Shrinkage-warping-resistant ASA 3D printing material and preparation method thereof

A printing material and anti-shrinkage technology, applied in the direction of additive processing, etc., can solve problems such as physical and mental health of operators that affect the forming accuracy of parts, shrinkage and warpage of materials, etc., to reduce molecular chain peristalsis, reduce surface tension, and improve thermal stability. sexual effect

Pending Publication Date: 2021-06-25
LIMING VOCATIONAL UNIV
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the molding process of this material by 3D printing technology, due to the open molding of the 3D printer and the continuous high-temperature heating of the nozzle, the materia

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Shrinkage-warping-resistant ASA 3D printing material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of anti-shrinkage warping ASA 3D printing material, the components are calculated by weight percentage: ASA resin 70%, HIPS resin 15%, organicized montmorillonite 5% (the layer spacing of organicized montmorillonite in this embodiment Preferred is 2.4 nm), acrylonitrile-butadiene-styrene grafted maleic anhydride 5%, zinc stearate 2%, antioxidant 1010 1% and stearic acid 2%.

[0026] A method for preparing an ASA 3D printing material resistant to shrinkage and warpage, comprising the following steps:

[0027] (1) ASA resin, HIPS resin, organic montmorillonite, acrylonitrile-butadiene-styrene grafted maleic anhydride, zinc stearate and antioxidant 1010 were vacuum-dried respectively, and each group after drying The parts are weighed according to the following weight percentage ratio: a kind of anti-shrinkage and warping ASA3D printing material, the components are calculated by weight percentage: ASA resin 70%, HIPS resin 15%, organic montmorillonite 5%, acrylonitri...

Embodiment 2

[0033] A kind of anti-shrinkage warping ASA 3D printing material, the components are calculated by weight percentage: ASA resin 65%, HIPS resin 20%, organicized montmorillonite 6% (the layer spacing of organicized montmorillonite in this embodiment Preferably 3.5nm), acrylonitrile-butadiene-styrene grafted glycidyl methacrylate 6%, calcium stearate 1%, antioxidant 168 1% and liquid paraffin 1%.

[0034] A method for preparing an ASA 3D printing material resistant to shrinkage and warpage, comprising the following steps:

[0035] (1) ASA resin, HIPS resin, organic montmorillonite, acrylonitrile-butadiene-styrene grafted glycidyl methacrylate, calcium stearate and antioxidant 168 are vacuum-dried respectively, and after drying The components are weighed according to the following weight percentage ratio: an anti-shrinkage and warping ASA 3D printing material, the components are calculated by weight percentage: ASA resin 65%, HIPS resin 20%, organic montmorillonite 6% , acryloni...

Embodiment 3

[0041]A kind of anti-shrinkage warping ASA 3D printing material, the components are calculated by weight percentage: ASA resin 75%, HIPS resin 12%, organicized montmorillonite 7% (the layer spacing of organicized montmorillonite in this embodiment Preferred are 3.8 nm) styrene, grafted glycidyl methacrylate 4%, magnesium stearate 0.5%, antioxidant CA 0.5% and polyethylene wax 1%.

[0042] A method for preparing an ASA 3D printing material resistant to shrinkage and warpage, comprising the following steps:

[0043] (1) ASA resin, HIPS resin, organic montmorillonite, styrene-grafted glycidyl methacrylate and magnesium stearate were vacuum-dried respectively, and each component after drying was weighed according to the following weight percentage ratio : An anti-shrinkage and warping ASA 3D printing material, the components are calculated by weight percentage: ASA resin 75%, HIPS resin 12%, organic montmorillonite 7%, styrene grafted glycidyl methacrylate 4 %, magnesium stearate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a shrinkage-warping-resistant ASA 3D printing material. ASA resin is used as a raw material, and HIPS, organic montmorillonite, a compatilizer, a heat stabilizer, an antioxidant and a lubricant are added; and the prepared 3D printing material has excellent shrinkage warping resistance, mechanical properties and weather resistance, and is especially suitable for 3D printing in the engineering field. In addition, the invention further discloses a preparation method of the 3D printing material, and the prepared ASA 3D printing material is low in shrinkage warping rate.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to an anti-shrinkage and warpage ASA 3D printing material and a preparation method thereof. Background technique [0002] 3D printing technology is a method of converting a three-dimensional model into a digital code through computer slicing software, then controlling the 3D printer to execute the digital code, and finally using polymer materials or metal materials to print layer by layer. This technology has been widely used in industry Design, aerospace and education teaching and other fields. [0003] ASA resin is a polymer material composed of acrylonitrile, styrene and acrylate. This material not only has good processing performance, but also has excellent weather resistance, especially in the field of outdoor products is widely used. However, during the molding process of the material by 3D printing technology, due to the open molding of the 3D printer ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L51/04C08L55/02C08L91/06C08L35/06C08L23/06C08K13/02C08K5/098C08K3/34C08K5/134C08K5/09C08K5/526B33Y70/10
CPCC08L51/04B33Y70/10C08L2205/025C08L2205/03C08L2205/035C08L55/02C08K13/02C08K5/098C08K3/346C08K5/1345C08K5/09C08L91/06C08K5/526C08L35/06C08L23/06
Inventor 黄欣茹蕉荃鹏叶辉灿张育铭
Owner LIMING VOCATIONAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap