Antibacterial halogen-free flame-retardant PC/ABS composite material with high ball pressure temperature and preparation method thereof

A technology of composite materials and high balls, applied in the field of thermoplastic polymer materials

Active Publication Date: 2021-04-20
株洲时代工程塑料实业有限公司
View PDF12 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This patent uses graphene with a two-dimensional layered structure to form a physical barrier layer to play a flame-retardant role, thereby reducing the amount of phosphate ester to improve heat resistance. Since graphene is black, this solution is only applicable to black products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial halogen-free flame-retardant PC/ABS composite material with high ball pressure temperature and preparation method thereof
  • Antibacterial halogen-free flame-retardant PC/ABS composite material with high ball pressure temperature and preparation method thereof
  • Antibacterial halogen-free flame-retardant PC/ABS composite material with high ball pressure temperature and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3

[0032] A kind of halogen-free flame-retardant PC / ABS composite material of antibacterial high ball pressure temperature of the present invention, by mass parts, the halogen-free flame-retardant PC / ABS composite material of embodiment 1-3 is made up of each component shown in table 1 Prepared after blending and melting, wherein:

[0033] The melt index of PC is 10g / 10min under the test conditions of 300°C and 1.2Kg;

[0034] ABS is 28 / 10min under the test conditions of 220°C and 10Kg;

[0035] The toughening agent is methyl methacrylate-butadiene-styrene terpolymer (MBS);

[0036] The antibacterial agent is a nano-zinc and silver composite antibacterial agent of zirconium phosphate carrier;

[0037] The anti-dripping agent is polytetrafluoroethylene coated with acrylonitrile-styrene copolymer;

[0038] The dispersant is PETS;

[0039] The antioxidant is obtained by compounding Irganox 1076 and Irganox 168 at a mass ratio of 1:1;

[0040] The preparation method of organopho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melt indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antibacterial halogen-free flame-retardant PC / ABS composite material with high ball pressure temperature. The composite material mainly comprises the following components in parts by mass: 59-88 parts of PC, 520 parts of ABS, 4-12 parts of an organophosphorus flame retardant, 2-5 parts of a flexibilizer, 0.4-1 part of an antibacterial agent, 0.2-0.5 part of an anti-dripping agent, 0.2-1 part of a dispersing agent and 0.2-1 part of an antioxidant. The halogen-free flame-retardant PC / ABS composite material is good in antibacterial property, high in ball pressure resistant temperature, good in flame retardant property and white in color, various bright-colored products can be manufactured by adding the coloring agent, no halogen flame retardant is adopted, the flame retardant grade of the material is high, cost is low, smell is small, and large-area application and popularization are facilitated. The invention also discloses a preparation method of the composite material. The preparation method is simple to operate, low in cost, short in preparation period and convenient for large-scale production.

Description

technical field [0001] The invention belongs to the technical field of thermoplastic polymer materials, and in particular relates to an antibacterial and high ball pressure temperature halogen-free flame-retardant PC / ABS composite material and a preparation method thereof. Background technique [0002] PC / ABS is an alloy material formed by blending PC (polycarbonate) and ABS (acrylonitrile-butadiene-styrene copolymer) resin in a certain proportion. It has excellent heat resistance, toughness, mechanical Performance, thermal stability and dimensional stability, it has been widely used in automotive interior and exterior parts, household appliances, consumer electronics and communication equipment and other fields. Since both PC and ABS materials are flammable or flammable materials, the greater the amount and scope of their use, this will bury safety hazards for fire prevention. Therefore, flame-retardant polymer materials are promoted in more application fields. Due to the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L69/00C08L55/02C08L51/04C08L27/18C08L33/20C08K13/06C08K9/12C08K3/08C08K5/5397C08K5/134C08K5/526
Inventor 李雄武胡天辉宋克东甘典松王雪晴
Owner 株洲时代工程塑料实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com