Anti-skid sole and preparation method thereof

A kind of anti-skid, nitrile rubber technology, applied in the direction of soles, footwear, applications, etc., can solve the problems of hydrolysis resistance, poor wear resistance, lack of antistatic properties in the application range, etc., to improve wear resistance and anti-skid properties. Effect

Pending Publication Date: 2021-02-19
福建省华昂体育用品有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for soft polyurethane soles, there are poor wear resistance and no resistance to hydrolysis, which can easily lead to cracks and fractures on the soles, resulting in certain limitations in the application range of polyurethane soles. At the same time, the existing polyurethane soles do not have antistatic properties. performance, for which we propose an improved way

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A non-slip sole, the non-slip sole is made of the following raw materials in parts by mass: 80 parts of nitrile rubber, 15 parts of isoprene rubber, 20 parts of butadiene rubber, 50 parts of 185 white carbon black, 15 parts of zinc oxide, and 15 parts of stearic acid 15 parts, MB antiaging agent 15 parts, polyethylene glycol 15 parts, 40 / 60 antifogging agent 15 parts, accelerator 15 parts, antiscorch agent 15 parts, antioxidant 15 parts, anti-slip agent 15 parts, antistatic agent 15 parts 10 parts, 10 parts of IS-80 sulfur, 10-20 parts of DCP cross-linking agent and 10 parts of TS-80 accelerator.

[0023] Preferably, the antioxidant is selected from one or more combinations of vitamin E, melatonin, glutathione, vitamin C, and uric acid.

[0024] Preferably, the anti-scorch agent is selected from one or more combinations of benzoic acid, salicylic acid, phthalic anhydride and N-nitrosodiphenylamine.

[0025] Preferably, the antistatic agent is selected from one or more ...

Embodiment 2

[0032] A non-slip sole, the non-slip sole is made of the following raw materials in parts by mass: 70 parts of nitrile rubber, 10 parts of isoprene rubber, 15 parts of butadiene rubber, 45 parts of 185 white carbon black, 15 parts of zinc oxide, and 15 parts of stearic acid 15 parts, MB antiaging agent 15 parts, polyethylene glycol 15 parts, 40 / 60 antifogging agent 15 parts, accelerator 15 parts, antiscorch agent 15 parts, antioxidant 15 parts, anti-slip agent 15 parts, antistatic agent 15 parts 10 parts, 10 parts of IS-80 sulfur, 10 parts of DCP cross-linking agent and 10 parts of TS-80 accelerator.

[0033] Preferably, the antioxidant is selected from one or more combinations of vitamin E, melatonin, glutathione, vitamin C, and uric acid.

[0034] Preferably, the anti-scorch agent is selected from one or more combinations of benzoic acid, salicylic acid, phthalic anhydride and N-nitrosodiphenylamine.

[0035] Preferably, the antistatic agent is selected from one or more com...

Embodiment 3

[0042] A non-slip sole, the non-slip sole is made of the following raw materials in parts by mass: 85 parts of nitrile rubber, 20 parts of isoprene rubber, 20 parts of butadiene rubber, 55 parts of 185 white carbon black, 20 parts of zinc oxide, 120 parts of stearic acid 20 parts, MB antiaging agent 20 parts, polyethylene glycol 20 parts, 40 / 60 anti-fogging agent 20 parts, accelerator 20 parts, anti-scorch agent 120 parts, antioxidant 20 parts, anti-slip agent 20 parts, antistatic agent 20 parts 20 parts, 20 parts of IS-80 sulfur, 20 parts of DCP cross-linking agent and 20 parts of TS-80 accelerator.

[0043] Preferably, the antioxidant is selected from one or more combinations of vitamin E, melatonin, glutathione, vitamin C, and uric acid.

[0044] Preferably, the anti-scorch agent is selected from one or more combinations of benzoic acid, salicylic acid, phthalic anhydride and N-nitrosodiphenylamine.

[0045]Preferably, the antistatic agent is selected from one or more comb...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-skid sole. The anti-skid sole is prepared from the following raw materials in parts by mass: 70-90 parts of nitrile butadiene rubber, 10-20 parts of isoprene rubber, 15-25 parts of butadiene rubber, 45-60 parts of 185 white carbon black, 15-20 parts of zinc oxide, 15-20 parts of stearic acid, 15-20 parts of an MB anti-aging agent, 15-20 parts of polyethylene glycol,15-20 parts of a 40 / 60 anti-fogging agent, 15-20 parts of an accelerant, 15-20 parts of an anti-scorching agent, 15-20 parts of an antioxidant, 15-20 parts of an anti-slip agent, 15-20 parts of an anti-static agent, 10-20 parts of an additional medicine IS-80 sulfur, 10-20 parts of a DCP cross-linking agent and 10-20 parts of a TS-80 accelerant. According to the invention, the nitrile butadiene rubber, the isoprene rubber, the butadiene rubber and the 185 white carbon black are matched for use, so that the wear resistance and the skid resistance of the sole are improved, and meanwhile, the anti-scorching agent, the antioxidant, the anti-skid agent and the anti-static agent are added, so that the sole material has the anti-static property.

Description

technical field [0001] The invention relates to the technical field of anti-slip soles, in particular to an anti-slip sole and a preparation method thereof. Background technique [0002] The structure of the sole is quite complex. In a broad sense, it can include all the materials that make up the bottom, such as the outsole, midsole and heel. In a narrow sense, it only refers to the outsole. The common characteristics of general sole materials should be wear-resistant, water-resistant, oil-resistant, heat-resistant, pressure-resistant, impact-resistant, good elasticity, easy to fit the shape of the foot, and not easy to change after being shaped. Heat preservation, easy to absorb moisture, etc., and at the same time, it must cooperate with the midsole, which has a braking effect when walking and changing feet, so that it will not slip and is easy to stop. There are many types of sole materials, which can be divided into natural base materials and synthetic base materials. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/02C08L9/00C08L71/02C08K13/04C08K7/26C08K3/22C08K5/09C08K5/14A43B13/04
CPCC08L9/02A43B13/04C08K2003/2296C08L2205/035C08L2205/025C08L2201/04C08L9/00C08L71/02C08K13/04C08K7/26C08K3/22C08K5/09C08K5/14
Inventor 杜丕皇方业永谭楚元刘建国
Owner 福建省华昂体育用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More