Random-color anti-static ceramic tile and preparation method thereof

An anti-static, ceramic tile technology, applied in the field of ceramic glaze, can solve problems such as loss of electrical conductivity, achieve low impact of metal oxides, and achieve the effect of sustainable production

Inactive Publication Date: 2021-02-05
佛山昕通新型材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is: to provide an antistatic ceramic tile of random color and its preparation method, by adding coloring materials, the problem of single brick color can be changed, and by adding elements with good conductivity, it will not lose its conductivity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Embodiment 1, a kind of antistatic ceramic tile glaze, is made of the following raw materials by weight: 10 parts of barium carbonate, 12 parts of zinc oxide, 3 parts of quartz, 14 parts of dolomite, 10 parts of washed soil, 46 parts of feldspar, 5 parts of talc, 30 parts of conductive powder, and 0.1 part of coloring material; wherein: the coloring material is metal oxide, and the metal oxide can be zirconia, ferric oxide and chromium oxide, or vanadium pentoxide, silicon Zirconium oxide and alumina; the weight ratio of zirconia, ferric oxide and chromium oxide is 25%:35%:40%. ; The weight ratio of vanadium pentoxide, zirconium silicate and aluminum oxide is 25%: 60%: 15%.

[0029] The preparation method of above-mentioned antistatic tile glaze, comprises the steps:

[0030] (1) Weigh barium carbonate, zinc oxide, quartz, dolomite, washed soil, feldspar, talc, conductive powder and coloring materials in proportion, and send them into a ball mill for grinding to obtain...

Embodiment 2

[0037] Embodiment 2, a kind of antistatic tile glaze, is made of the following raw materials by weight: 13 parts of barium carbonate, 14 parts of zinc oxide, 5 parts of quartz, 15 parts of dolomite, 11 parts of washed soil, 49 parts of feldspar, 7 parts of talc, 34 parts of conductive powder, and 0.3 part of coloring material; the coloring material is a metal oxide, and the metal oxide can be zirconia, ferric oxide and chromium oxide, or vanadium pentoxide, Zirconium silicate and alumina; the weight ratio of zirconia, ferric oxide and chromium oxide is 25%:35%:40%. ; The weight ratio of vanadium pentoxide, zirconium silicate and aluminum oxide is 25%: 60%: 15%. .

[0038] The preparation method of above-mentioned antistatic tile glaze, comprises the steps:

[0039] (1) Weigh barium carbonate, zinc oxide, quartz, dolomite, washed soil, feldspar, talc, conductive powder and coloring materials in proportion, and send them into a ball mill for grinding to obtain mixed powder A; ...

Embodiment 3

[0046] Embodiment 3, a kind of antistatic tile glaze, is made of the following raw materials by weight: 10 parts of barium carbonate, 12 parts of zinc oxide, 3 parts of quartz, 14 parts of dolomite, 10 parts of washed soil, 46 parts of feldspar, 5 parts of talc, 30 parts of conductive powder, 0.1 part of coloring material; among them: the coloring material is metal oxide, metal oxide can be zirconia, ferric oxide and chromium oxide, zirconia, ferric oxide and oxidized The weight ratio of chromium is 25%:35%:40%. .

[0047] The preparation method of above-mentioned antistatic tile glaze, comprises the steps:

[0048] (1) Weigh barium carbonate, zinc oxide, quartz, dolomite, washed soil, feldspar, talc, conductive powder and coloring materials in proportion, and send them into a ball mill for grinding to obtain mixed powder A;

[0049] (2) Add 0.4% methyl base, 0.45% sodium tripolyphosphate and 46% water to the mixed powder A, and mix and stir for 25-40 minutes to obtain the m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a random-color anti-static ceramic tile and a preparation method thereof. The random-color anti-static ceramic tile is prepared from the following raw materials in parts by weight: 10-13 parts of barium carbonate, 12-14 parts of zinc oxide, 3-5 parts of quartz, 14-15 parts of dolomite, 10-11 parts of water-washed soil, 46-49 parts of feldspar, 5-7 parts of talc, 30-34 partsof electrically conductive powder and 0.1-0.3 part of a coloring material. The situation that a ceramic tile is single in color is changed, the ceramic tile keeps good electric conductivity, a stableelectric conductive network is formed, the influence of metal oxide is reduced to the minimum, and sustainable production is realized.

Description

Technical field: [0001] The invention relates to a tile glaze, in particular to a random-color antistatic tile and a preparation method thereof, belonging to the technical field of ceramic glazes. Background technique: [0002] There are many different electrostatic tiles on the market. The common problem of electrostatic tiles is that the color is single, and the color can only be made into beige and light-colored tiles. In fact, this color is the original color of the glaze. If you make patterns or other dark colors (similar to Black) glaze, ceramic tiles will lose conductivity after being fired. This is a common problem in the market, and there is no way to solve it for the time being. It cannot meet the different styles and colors of consumer conductive tiles. Invention content: [0003] The technical problem to be solved by the present invention is to provide an antistatic ceramic tile of random color and its preparation method. By adding coloring materials, the probl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/86C04B41/5022C04B41/4539C04B41/0072
Inventor 陆奕建郑琳
Owner 佛山昕通新型材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com