A kind of soil heavy metal removal composite material and its preparation method and application

A composite material and heavy metal technology, applied in the restoration of polluted soil, etc., can solve the problems of soil property change, high cost, deterioration, etc., and achieve the effect of easy degradation and complete removal

Active Publication Date: 2022-03-25
SOUTH CHINA AGRI UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the use of this technology will inevitably produce a large amount of leaching waste liquid, and the disposal of waste liquid will incur high costs; soil properties will change or even deteriorate after leaching

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of soil heavy metal removal composite material and its preparation method and application
  • A kind of soil heavy metal removal composite material and its preparation method and application
  • A kind of soil heavy metal removal composite material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] (1) At room temperature, take 0.5g carboxymethyl chitosan, add 3.8g acrylic acid and 5ml deionized water, stir mechanically at 800rpm until completely dissolved.

[0043] (2) At a stirring speed of 800rpm, add 2g of sodium hydroxide to adjust the degree of neutralization of the acrylic acid monomer. After cooling, add 30μl of N,N,N',N'-tetramethyl-1,2-ethylenediamine, 0.001g of N,N'-methylenebisacrylamide, 1.5g of 500nm ferric oxide and 0.2g of potassium persulfate, nitrogen gas was introduced, and the temperature was adjusted to 80°C for polymerization reaction. After 3 hours of reaction, the product was taken out and poured into 10 Settled in cold ethanol with double vigorous stirring, filtered the precipitate, washed with deionized water and ethanol three times alternately, dried in vacuum at 60°C for 24 hours, and obtained double-network superabsorbent resin;

[0044] (3) After crushing the above-mentioned double-network superabsorbent resin and passing it through a...

Embodiment 2

[0047] (1) At room temperature, take 0.5 g of sodium alginate, add 3.8 g of acrylic acid and 5 ml of deionized water, and stir mechanically at 800 rpm until completely dissolved.

[0048](2) While stirring at 800rpm, add 2g of sodium hydroxide to adjust the degree of neutralization of the acrylic acid monomer. After cooling, add 30μl of N,N,N',N'-tetramethyl-1,2-ethylenediamine, 0.001g of N,N'-methylenebisacrylamide, 1.5g of 500nm ferric oxide and 0.2g of potassium persulfate, nitrogen gas was introduced, and the temperature was adjusted to 80°C for polymerization reaction. After 3 hours of reaction, the product was taken out and poured into 10 Settled in cold ethanol with double vigorous stirring, filtered the precipitate, washed with deionized water and ethanol three times alternately, dried in vacuum at 60°C for 24 hours, and obtained double-network superabsorbent resin;

[0049] (3) After crushing the above-mentioned double-network superabsorbent resin and passing it throu...

Embodiment 3

[0052] (1) At room temperature, take 1.0 g of carboxymethyl chitosan, add 3.8 g of acrylic acid and 5 ml of deionized water, and stir mechanically at 800 rpm until completely dissolved.

[0053] (2) While stirring at 800rpm, add 2g of sodium hydroxide to adjust the degree of neutralization of the acrylic acid monomer. After cooling, add 30μl of N,N,N',N'-tetramethyl-1,2-ethylenediamine, 0.001g of N,N'-methylenebisacrylamide, 1.5g of 500nm ferric oxide and 0.2g of potassium persulfate, nitrogen gas was introduced, and the temperature was adjusted to 80°C for polymerization reaction. After 3 hours of reaction, the product was taken out and poured into 10 Settled in cold ethanol with double vigorous stirring, filtered the precipitate, washed with deionized water and ethanol three times alternately, dried in vacuum at 60°C for 24 hours, and obtained double-network superabsorbent resin;

[0054] (3) After crushing the above-mentioned double-network superabsorbent resin and passing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a soil heavy metal removal composite material, a preparation method and application thereof. In the present invention, firstly, the magnetic double-network superabsorbent resin material is obtained by catalyzing and initiating polymerization of carboxymethyl chitosan or sodium alginate, acrylic acid and magnetic nanoparticles, and then doped with polylactic acid to finally obtain an activated-adsorption integrated magnetic superabsorbent resin composite Material. The composite material obtained in the present invention has high water-absorbing expansibility endowing it with high adsorption capacity for heavy metals, doped with organic acids can activate insoluble heavy metals in soil, and can be recovered by using material magnetism, making up for the passivation of existing heavy metals It can completely and efficiently remove highly harmful heavy metals in the soil due to the lack of detergent and leaching agent.

Description

technical field [0001] The invention belongs to the field of soil heavy metal pollution control, and in particular relates to a soil heavy metal removal composite material, a preparation method thereof and an application in treating soil heavy metal pollution. Background technique [0002] Due to the high toxicity, persistence, non-biodegradability and bioaccumulation of heavy metals, heavy metal pollution has attracted widespread attention worldwide. In recent years, various in-situ or ex-situ remediation of heavy metal-contaminated soils have been developed, such as landfill coverage, chemical fixation, soil leaching, physical and chemical adsorption, soil vitrification, electrochemical remediation, microbial or phytoremediation, etc. At present, the widely used technology is soil heavy metal fixation technology, which uses lime, phosphate, humus, biochar or various organic-inorganic composite porous materials as fixatives to adsorb and fix heavy metals, and absorb acid-so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/04C08L51/02B09C1/08C08F251/00C08F220/06C08F222/38C08K3/22C08K3/30
CPCC08L67/04C08F251/00B09C1/08C08K3/22C08K3/30C08K2201/011C08K2003/2272C08K2003/2275C08K2003/3009C08K2201/01C08K2201/005C08F220/06C08F222/385C08L51/02
Inventor 蒋刚彪刘金文胡甜刘步宁胡汉剑
Owner SOUTH CHINA AGRI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com