A kind of outdoor floor water-based asphalt primer and its processing technology

A processing technology and modified asphalt technology, which is applied in the field of outdoor floor water-based asphalt primer and its processing technology, can solve the problems of poor corrosion resistance and poor overall application effect, and achieve high product quality, improved aging resistance, and good The effect of corrosion resistance

Active Publication Date: 2021-12-03
安徽欣苗新材料科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem of poor corrosion resistance in the prior art, which leads to poor overall application effect, the application provides a water-based asphalt primer for outdoor floors and its processing technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of outdoor floor water-based asphalt primer and its processing technology
  • A kind of outdoor floor water-based asphalt primer and its processing technology
  • A kind of outdoor floor water-based asphalt primer and its processing technology

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0053] The preparation method of modified asphalt A may further comprise the steps:

[0054] Step 1, weigh 1.3 parts of sodium dodecylbenzenesulfonate, 0.8 parts of Foamex-825 defoamer, 1.2 parts of hydroxyethyl cellulose, 0.6 parts of caustic alkali, 1.5 parts of sodium abietate And 42 parts of deionized water, put into the first reactor (commercially available, the electric heating reactor of Laizhou Shenglong Chemical Machinery Co., Ltd.), be warming up to 40 ℃, under the stirring speed of 400 rev / mins, mix 10 Minutes, then heated up to 60 ℃ to save the spare material A;

[0055] Step 2, weighing 50 parts of 70# asphalt, 12.5 parts of 90# asphalt and 5 parts of 110# asphalt, first throw 70# asphalt into the second reactor (commercially available, Laizhou Shenglong Chemical Machinery Co., Ltd. Electric heating reaction kettle), heated to 80°C, and kept stirring for 15 minutes at a stirring speed of 200 rpm, then poured 90# asphalt into the second reaction kettle, controlled...

preparation example 2

[0058] The difference between Preparation Example 2 and Preparation Example 1 is that modified asphalt B is prepared from the following raw materials in parts by weight: 47.6 parts of 70# asphalt, 8.2 parts of 90# asphalt, 2.2 parts of 110# asphalt, 1.2 parts of Sodium dodecylbenzenesulfonate, 0.8 parts of Foamex-825 defoamer, 1.0 parts of hydroxyethyl cellulose, 0.4 parts of caustic, 1.4 parts of sodium abietate and 40 parts of deionized water.

preparation example 3

[0060] Compounding of fillers: Weigh ultrafine calcium carbonate, tetragonal zirconia, pitch-based carbon fiber, and zinc oxide whiskers at a mass ratio of 8.8:1.2:2.3:0.8 , zinc oxide whiskers, put ultra-fine calcium carbonate, tetragonal zirconia, pitch-based carbon fiber, and zinc oxide whiskers into the disperser (twin-shaft stirring disperser, electric heating reactor of Laizhou Shenglong Chemical Machinery Co., Ltd.) , at a stirring speed of 200 rpm, stirred for 2 minutes to obtain filler A.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The application relates to the technical field of asphalt paint production, in particular to a water-based asphalt primer for outdoor floors and its processing technology. A water-based asphalt primer for outdoor floors is prepared from the following raw materials in parts by weight: modified asphalt, filler, film-forming resin emulsion, emulsifier, liquid-phase rare earth stabilizer, film-forming stabilizer, defoamer, initiator agent, UV agent, deionized water. The water-based asphalt primer of the present application has good corrosion resistance, low temperature resistance and aging resistance, and can improve the impact strength of the outdoor floor at the same time. The processing technology of the present invention is: first weigh the modified asphalt and put it into the batching device, then weigh the film-forming resin emulsion and deionized water, and then put in the weighing filler, liquid phase rare earth stabilizer, UV agent, emulsifier, film-forming Stabilizer, defoamer, and initiator are placed in the batching device, stirred, vacuumed, naturally cooled to room temperature, finally screened, and filled. This process has the advantage of quantitative production to obtain high-quality asphalt primer.

Description

technical field [0001] The application relates to the technical field of asphalt paint production, in particular to a water-based asphalt primer for outdoor floors and a processing technology thereof. Background technique [0002] The outdoor floor must be able to withstand the changeable outdoor weather and strong temperature changes. Therefore, the floor must have the characteristics of strong stability, strong corrosion resistance, and strong pressure resistance. By coating the surface of the outdoor floor with anti-corrosion primer or anti-corrosion paint. At present, the vast majority of anti-corrosion coatings at home and abroad are mainly solvent-based coatings. Solvent-based anti-corrosion coatings pose a greater threat to the environment and human health. The study of lacquer has received great attention. Asphalt is a commonly used anti-corrosion material with low cost and wide sources of raw materials. Petroleum asphalt has good adhesion, anti-aging and anti-cor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D195/00C09D111/02C09D127/16C09D7/61C09D7/65C09D5/08C09D5/00B01F13/06B01F7/18B01F3/08B01F3/00B01F23/00
CPCC09D195/00C09D5/08C09D7/65C09D7/61C09D7/70C09D5/002C08L2205/035C08L2205/025C08K2003/265C08K2003/2244B01F23/09B01F23/405B01F23/43B01F27/90B01F33/70B01F2101/30C08L11/02C08L27/16C08L33/04C08K13/04C08K3/22C08K3/26C08K7/06C08K7/08
Inventor 林海
Owner 安徽欣苗新材料科技有限公司