Nitrogen dioxide sensor based on composite material blocking effect and preparation method thereof

A blocking effect, composite material technology, applied in the direction of material resistance, can solve the problems of high power consumption and poor gas sensor performance, and achieve the effect of large response, fast response/recovery speed, and good recovery

Active Publication Date: 2022-05-06
UNIV OF ELECTRONICS SCI & TECH OF CHINA
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a nitrogen dioxide sensor based on the blocking effect of composite materials and a preparation method thereof to solve the problems of poor performance and high power consumption of gas sensors at room temperature in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nitrogen dioxide sensor based on composite material blocking effect and preparation method thereof
  • Nitrogen dioxide sensor based on composite material blocking effect and preparation method thereof
  • Nitrogen dioxide sensor based on composite material blocking effect and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The sensitive device selected in this embodiment is a flexible interdigital electrode, and the interdigital electrode is a gold electrode made on a flexible polyimide (PI) substrate. The interdigital spacing of the interdigital electrode is 200 μm, and the interdigital width of the interdigital electrode is The electrode thickness of the interdigitated electrode is 200 μm, and the electrode thickness of the interdigitated electrode is 100 nm; in this embodiment, the γ-polyglutamic acid / Ti2C3Tx composite material is selected as the gas sensitive material, and the composite thin film sensitive layer is prepared by a drop coating process, and its specific process steps are:

[0035] (1) Pretreatment of PI substrate gold interdigitated electrodes, cleaning with deionized water, acetone, alcohol and deionized water; dry for later use;

[0036] (2) Prepare the γ-polyglutamic acid dispersion, the solvent is deionized water, configure the γ-polyglutamic acid dispersion with a co...

Embodiment 2

[0041] The sensitive device selected in this embodiment is a flexible interdigital electrode, and the interdigital electrode is a gold electrode made on a flexible polyimide (PI) substrate. The interdigital spacing of the interdigital electrode is 200 μm, and the interdigital width of the interdigital electrode is 200 μm, and the electrode thickness of interdigitated electrode is 100nm; Select gamma-polyglutamic acid / multi-walled carbon nanotube (MWCNTs) composite material as gas-sensitive material in the present embodiment, adopt spraying process to prepare composite film sensitive layer, its concrete The process steps are:

[0042] (1) Pretreatment of PI substrate gold interdigitated electrodes, cleaning with deionized water, acetone, alcohol and deionized water; dry for later use;

[0043] (2) Prepare the γ-polyglutamic acid dispersion, the solvent is deionized water, configure the γ-polyglutamic acid dispersion with a concentration of 1 mg / mL, and use it for later use afte...

Embodiment 3

[0048] In this embodiment, the sensitive device is a flexible interdigital electrode, and the interdigital electrode is a nickel-chromium-gold electrode on a flexible PET substrate. The interdigital spacing of the interdigital electrode is 50 μm, the interdigital width is 50 μm, and the electrode thickness is 100 nm; In this example, the γ-polyglutamic acid / carbon nanofiber composite material is selected as the gas-sensitive material, and the composite film sensitive layer is prepared by a drop coating process, and the specific process steps are as follows:

[0049] (1) Pre-treat the nickel-chromium-gold interdigitated electrode on the PET substrate, wash it with ionized water, acetone, alcohol and deionized water; after drying, perform 10min ultraviolet hydrophilic treatment and set aside;

[0050] (2) Prepare the γ-polyglutamic acid dispersion, the solvent is deionized water, configure the γ-polyglutamic acid dispersion with a concentration of 1 mg / mL, and use it for later us...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
interdigital gapaaaaaaaaaa
Login to view more

Abstract

The invention provides a nitrogen dioxide sensor based on the blocking effect of composite materials and a preparation method thereof, and relates to the technical field of gas sensors and composite nanomaterials, including sensitive devices, on which a gas-sensitive layer is arranged, and the gas-sensitive layer adopts a composite material with blocking effect The material is made; the preparation method includes the following steps: S1: pretreating the substrate of the sensitive device, including cleaning, drying, and hydrophilic treatment; S2: preparing a polymer dispersion and an inorganic conductive material dispersion; S3: making the sensitive material The dispersion liquid is deposited on the substrate of the sensitive device to form a gas-sensing layer; S4: drying and aging the sensitive device with the gas-sensing layer to obtain a nitrogen dioxide sensor based on the blocking effect of the composite material. The nitrogen dioxide sensor of the present invention has the characteristics of large response, fast response / recovery speed, good recovery, and good repeatability. Development of power consumption devices.

Description

technical field [0001] The invention relates to the technical field of gas sensors and composite nanomaterials, in particular to a nitrogen dioxide sensor based on the blocking effect of composite materials and a preparation method thereof. Background technique [0002] As a poisonous and irritating gas, nitrogen dioxide (NO 2 ) is the main air pollutant, which can cause reduction of atmospheric visibility, acidification of surface water, eutrophication and increase of toxin content of aquatic organisms; in addition, NO 2 After being inhaled by the human body, it is highly irritating and corrosive to lung tissue. Therefore, the development of NO 2 Gas sensors are of great significance. [0003] Currently, NO 2 Most gas sensors are based on the electron transport mechanism. For example, the invention patent with application number 201910276010.0 discloses a nitrogen dioxide sensor based on two-dimensional molybdenum disulfide nanomaterials. Molybdenum sulfide adsorbs NO ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G01N27/12
CPCG01N27/12
Inventor 太惠玲赵秋妮黄琦蒋亚东段再华王斯刘勃豪张亚杰
Owner UNIV OF ELECTRONICS SCI & TECH OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap