Method for preparing mesophase asphalt by using catalytic cracking slurry oil
A technology of catalytic cracking oil slurry and mesophase pitch, which is applied in the field of petroleum pitch, can solve the problems of limited use range, no economic benefits, waste of resources, etc., achieve low softening point, realize large-scale industrial production, and reduce waste Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0029] Example 1:
[0030] The first step was added 0.01 g of a small reduction oxide graphene combination (oxygen content of 1%) and 400 g of catalytic cracking oil pulp to a high temperature and high pressure reactor, and a nitrogen purge replacement air was closed. The rate of 5 ° C / min was raised to 150 ° C and stirred (500 rpm) for 1 h, and the graphene was uniform in the oil pulley. Then rose at a rate of 2 ° C / min to 430 ° C, stirred (300 rpm), and the pressure is self-boost during the reaction. When the insulation process ends, the internal pressure is released, and the nitrogen purge is removed from the light component, and the mixing device is stopped, and the reaction kettle is cooled to room temperature, obtain 300 g of petroleum asphalt, and the softening point is 120 ° C, the molecular weight is 1.72, crystal layer The spacing is 0.3483 nm.
[0031] In the second step, the above 300 g of petroleum asphalt was pulverized and placed in a high temperature and high p...
Example Embodiment
[0033] Example 2
[0034] The amount of reductant oxidation graphene was added from 0.01 g to 0.04 g, and the other conditions were as in Example 1, the obtained petroleum asphalt softening point was 135 ° C, the molecular weight distribution was 1.70, the crystal layer spacing was 0.3481 nm, and the final prepared intermediate phase The softening point of the asphalt is 265 ° C, the intermediate phase content is 95%. The foam thermal conductivity prepared by the intermediate phase asphalt was 106 W / (m · k); the modulus of carbon fibers was 510 GPa, and the thermal conductivity was 983 w / (m · k).
Example Embodiment
[0035] Example 3
[0036]The amount of reductant oxidation graphene is added from 0.01 g to 0.08 g, and the other conditions are as in Example 1, the obtained petroleum asphalt softening point is 142 ° C, the molecular weight distribution is 1.66, the crystal layer spacing is 0.3479 nm, and the final prepared intermediate phase The softening point of the asphalt is 261 ° C, the intermediate phase content is 97%. The foam thermal conductivity prepared by the intermediate phase asphalt was 115 w / (m · k); the modulus of carbon fibers was 550 GPa, and the thermal conductivity was 1008 w / (m · k).
PUM
Property | Measurement | Unit |
---|---|---|
Softening point | aaaaa | aaaaa |
Softening point | aaaaa | aaaaa |
Thermal conductivity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap