Glass frosting liquid, frosted glass prepared from glass frosting liquid and preparation method of glass frosting liquid

A frosting liquid and glass technology, which is applied in the field of frosted glass preparation, can solve the problems of glass light pollution and achieve the effect of eliminating glare

Pending Publication Date: 2021-11-19
XIANGSHI ENERGY SAVING GLASS KUNSHAN CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a glass frosting solution to solve the problem of light pollution caused by glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass frosting liquid, frosted glass prepared from glass frosting liquid and preparation method of glass frosting liquid
  • Glass frosting liquid, frosted glass prepared from glass frosting liquid and preparation method of glass frosting liquid
  • Glass frosting liquid, frosted glass prepared from glass frosting liquid and preparation method of glass frosting liquid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-8A

[0050] Embodiment 1-8AG glass frosting liquid

[0051] The frosting powder formulations of Examples 1-8 are shown in Table 1. The frosting liquid of Examples 1-8 is obtained by dispersing 100 g of frosting powder in 35 g of deionized water. The specific preparation method is: accurately weigh ammonium bifluoride according to the number of parts by mass , ammonium fluoride, oxalic acid dihydrate, sulfamic acid, white sugar, sucrose, barium sulfate, barium fluoride, calcium fluoride, sodium fluoride, potassium fluoride dihydrate, potassium chloride, aluminum fluorosilicate, twelve Sodium alkylsulfonate and magnesium fluorosilicate medicines are finely ground in a ceramic mortar (because many medicines are crystal blocks, so they need to be ground), and the grinding time is about 10 minutes (grinding until the medicine is dispersed) non-agglomerative powder, no agglomeration phenomenon), after the grinding is completed, transfer all the medicines in the mortar to a 1000mL beaker ...

Embodiment 1

[0061] Compared with Example 1 and Example 2, the appearance of the AG powder frosted glass in Example 1 is very smooth, and the content of aluminum fluorosilicate increases, which improves the flatness of the frosted glass.

[0062] Such as figure 1 As shown in the upper left corner, after the silicic acid in the glass is dissolved, aluminum fluorosilicate acts as a silicic acid gel accelerator to accelerate the polymerization of the silicic acid dissolved by ammonium bifluoride on the glass surface to form uniform gel particles. Aluminum fluorosilicate content reduces among the embodiment 2, causes figure 2 No homogeneous gel particles were observed in . Compared with Example 4, the ammonium bifluoride is slightly increased, causing the apparent roughness of the AG powder frosted glass to increase from an average of 0.359 to 0.532. Compared with Example 5, the content of aluminum fluorosilicate increased from 3.872% to 4.350%, which caused the apparent roughness of AG pow...

Embodiment 6

[0064] Examples 6-7 are different from Examples 1-5 and Example 8. Magnesium fluorosilicate is added to the AG powder frosting powder, and the roughness of the AG powder frosting glass is greatly improved. In Example 6, a large amount of magnesium fluorosilicate was added, and the roughness increased significantly, with an average roughness value of 0.970; while when the amount of magnesium fluorosilicate was only 0.5%, the average roughness value of Example 7 only increased to 0.810. Image 6 with Figure 7 The morphology scan of AG powder frosted glass also shows that due to the increase of magnesium fluorosilicate, magnesium fluorosilicate acts as an accelerator to promote the quick-setting of silicic acid sol, and the apparent roughness increases significantly. Moreover, the higher the magnesium fluorosilicate content, the lower the uniformity of the surface gel particles, Image 6 The coexistence of medium and large particles of gel and small particles of gel directly l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a glass frosting liquid, frosted glass prepared from the glass frosting liquid and a preparation method of the glass frosting liquid. The glass frosting liquid comprises frosting powder and a solvent. The frosting powder comprises the following raw materials in mass percentage 1.0 to 5.0% of oxalic acid dihydrate, 2.0 to 8.0% of sulfamic acid, 0 to 2.0%of white granulated sugar, 0 to 3.0% of cane sugar, 11.0 to 14.0% of barium sulfate, 5.0 to 11.0% of barium fluoride, 0.02 to 0.5% of calcium fluoride, 0.1 to 2.5% of sodium fluoride, 0.05 to 4.0% of potassium fluoride dihydrate, 0 to 3.0% of potassium chloride, 1.5 to 6.0% of aluminum fluosilicate, 0.5 to 1.5% of sodium dodecyl sulfate, 0.1 to 9%of ammonium fluoride, 0.5 to 3.0%of magnesium fluosilicate and the balance of ammonium hydrogen fluoride, the sum of the mass percentage of the raw materials is 100%. According to the frosted glass prepared by the method of the invention, glare is effectively eliminated, and the anti-glare purpose is achieved.

Description

technical field [0001] The invention relates to the technical field of frosted glass preparation, in particular to a glass frosting liquid, prepared frosted glass and a preparation method. Background technique [0002] In a broad sense, glass is defined as an amorphous solid with complete long-range disorder in structure and glass transition characteristics. In a narrow sense, it is defined as an inorganic substance obtained by cooling a melt without crystallization. Therefore, glass is an amorphous inorganic non-metallic material, and it is also a material similar to a solid external structure and a liquid internal structure. [0003] Glass is widely used in people's daily life, such as glass cups, glass doors, glasses, etc., due to its high mechanical strength, excellent optical properties, uniform texture, difficult aging and smooth surface. A special use of glass is in decorative finishing. A certain modification of the surface of the glass can make the glass used in m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C15/00
CPCC03C15/00
Inventor 韩伟军杨宇翔刘稳文黄忠祥汤哲辉黄艳
Owner XIANGSHI ENERGY SAVING GLASS KUNSHAN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap