A kind of waterproof dry-mixed mortar and its production process

A technology of dry-mixed mortar and production process, applied in the field of mortar production, which can solve the problems of poor construction workability, high cost of raw materials, low cohesive force, etc., reduce the amount of large particles or impurities, have good durability, and improve water retention sexual effect

Active Publication Date: 2021-09-21
浙江龙游通衢建材有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a waterproof dry-mixed mortar and its production process to solve the problems of high raw material cost, poor construction workability, low cohesive force, poor impermeability, easy cracking, falling off and leakage proposed in the above background technology The problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of waterproof dry-mixed mortar and its production process
  • A kind of waterproof dry-mixed mortar and its production process
  • A kind of waterproof dry-mixed mortar and its production process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A waterproof dry-mixed mortar, comprising the following powders, the components are calculated as percentages by weight:

[0040]

[0041] The mixed sand includes yellow sand and improved powder, and the yellow sand replacement rate of the improved powder is 30-%-35%. The improved powder includes fly ash and stone powder, and the ratio of fly ash and stone powder is 5:1.

[0042] The redispersible polymer rubber powder is selected from HPMC-45000, and the silicone waterproofing agent is a composite siloxane formed by copolymerization of polydimethylsiloxane and long carbon chain alkylpolysiloxane.

[0043] The water-retaining thickener is formed by mixing starch ether, cellulose ether and bentonite, and the mixing ratio of the starch ether, cellulose ether and bentonite is 1:4:10.

[0044]The additives include expansion agent and water reducer, the weight percentage of the expansion agent is 6.5%, and the rest is water reducer.

[0045] The expansion agent is calciu...

Embodiment 2

[0048] A waterproof dry-mixed mortar, comprising the following powders, the components are calculated as percentages by weight:

[0049]

[0050]

[0051] The mixed sand includes yellow sand and improved powder, and the yellow sand replacement rate of the improved powder is 30-%-35%. The improved powder includes fly ash and stone powder, and the ratio of fly ash and stone powder is 5:1.

[0052] The redispersible polymer rubber powder is selected from HPMC-45000, and the silicone waterproofing agent is a composite siloxane formed by copolymerization of polydimethylsiloxane and long carbon chain alkylpolysiloxane.

[0053] The water-retaining thickener is formed by mixing starch ether, cellulose ether and bentonite, and the mixing ratio of the starch ether, cellulose ether and bentonite is 1:4:10.

[0054] The admixture comprises an expansion agent and a water reducer, the weight percentage of the expansion agent is 8%, and the rest is a water reducer.

[0055] The expan...

Embodiment 3

[0058] A waterproof dry-mixed mortar, comprising the following powders, the components are calculated as percentages by weight:

[0059]

[0060] The mixed sand includes yellow sand and improved powder, and the yellow sand replacement rate of the improved powder is 30-%-35%. The improved powder includes fly ash and stone powder, and the ratio of fly ash and stone powder is 5:1.

[0061] The redispersible polymer rubber powder is selected from HPMC-45000, and the silicone waterproofing agent is a composite siloxane formed by copolymerization of polydimethylsiloxane and long carbon chain alkylpolysiloxane.

[0062] The water-retaining thickener is formed by mixing starch ether, cellulose ether and bentonite, and the mixing ratio of the starch ether, cellulose ether and bentonite is 1:4:10.

[0063] The admixture comprises an expansion agent and a water reducer, the weight percentage of the expansion agent is 6%, and the rest is a water reducer.

[0064] The expansion agent i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waterproof dry-mixed mortar in the technical field of mortar production and a production process thereof, which comprises the following powder, and the components are calculated by weight percentage: 40%-60% of ordinary Portland cement, 30%-50% of mixed sand %, redispersible polymer rubber powder 1%-1.5%, silicone waterproofing agent 0.2%-1.2%, fiber 0%-0.3%, water-retaining thickener 0.6%-1.5%, and the balance is admixture; and It is prepared by the following process: screen the components of the mixed sand through a sieving device, measure and mix them according to the proportion; mix starch ether, cellulose ether and bentonite according to the proportion to obtain a water-retaining thickener; ordinary silicate Cement, mixed sand after screening and mixing, redispersible polymer rubber powder, silicone waterproofing agent, fiber, water-retaining thickener, and additives are measured and mixed according to the proportion to prepare a dry mix; the dry mix is ​​dispersed and packaged as Finished product; the present invention improves the various performances of the mortar, can save a certain cost of raw materials, facilitates construction, has excellent waterproof performance and anti-cracking performance, and has good durability.

Description

technical field [0001] The invention relates to the technical field of mortar production, in particular to a waterproof dry-mixed mortar and a production process thereof. Background technique [0002] my country is both a big cement producer and a big cement consumer. According to incomplete statistics, 70% of cement is used for concrete preparation every year, and 30% is used for the production of cement mortar. Cement mortar plays the role of bonding, lining and transmitting stress in construction engineering. Like traditional concrete, cement mortar used to be made by mixing cement and sand with water at the construction site. With the development of society and technological progress, the market's requirements for product refinement and diversification have increased, and the "ready-mixed mortar" produced by professional mortar manufacturers has become an effective means to solve these problems, including: wet-mixed mortar and dry-mixed mortar mortar. On August 1, 20...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B24/38C04B24/42C04B18/08C04B111/27C04B103/46C04B103/44C04B103/65
CPCC04B24/42C04B28/04C04B40/0039C04B2103/44C04B2103/46C04B2103/65C04B2111/27C04B14/068C04B18/08C04B14/02C04B2103/0057C04B16/0633C04B22/142C04B2103/302C04B24/38C04B24/383C04B22/00Y02W30/91
Inventor 韩杰陈雄伟张樟雄
Owner 浙江龙游通衢建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com