Water-borne epoxy resin coating, water-borne epoxy resin coating layer, floor and preparation method of water-borne epoxy resin coating layer

A water-based epoxy resin and water-based epoxy technology, applied in the field of coatings, can solve problems such as harsh construction conditions

Active Publication Date: 2021-05-11
ASIA PAINT SHANGHAI
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the water-based epoxy resin coatings on the market have harsh construction conditions. The construction can only be carried out under the condition that the ambient temperature is 8°C-35°C, the humidity is <80%, and the surface temperature is 3°C higher than the dew point temperature, so it is severely limited. its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045] One embodiment of the present invention provides the preparation method of above-mentioned waterborne epoxy resin coating, comprises the following steps:

[0046] S101: Mix the raw materials of component A and stir evenly to prepare component A;

[0047] S102: Mix the raw materials of component B and stir evenly to prepare component B.

[0048] One embodiment of the present invention provides a water-based epoxy resin coating, which is prepared by using the above-mentioned water-based epoxy resin coating.

[0049] One embodiment of the present invention provides a kind of preparation method of waterborne epoxy coating, comprises the following steps:

[0050] S201: Provide the above-mentioned water-based epoxy resin coating;

[0051] In step S201, the water-based epoxy resin coating is as described above, and will not be repeated here.

[0052] Further, in step S201, the preparation method of waterborne epoxy resin coating comprises the following steps:

[0053] S201...

Embodiment 1

[0063] A component: non-ionic water-based epoxy curing agent 45%, water-based polyamide curing agent 2%, latex powder 3%, dispersant 0.8%, defoamer 0.3%, titanium dioxide 15%, barium sulfate 15%, Quartz powder 8%, wax powder 1.5%, water balance;

[0064] B component: 128 resin (hydrogenated bisphenol A type epoxy resin) 90%, reactive diluent AGE 7.5%, emulsifier 2.5%.

[0065] Preparation:

[0066] (1) Mix all the raw materials of component A, and stir for 30-40 minutes under the condition of 1300-1500r / min to prepare component A;

[0067] (2) Mix the raw materials of component B and stir evenly to obtain component B;

[0068] (3) Mix component A and component B at a mass ratio of 6:1 to prepare a mixed slurry;

[0069] (4) Construction under the environment of about 0 °, the mixed slurry is coated on the substrate, and dried to obtain the water-based epoxy resin coating of Example 1.

Embodiment 2

[0071] A component: non-ionic water-based epoxy curing agent 50%, water-based polyamide curing agent 2.5%, latex powder 3.5%, dispersant 1%, defoamer 0.4%, titanium dioxide 17%, barium sulfate 15%, Quartz powder 8%, wax powder 1.2%, water balance;

[0072] Component B: 128 resin (hydrogenated bisphenol A type epoxy resin) 89%, active diluent AGE 8%, emulsifier 3%; A:B=5:1 mixing and stirring.

[0073] Preparation:

[0074] (1) Mix all the raw materials of component A, and stir for 30-40 minutes under the condition of 1300-1500r / min to prepare component A;

[0075] (2) Mix the raw materials of component B and stir evenly to obtain component B;

[0076] (3) Mix component A and component B at a mass ratio of 5:1 to prepare a mixed slurry;

[0077] (4) Construction under the environment of about 0 °, the mixed slurry is coated on the substrate, and dried to obtain the water-based epoxy resin coating of Example 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a water-borne epoxy resin coating, a water-borne epoxy resin coating layer, a floor and a preparation method of the water-borne epoxy resin coating layer. Thewater-borne epoxy resin coating comprises a component A and a component B, wherein the component A comprises the following components in parts by weight: 40-60 parts of a nonionic waterborne epoxy curing agent, 2-3 parts of a waterborne polyamide curing agent, 1.1-2 parts of an auxiliary agent and 20-50 parts of powder; the hydrogen equivalent of the nonionic waterborne epoxy curing agent is 120 to 280; the powder comprises latex powder, quartz powder, wax powder, titanium dioxide and barium sulfate; and the component B comprises the following components in parts by weight: 83-91 parts of hydrogenated bisphenol A type epoxy resin, 3-10 parts of a diluent and 1-3 parts of an emulsifier. The water-borne epoxy resin coating can be constructed in a low-temperature environment (such as about 0 DEG C), and a coating obtained through construction has high wear resistance and hardness.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to water-based epoxy resin coatings, water-based epoxy resin coatings, floors and preparation methods thereof. Background technique [0002] Epoxy resin coatings are widely used in the preparation of epoxy resin floors, especially industrial floors, due to their high hardness, good wear resistance, strong adhesion, good flexibility, and excellent chemical corrosion resistance. At present, epoxy resin floors are mainly divided into solvent-based epoxy resin floors and water-based epoxy resin floors. Among them, solvent-based epoxy resin floors contain a large amount of volatile organic solvents, which have a greater impact on the environment, so they are gradually replaced by water-based epoxy resin floors. At present, the water-based epoxy resin floor on the market is mainly prepared by mixing and proofing curing agent, various additives and powder, and then compounded with 128 ep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D7/61C09D7/65C09D7/20C08G59/40C08G59/68E04F15/12
CPCC09D163/00C09D7/61C09D7/65C09D7/20C08G59/40C08G59/686E04F15/12C08K2003/2241C08K2003/3045C08L2205/035C08L2205/025C08L91/06C08L71/02C08L63/00C08K3/36C08K3/22C08K3/30
Inventor 毛美琴李金钟徐志新
Owner ASIA PAINT SHANGHAI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com