Preparation method of high-strength casting coating for stainless steel casting
A casting coating, high-strength technology, used in casting molding equipment, coatings, molds, etc., can solve problems such as poor strength, and achieve the effect of improving the strength of the coating film, reducing stress concentration, and increasing the area
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0033]In parts by weight, weigh 10 parts of zirconia whiskers with an average length of 20 μm, 10 parts of silicon carbide whiskers with an average length of 10 μm, 2 parts of ethyl orthosilicate, 10 parts of nitric acid solution with a mass fraction of 10%, 120 Add ethyl silicate and nitric acid to absolute ethanol, stir at 200~250r / min for 10 minutes at room temperature to obtain a modified solution, add zirconia whiskers and silicon carbide whiskers to the modified solution , stirred at 400r / min for 40min in a water bath at 50°C to obtain a mixed whisker suspension, put the mixed whisker suspension in an ultrasonic disperser, and ultrasonically treat it at 30°C with a power of 300W for 20min , to obtain a mixed whisker dispersion, put the mixed whisker dispersion in a centrifuge, centrifuge at a speed of 4000r / min at room temperature for 20min, take the lower layer of solid, wash it with deionized water until neutral, and place it in an oven at 80°C Drying in medium tempera...
Embodiment 2
[0037] In parts by weight, weigh 15 parts of zirconia whiskers with an average length of 25 μm, 15 parts of silicon carbide whiskers with an average length of 15 μm, 3 parts of tetraethyl orthosilicate, 15 parts of nitric acid solution with a mass fraction of 10%, 180 Add ethyl silicate and nitric acid to absolute ethanol, stir at 225r / min for 15min at room temperature to obtain a modified solution, add zirconia whiskers and silicon carbide whiskers to the modified solution, and Stirring treatment at 450r / min for 50min in a water bath at 55°C to obtain a mixed whisker suspension, put the mixed whisker suspension in an ultrasonic disperser, and ultrasonically treat it at 35°C with a power of 350W for 25min to obtain Mix the whisker dispersion, put the mixed whisker dispersion in a centrifuge, centrifuge at a speed of 4500r / min for 25min at room temperature, remove the lower layer of solid, wash with deionized water until neutral, and dry in an oven at 90°C 1.5h, cooled at room ...
Embodiment 3
[0041] In parts by weight, weigh 20 parts of zirconia whiskers with an average length of 30 μm, 20 parts of silicon carbide whiskers with an average length of 20 μm, 4 parts of tetraethyl orthosilicate, 20 parts of nitric acid solution with a mass fraction of 10%, 240 Add ethyl silicate and nitric acid to absolute ethanol, and stir at 250r / min for 20 minutes at room temperature to obtain a modified solution. Add zirconia whiskers and silicon carbide whiskers to the modified solution, and mix at 60 Under the condition of a water bath at 500r / min for 60min, a mixed whisker suspension was obtained. The mixed whisker suspension was placed in an ultrasonic disperser, and ultrasonically treated at 40°C with a power of 400W for 30min to obtain a mixed whisker suspension. Whisker dispersion, put the mixed whisker dispersion in a centrifuge, centrifuge at a speed of 5000r / min for 30min at room temperature, remove the lower layer of solid, wash with deionized water until neutral, and dry...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
quality score | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com