Asphalt polyurethane waterproof coating and preparation method thereof

A polyurethane waterproof and waterproof coating technology, applied in polyurea/polyurethane coatings, asphalt coatings, coatings, etc., can solve the problems of easy adverse reactions, poor adhesion, high surface energy, etc., to improve compatibility and adhesion Adhesion, strong adhesion, and low surface energy

Active Publication Date: 2021-10-22
KESHUN WATERPROOF TECH CO LTD
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the self-adhesive asphalt membrane is a non-polar material with low surface energy, and the polyurethane waterproof coating is a polar material with high surface energy, and when the two are combined due to the presence of solvents, adverse reactions between the two are prone to occur. , poor adhesion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Asphalt polyurethane waterproof coating and preparation method thereof
  • Asphalt polyurethane waterproof coating and preparation method thereof
  • Asphalt polyurethane waterproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0050] The second aspect of the embodiment of the present application provides a method for preparing an asphalt polyurethane waterproof coating, comprising steps:

[0051] S01. Stir and mix polyether polyol, polyolefin polyol, asphalt, plasticizer, defoamer and filler to obtain a first mixture;

[0052] S02. Under the condition that the relative vacuum degree is -0.08MPa~-0.1MPa, the first mixture is stirred and heated to 100°C-110°C, and dehydrated for 2h-3h to obtain the second mixture;

[0053] S03. Add diisocyanate, latent curing agent and catalyst to the second mixture to react for a preset time to obtain bituminous polyurethane waterproof coating.

[0054] In step S01, the polyether polyol, hydroxyl-terminated polybutadiene acrylonitrile, asphalt, filler and plasticizer can be dispersed for 4 minutes to 6 minutes at a rotation speed of 800 rpm to 1200 rpm; then the rotation speed is adjusted to 1500 rpm to 2000 rpm to further Disperse for 30 minutes to 50 minutes to ob...

Embodiment 1

[0065] A kind of asphalt polyurethane waterproof coating, raw material comprises by weight: polyether glycol 2000, 10 parts; polyether trihydric alcohol 330N, 5 parts; Acrylonitrile, 2 parts; BASF TDI-80, 2 parts; Chlorinated paraffin, 3 parts; No. 70 petroleum pitch, 5 parts; Dibutyltin dilaurate, 0.2 parts; Foaming agent, 0.1 part; 1250 mesh talcum powder, 20 parts; 800 mesh heavy calcium, 25 parts.

Embodiment 2

[0067] A kind of asphalt polyurethane waterproof coating, raw material comprises by weight: polyether glycol 2000, 10 parts; polyether trihydric alcohol 330N, 7 parts; Acrylonitrile, 4 parts; BASF TDI-80, 3 parts; chlorinated paraffin, 3 parts; No. 70 petroleum pitch, 10 parts; dibutyltin dilaurate, 0.3 parts; imine latent curing agent, 1 part; Foaming agent, 0.1 part; 1250 mesh talcum powder, 20 parts; 800 mesh heavy calcium, 25 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an asphalt polyurethane waterproof coating and a preparation method thereof. The asphalt polyurethane waterproof coating comprises the following main raw materials by weight: 15-25 parts of polyether polyol; 2-10 parts of polyolefin polyol; 2- 6 parts of diisocyanate; and 5 -20 parts of asphalt. According to the invention, hydroxyl-terminated polybutadiene acrylonitrile is used for partially replacing traditional polyether polyol and is reacted with isocyanate, and two chain segments of non-polar butadiene and strong-polar acrylonitrile are introduced into the synthesized polyurethane prepolymer, so that the compatibility of the polyurethane prepolymer and asphalt is greatly enhanced, and the prepared asphalt polyurethane coating has relatively good compatibility and adhesion with an asphalt coiled material.

Description

technical field [0001] The present application relates to the technical field of waterproof coatings, in particular to an asphalt polyurethane waterproof coating and a preparation method thereof. Background technique [0002] In recent years, the composite waterproof process represented by coatings and membranes has become a hot spot in the field of building waterproofing. The most common construction process is the composite use of polyurethane waterproof coatings and self-adhesive bitumen waterproof membranes. Since the self-adhesive asphalt membrane is a non-polar material with low surface energy, and the polyurethane waterproof coating is a polar material with high surface energy, and when the two are combined due to the presence of solvents, adverse reactions between the two are prone to occur. , poor adhesion. Contents of the invention [0003] In view of this, the present application provides an asphalt polyurethane waterproof coating with better compatibility and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D195/00C08G18/69C08G18/48C08G18/12
CPCC09D175/14C08G18/698C08G18/4812C08G18/12C08G2150/00C08L95/00
Inventor 戴小聪姜仡鹏陈立义
Owner KESHUN WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com