A kind of preparation method of building tile grout

A technology of caulking agent and ceramic tiles, which is applied in the field of building materials, can solve the problems of ceramic tile caulking agents such as reduced pan-alkali resistance, unfavorable industrialization, and reduced strength, and achieves the effects of reducing pan-alkali phenomenon, reducing content, and improving compactness

Active Publication Date: 2022-04-08
广东靓砂建材科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method requires protein (such as bovine serum albumin) and protease, and the cost is extremely high, which is not conducive to industrialization. It can be seen from its examples that if no pretreatment hydrogel (Example 2) or no added degraded protein Modified zeolite (Example 3), tile grouting agent has significantly reduced pan-alkaline resistance and reduced strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A preparation method for building tile grout, comprising the following steps:

[0026] (1) Dissolve polyvinyl alcohol in an aqueous ethanol solution with a mass fraction of 20% at 90°C, and then add water-soluble resin liquid to obtain polyvinyl alcohol glue;

[0027] (2) Pulverize the natural zeolite and heat-preserve it at 250°C for 50 minutes to obtain the pretreated zeolite;

[0028] (3) Add alkali solution to ethanol aqueous solution of tetraethyl orthosilicate, control the pH to 9, then add lithium nitrate, stir and react at 73°C for 2 hours, mix the obtained solution with pretreated zeolite at a mass ratio of 13:1, and store at room temperature 1. Stir and mix for 60 minutes under the condition of rotating speed 350r / min and filter to obtain modified zeolite;

[0029] (4) Mix graphite and oxidant at a mass ratio of 1:5, then stir and react, then concentrate by rotary evaporation to obtain graphite oxide;

[0030] (5) Take 45 parts of cement, 45 parts of quartz ...

Embodiment 2

[0033] A preparation method for building tile grout, comprising the following steps:

[0034] (1) Dissolve polyvinyl alcohol in an aqueous ethanol solution with a mass fraction of 30% at 87°C, and then add a water-soluble resin solution to obtain polyvinyl alcohol glue;

[0035] (2) Pulverize the natural zeolite and heat-preserve it at 230°C for 60 minutes to obtain the pretreated zeolite;

[0036] (3) Add alkali solution to ethanol aqueous solution of tetraethyl orthosilicate, control the pH to 10, then add lithium nitrate, stir and react at 70°C for 1 hour, mix the obtained solution with pretreated zeolite at a mass ratio of 10:1, and store at room temperature 1. Stir and mix for 70 minutes under the condition of rotating speed 400r / min and filter to obtain modified zeolite;

[0037] (4) Mix graphite and oxidant at a mass ratio of 1:4, stir and react, and concentrate by rotary evaporation to obtain graphite oxide;

[0038] (5) Take 35 parts of cement, 40 parts of quartz sa...

Embodiment 3

[0041] A preparation method for building tile grout, comprising the following steps:

[0042] (1) Dissolve polyvinyl alcohol in an aqueous ethanol solution with a mass fraction of 10% at 95°C, and then add a water-soluble resin solution to obtain polyvinyl alcohol glue;

[0043] (2) Pulverize the natural zeolite and heat-preserve it at 260°C for 40 minutes to obtain the pretreated zeolite;

[0044] (3) Add alkali solution to ethanol aqueous solution of tetraethyl orthosilicate, control the pH to 8, then add lithium nitrate, stir and react at 75°C for 3 hours, mix the obtained solution with pretreated zeolite at a mass ratio of 15:1, and store at room temperature 1. Stir and mix for 70 minutes under the condition of rotating speed 300r / min and filter to obtain modified zeolite;

[0045] (4) Mix graphite and oxidant at a mass ratio of 1:6, then stir and react, then concentrate by rotary evaporation to obtain graphite oxide;

[0046] (5) Take 50 parts of cement, 50 parts of quart...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of building materials, and discloses a preparation method of a building tile joint filler. The preparation method of the building tile joint filler of the present invention comprises: (1) dissolving polyvinyl alcohol in ethanol aqueous solution, and then adding water-soluble resin liquid to obtain polyvinyl alcohol glue; (2) pulverizing natural zeolite, heat preservation and heat treatment to obtain Pretreatment zeolite; (3) Add alkali solution to ethanol aqueous solution of ethyl orthosilicate, control pH to 8‑10, then add lithium nitrate, stir and react, and mix the obtained solution with pretreatment zeolite to obtain modified zeolite; (4 ) Mix graphite with oxidant and stir to react to obtain graphite oxide; (5) Take cement, quartz sand, pigment, polyvinyl alcohol glue, modified zeolite and graphite oxide, stir and mix, then add water, and stir to obtain tile joint sealant . The method is suitable for large-scale industrial application, the process is simple, the cost is low, and it is easy to popularize, and the prepared ceramic tile grout has excellent mechanical properties and good pan-alkali resistance.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a preparation method of building tile grout. Background technique [0002] A kind of acid and alkali resistant porcelain or stone building or decorative material is called ceramic tile, which is formed by grinding, mixing, pressing, glazing and sintering with refractory metal oxides and semi-metal oxides. It is mostly made of clay, quartz sand, compressed after high temperature, etc., and has high hardness. In tile laying, it is essential to fill the gaps between bricks. Using tile grout to caulk the seams can ensure that there are no cracks in the seams, and has good anti-seepage performance. Prevent moisture and rainwater from penetrating into the wall, especially in winter, when the water infiltrated into the seams freezes and expands, causing the pasted bricks to fall off and affect the appearance. [0003] The traditional tile grout is made of cement as the main...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B20/02
CPCC04B28/04C04B20/023C04B2201/50C04B2111/00672C04B24/2623C04B14/047C04B14/024C04B14/06C04B2103/54
Inventor 蒋建平
Owner 广东靓砂建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com