Water-based polyamide-imide anti-corrosion non-stick coating and preparation method thereof

A polyamide-imide, non-stick coating technology, used in anti-corrosion coatings, fire-retardant coatings, coatings, etc., can solve the problems of poor safety, high VOCs emission, and anti-corrosion performance to be improved.

Active Publication Date: 2021-05-07
HANGZHOU JIHUA POLYMER MATERIAL CO LTD +1
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, at present, domestic PAI resins are mainly solvent-based, and organic solvents need to be used as diluting solvents, which cause great environmental pollution and poor safety. Moreover, when used in water-based non-stick coatings, more organic solvents will be introduced, resulting in higher VOCs emissions in the end.
However, the synthesis technology of water-based PAI is relatively difficult, and it is still controlled by a few companies (such as Solvay's AI-10, Quark's SI-601, Bolian's BLPSY225, etc.), and there is a certain technical threshold, and water-based PAI is used as a viscous material. Knot resin is sprayed on iron substrates, compared with oil-based PAI, the anti-corrosion performance still needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based polyamide-imide anti-corrosion non-stick coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0062] A preparation method of water-based polyamide-imide anti-corrosion non-stick coating, comprising the following steps:

[0063] 1) Preparation of PAI:

[0064] 1.1) Scheme 1: add trimellitic anhydride to the reaction flask and dissolve in N-methylpyrrolidone and xylene, under the protection of an inert gas, heat to 70-90°C, when the trimellitic anhydride is completely dissolved, add diphenylmethane-4, 4'-diisocyanate, heat preservation reaction for 1-3h, heat up to 120-140°C, continue heat preservation reaction for 3-5h, wash with absolute ethanol, suction filter and dry to obtain PAI; trimellitic anhydride and diphenylmethane-4,4 The molar ratio of '-diisocyanate is 1:1-1.05, the quality of N-methylpyrrolidone is 2-3 times of the sum of trimellitic anhydride and diphenylmethane-4,4'-diisocyanate, and the content of xylene is 5- 10 wt%.

[0065] 1.2) Option 2:

[0066] Preparation of isocyanate-terminated polyamide-imide: dissolve the acid anhydride in a solvent, heat...

Embodiment 1

[0075] 1) Preparation of PAI: Add trimellitic anhydride to the reaction flask and dissolve in NMP and xylene, under nitrogen protection, heat to 70°C, when trimellitic anhydride is completely dissolved, add diphenylmethane-4,4'-diisocyanate, Heat preservation reaction for 3 hours, heat up to 120°C, continue heat preservation reaction for 5 hours, wash with absolute ethanol, suction filter and dry to obtain PAI. The mol ratio of trimellitic anhydride and diphenylmethane-4,4'-diisocyanate is 1:1, the quality of NMP is 2 times of the sum of trimellitic anhydride and diphenylmethane-4,4'-diisocyanate, and the content of xylene is 5wt%.

[0076] 2) Preparation of PAI emulsion: Dissolve the PAI prepared in step 1) in 5wt% of NMP, add 1wt% of SDBS and TMN-10 with a mass ratio of 1:6, mix evenly with high-speed shear stirring, and the stirring rate is 6000rpm , and then dropwise add 70wt% deionized water until the viscosity of the system drops suddenly, less than 1Pa·s, add the unfin...

Embodiment 2

[0079] 1) Preparation of PAI: add trimellitic anhydride to the reaction flask and dissolve in NMP and xylene, under nitrogen protection, heat to 90°C, when the trimellitic anhydride is completely dissolved, add diphenylmethane-4,4'-diisocyanate, Heat preservation reaction for 1 hour, heat up to 140°C, continue heat preservation reaction for 3 hours, wash with absolute ethanol, suction filter and dry to obtain PAI. The mol ratio of trimellitic anhydride and diphenylmethane-4,4'-diisocyanate is 1: 1.05, the quality of NMP is 3 times of the sum of trimellitic anhydride and diphenylmethane-4,4'-diisocyanate, and the content of xylene is 10 wt%.

[0080] 2) Preparation of PAI emulsion: Dissolve the PAI prepared in step 1) in 10wt% NMP, add 2wt% of STBS and TMN-6 with a mass ratio of 1:2, mix evenly with high-speed shear stirring, and the stirring rate is 4000rpm , and then dropwise add 65wt% deionized water until the viscosity of the system suddenly drops to less than 1Pa·s, add t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of coatings, and discloses a water-based polyamide-imide anti-corrosion non-stick coating and a preparation method thereof. The water-based polyamide-imide anti-corrosion non-stick coating comprises 30-60 parts of a fluororesin emulsion, 20-40 parts of a PAI emulsion, 15-30 parts of an anti-corrosion functional filler, 10-20 parts of a pigment, 1-5 parts of an auxiliary agent, 1-5 parts of a pH regulator, and 10-30 parts of water. According to the invention, PAI resin is firstly prepared, then an anionic surfactant and a nonionic surfactant are compounded as an emulsifier, and the PAI emulsion with good stability is prepared by a phase inversion method. The PAI emulsion and the fluororesin emulsion form the composite resin, the flaky or flaky anticorrosive filler is added into the composite resin to obtain the polyamide-imide anticorrosive non-stick coating, and the anticorrosive filler and the adhesive resin can form a compact coating, so the corrosion resistance of a coating film can be effectively enhanced.

Description

technical field [0001] The invention relates to the field of polymer materials, in particular to a water-based polyamide-imide anti-corrosion and non-stick coating and a preparation method thereof. Background technique [0002] Non-stick coating is a special coating whose coating surface is not easily adhered by other substances or easily removed after adhesion. The coating formed by this type of coating has the characteristics of extremely low surface energy, small friction coefficient, and easy sliding, and is widely used in household appliances, cooking utensils, automobiles, machinery, and chemical industries. Compared with traditional oil-based coatings, water-based non-stick coatings have the advantages of less organic solvents, better safety, less environmental pollution and compliance with food hygiene requirements. It is one of the guiding directions of national industrial policies. Water-based non-stick coatings are mainly composed of fluororesin dispersions such ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/18C09D179/08C09D5/08C08G73/14C08G81/00C08J3/03C08L79/08
CPCC09D127/18C09D179/08C09D5/08C09D5/18C08G73/14C08G81/00C08J3/03C08J2379/08C08L2201/08C08L79/08C08K13/04C08K7/00C08K3/34C08K3/042C08L27/18C08K3/40
Inventor 刘海龙钱涛
Owner HANGZHOU JIHUA POLYMER MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap