Zirconite tailing and coal gangue ceramic grinding ball and preparation method thereof

A technology of coal gangue and zircon, which is applied in the field of zircon tailings and coal gangue ceramic grinding balls and their preparation, can solve the problems of polluting water environment, soil environment, destroying geological landscape, polluting atmospheric environment, etc. The effect of stable quality, realization of solid waste resource utilization, and reduction of firing temperature

Active Publication Date: 2021-02-19
江苏金石研磨有限公司
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is very harmful: coal gangue is stacked in the open air, occupying a large amount of cultivated land, forest land, residential areas, and industrial and mining land, and destroying the geological landscape; Dissolved substances can pollute the water environment and soil environment; dust or spontaneous combustion of gangue piles can also pollute the atmospheric environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Example 1: A zircon tailings and coal gangue ceramic grinding ball, including the following components by mass fraction: zircon tailings 40wt%, coal gangue 20wt%, alumina 18wt%, feldspar 10wt%, dolomite 3wt %, talc 1wt%, calcite 1wt%, barium carbonate 2wt%, quartz 5wt%; zircon tailings include the following mass fraction components: Al 2 o 3 40wt%, SiO 2 50wt%, ZrO 2 4wt%, TiO 2 2wt%, MgO2wt%, Fe 2 o 3 2wt%; coal gangue comprises the following mass fraction components: Al 2 o 3 35wt%, SiO 2 55wt%, carbon 10wt%. Alumina is high temperature α-alumina, Al in alumina 2 o 3 The content is 98.5wt%. Feldspar is potassium feldspar, K in potassium feldspar 2 O content is 9.5wt%, Al 2 o 3 The content is 14.5wt%, SiO 2 The content is 69wt%. The content of CaO in dolomite is 29 wt%, and the content of MgO is 20 wt%. The content of MgO in talc is 30.5wt%, SiO 2 The content of CaO in calcite is 62wt%; the content of CaO in calcite is 53wt%. BaCO in barium carbonat...

Embodiment 2

[0028] Example 2: A zircon tailings and coal gangue ceramic grinding ball, including the following components in mass fractions: 40wt% zircon tailings, 30wt% coal gangue, 10wt% alumina, 8wt% feldspar, 1wt dolomite %, talc 5wt%, calcite 1wt%, barium carbonate 2wt%, quartz 3wt%; the zircon tailings include the following mass fraction components: Al 2 o 3 50wt%, SiO 2 43wt%, ZrO 2 5wt%, TiO 2 0.2wt%, MgO1.6wt%, Fe 2 o 3 0.2wt%; coal gangue comprises the following mass fraction components: Al 2 o 3 40wt%, SiO 2 40wt%, carbon 20wt%. Alumina is high temperature α-alumina, Al in alumina 2 o 3 The content is 99wt%. Feldspar is albite, Na in albite2 O content is 10wt%, Al 2 o 3 The content is 16.5wt%, SiO 2 The content is 65wt%. The content of CaO in dolomite is 33 wt%, and the content of MgO is 23 wt%. The content of MgO in talc is 31wt%, SiO 2 The content of CaO in the calcite is 63wt%; the content of CaO in the calcite is 54wt%. BaCO in barium carbonate 3 The con...

Embodiment 3

[0029] Embodiment 3: A ceramic grinding ball of zircon tailings and coal gangue, comprising the following components in mass fraction: 45wt% of zircon tailings, 15wt% of coal gangue, 15wt% of alumina, 5wt% of feldspar, and 5wt of dolomite %, talc 5wt%, calcite 3wt%, barium carbonate 5wt%, quartz 10wt%; the zircon tailings include the following mass fraction components: Al 2 o 3 60wt%, SiO 2 35wt%, ZrO 2 2.5wt%, TiO 2 1wt%, MgO0.5wt%, Fe 2 o 3 1wt%; coal gangue includes the following mass fraction components: Al 2 o 3 45wt%, SiO 2 50wt%, carbon 5wt%. Alumina is high temperature α-alumina, Al in alumina 2 o 3 The content is 99.5wt%. Feldspar is two combinations of potassium feldspar and albite, K feldspar in K 2 O content is 11wt%, Al 2 o 3 The content is 15wt%, SiO 2 The content is 70wt%, Na in albite 2 O content is 11wt%, Al 2 o 3 The content is 17wt%, SiO 2 The content is 66wt%. The content of CaO in dolomite is 32 wt%, and the content of MgO is 22 wt%. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

A disclosed zirconite tailing and coal gangue ceramic grinding ball is prepared from the following components in percentage by mass: 40-80 percent of zirconite tailings, 5-30 percent of coal gangue, 5-20 percent of aluminum oxide, 2-10 percent of feldspar, 1-5 percent of dolomite, 1-5 percent of talc, 1-5 percent of calcite, 1-5 percent of barium carbonate and 1-10 percent of quartz. The inventionfurther discloses a preparation method of the zirconite tailing and coal gangue ceramic grinding ball. The ceramic grinding ball prepared by taking the zirconite tailings and the coal gangue as mainraw materials is suitable for the related fields of mine metal mineral grinding, white mineral grinding, petroleum fracturing propping agents and the like, solid waste resource utilization is realized, and the production cost is greatly reduced.

Description

technical field [0001] The invention relates to the field of ceramic grinding balls, in particular to a zircon tailings and coal gangue ceramic grinding ball and a preparation method thereof. Background technique [0002] The main producing countries of zircon in the world are Australia, the United States, Brazil, etc. my country's zirconium resource reserves rank fifth in the world, about 500,000 tons, accounting for only 1% of the world. The main producing areas are Guangdong, Hainan, Guangxi and other provinces, of which 94% of the production comes from seaside placer mines in Hainan. There are not many sources of zircon in my country, and Hainan sand has also been scarce in recent years. Therefore, the tailings produced by enriching zircon are also increasing year by year, the mining cost is getting higher and higher, and the tailing waste is also increasing. Environmental pressure is increasing. [0003] Coal gangue is the solid waste discharged during the process of co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B33/13C04B35/622
CPCC04B33/1328C04B33/13C04B35/62204C04B35/622C04B2235/3217C04B2235/3472C04B2235/321C04B2235/3445C04B2235/3208C04B2235/3215C04B2235/3418C04B2235/5436C04B2235/602C04B2235/656C04B2235/6562C04B2235/6567C04B2235/96C04B2235/77Y02P40/60
Inventor 王俊甫罗甲业周雄李强
Owner 江苏金石研磨有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap