layer, and relates to the technical field of alumina fiber reinforced ceramic composite materials, which comprises the following steps: preparing alumina sol by an acidolysis method, pretreating alumina fibers to remove an impregnating agent, impregnating the alumina sol, and winding the impregnated alumina sol on a core mold for molding; and repeatedly dipping the oxide sol for many times, drying the sol, and performing heat treatment to obtain the composite material. According to the method, the weaving forming process of the fiber prefabricated body is omitted, the aluminum oxide fiber reinforced ceramic matrix composite material is prepared in one stepby adopting a winding forming method, and yarn breaking waste of fibers in the weaving process is reduced. The alumina interface layer is formed between the alumina fiber and the oxide matrix, so thebonding strength between the fiber and the matrix is effectively reduced, the toughening and reinforcing effects of the fiber are exerted, and the mechanical properties of the composite material are improved. The preparation method provided by the invention has the advantages of simplicity, feasibility, low cost, no pollution and the like.

Description

technical field [0001] The invention relates to the technical field of alumina fiber-reinforced ceramic composite materials, in particular to a preparation method of alumina fiber-reinforced ceramic composite materials containing an alumina interface layer. Background technique [0002] The continuous alumina fiber reinforced oxide ceramic matrix composite material has high temperature resistance, oxidation resistance, good mechanical strength and heat insulation performance, and can be used for a long time at 1200 ° C. This material can replace the poor strength and toughness under high temperature oxidative conditions. Metal materials and non-oxide-based ceramic composite materials meet the application requirements of a new generation of aerospace vehicles and aero-engines, and have broad application prospects in aviation, aerospace, nuclear energy and other fields. Fiber-reinforced oxide composites tend to have a strong bond between the fiber and the matrix under high-tem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/80C04B41/87C04B35/64B29C70/34
CPCC04B41/87C04B41/5031C04B35/64B29C70/34C04B2235/6562C04B41/4584C04B41/0072
Inventor 慈吉良吴焘张剑吕毅赵英民张昊
Owner AEROSPACE INST OF ADVANCED MATERIALS & PROCESSING TECH